Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (119)
- Beitrag zu einem Tagungsband (6)
- Buchkapitel (1)
Referierte Publikation
- ja (126) (entfernen)
Schlagworte
- Femtosecond laser ablation (19)
- Laser-induced periodic surface structures (LIPSS) (18)
- Femtosecond laser (15)
- Laser ablation (15)
- Silicon (8)
- Radiation protection (7)
- Laser cleaning (6)
- Laser processing (6)
- Titanium (6)
- High-speed optical techniques (5)
Organisationseinheit der BAM
- 6 Materialchemie (26)
- 6.2 Material- und Oberflächentechnologien (26)
- 6.7 Materialsynthese und Design (3)
- 9 Komponentensicherheit (3)
- 9.5 Tribologie und Verschleißschutz (3)
- 4 Material und Umwelt (2)
- 4.1 Biologische Materialschädigung und Referenzorganismen (2)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
Paper des Monats
- ja (2)
Zusammenfassung
The surface chemical modification of polyurethane (PU) films was performed by an UV laser-induced chemical reaction in a polysaccharide solution. This process may be applicable as hydrophilic packaging of implantable medical devices and in vivo sensors. When a PU film in contact with an aqueous alginic acid (AAC) solution was irradiated with a XeCl laser, the PU film turned hydrophilic. Contact angles of water on the film were reduced from 110° to 60°. Since light absorption of the AAC solution at 308 nm was negligibly small, reactive sites were generated solely on the PU surface. There, AAC could be immobilized by chemical bonds thus allowing for a nanometer-scaled grafting of this biomolecule. The mechanism was investigated by surface analyses with Fourier-transform infrared spectroscopy (FT-IR), dye staining, ultraviolet-visible (UV-VIS) spectroscopy, and scanning electron microscopy (SEM) techniques. A one-photon photochemical process could beidentified.
Zusammenfassung
Laser pulses in the 10-fs domain provide a quality of micromachining of fused silica and borosilicate glass that is unobtainable with longer pulses in the range of several 100 femtoseconds up to picoseconds. The shortening of the pulses reduces the statistical behavior of the material removal and the ablation process thus attains a more deterministic and reproducible character. The improved reproducibility of ablation is accompanied by significantly smoother morphology. This offers the potential for lateral and vertical machining precision of the order of 100 nm and 10 nm, respectively.
We present surface micro-modifications of bariumalumoborosilicate glasses with a high transformation temperature near 700 °C. Laser processing of the glass substrate was realized by using ultra-short laser pulses at 800 nm. The morphological conversion of the laser-treated surfaces was characterized by scanning force microscopy and nano-indentation. A hardness increase by at least a factor of six on the laser ablation crater edge relative to illuminated non- ablated areas shows that the material in the crater walls underwent drastic morphological and mechanical changes. In this heat- and shock-affected zone, the material became more elastic as a result of increased stress.
Femtosecond-pulse laser ablation of dental hydroxyapatite and single-crystalline fluoroapatite
(1999)
Laser microdrilling of healthy human enamel and dentine using 300 fs pulses at a wavelength of 615 nm and 3 Hz repetition rate leads to an enhanced structuring quality in comparison with nanosecond-laser results. Microcracking and damage to neighboring tissue can be reduced. Ablation threshold fluences for 100 laser pulses of 0.3 J cm-2 (human dentine), 0.6 J cm-2 (human enamel) and 0.8 J cm-2 (single crystalline fluoroapatite) could be determined. Ablation depths per pulse below 1 7m were observed.
Zusammenfassung
The threshold fluences for laser-induced damage of fused silica with single 5-fs pulses from a Ti:sapphire laser system were determined by extrapolating the ablated volume to zero. These thresholds are about 4 times as high as the values previously obtained from multi-shot experiments. This result is interpreted in terms of an irreversible modification of the original material below the single-shot threshold (incubation).
Ablation experiments in several glasses with single and multishot irradiation by laser pulses in the 10-fs pulse duration domain are presented; physical and technological implications are discussed. We demonstrate that these short pulses offer the potential for lateral and vertical machining precision of the order of 100 nm.
KrF excimer laser ablation of polyethylene terephthalate (PET), polyimide (PI) and polycarbonate (PC) in air was studied by an in situ monitoring technique using a microphone. The microphone signal generated by a short acoustic pulse represented the etch rate of laser ablation depending on the laser fluence, i.e., the ablation strength. From a linear relationship between the microphone output voltage and the laser fluence, the single-pulse ablation thresholds were found to be 30 mJ cm-2 for PET, 37 mJ cm-2 for PI and 51 mJ cm-2 for PC (20-pulses threshold). The ablation thresholds of PET and PI were not influenced by the number of pulses per spot, while PC showed an incubation phenomenon. A microphone technique provides a simple method to determine the excimer laser ablation threshold of polymer films.
Near-ablation threshold investigations focusing on the generation of periodic nanostructures and their correlation with physico-chemical
properties of the solid phase such as e.g., the material-dependent surface energy, were conducted. Molecular dynamic modelling in the
sub-picosecond time domain was used to consider ultrafast opto-electronic processes triggering surface reorganization reactions.
Fluid containment of solid interfaces showed strong influence on the resulting micro- and nanostructures due to its drastic reduction of the
surface energy. The phenomena are discussed in respect to the minimization of the surface free energy in dependence of material composition
and interfacial structure.
Femto- and nanosecond laser ablation of polymethylmethacrylate (PMMA) and PMMA doped with a linear absorber was
investigated in the infrared spectral region. Ablation thresholds were determined and incubation phenomena were identified. The
degree of incubation was calculated employing a phenomenological model. The influence of the pulse duration on the
machining quality of the polymers was examined. The presence of an absorbing chromophore is not a prerequisite for a
controllable fs-laser structuring in contrast to the ns-treatment. Surface swelling always accompanied ablation.
Femtosecond laser interaction with silicon was investigated in water and in air, with 130-fs laser pulses at 800 nm wavelength. Under water confinement, higher modification thresholds, lower ablation depths and similar incubation factors were found in comparison to the dry experiment. Morphological features of the laser-induced cavities also differed. In contrast to air experiments, debris redeposition was negligible, while the ablated material remained suspended in the water layer phase. Underwater cavities obtained at high fluences and high number of pulses per spot showed anomalous profiles, consistent with a strong spatial deformation of the laser beam coupled into the target. Ripples formed at the edges of the modified area showed varying spacings: f100 and f700 nm for water and air experiments, respectively. Differences to the air experiment were related to a complex combination of fluence-dependent non-linear effects occurring in the water layer and to pulse-number-dependent shielding effects induced by cavitation bubbles and suspended ablated
material.
In situ second harmonic generation measurements during the electrodeposition of Ni on n-Si(111)
(1993)
A femtosecond pulse laser in the visible spectral region shows promise as a potentially new powerful corneal sculpting tool. It combines the clinical and technical advantages of visible wavelengths with the high ablation quality observed with nanosecond-pulse excimer lasers at 193 nm. A femtosecond and a nanosecond dye laser with pulse durations of 300 fs and 7 ns, and centre wavelengths at 615 nm and 600 nm, respectively, both focused to an area of the order of 105 cm2, have been applied to human corneal ablation. Nanosecond laser pulses caused substantial tissue disruption within a 30100 m range from the excision edge at all fluences above the ablation threshold of F th60 J cm2 (I th9 GW cm2). Completely different excisions are produced by the femtosecond-pulse laser: high quality ablations of the Bowman membrane and the stroma tissue characterised by damage zones of less than 0.5 m were observed at all fluences above ablation threshold of F th1 J cm2 or I th3 TW cm2 (3×1012 W cm2). The transparent cornea material can be forced to absorb ultrashort pulses of extremely high intensity. The fs laser generates its own absorption by a multiphoton absorption process.
Censorship of parts of written text was and is a common practice in totalitarian regimes. It is used to destroy information not approved by the political power. Recovering the censored text is of interest for historical studies of the text. This paper raises the question, whether a censored postcard from 1942 can be made legible by applying multispectral imaging in combination with laser cleaning. In the fields of art conservation (e.g. color measurements), investigation (e.g. Analysis of underdrawings in paintings), and historical document analysis, multispectral imaging techniques have been applied successfully to give visibility to information hidden to the human eye.
The basic principle of laser cleaning is to transfer laser pulse energy to a contamination layer by an absorption process that leads to heating and evaporation of the layer. Partial laser cleaning of postcards is possible; dirt on the surface can be removed and the obscured pictures and writings made visible again. We applied both techniques to the postcard. The text could not be restored since the original ink seems to have suffered severe chemical damage.
Optical fibers made of fused silica are a common method of transmitting high laser pulse energies. Failure of those fibers is a significant risk. The determination of laser-induced damage thresholds (LIDT) on fiber end facets according to ISO 21254 standard is needed. In the past, single pulse nanosecond laser experiments showed an improvement of LIDT with increasing fiber core diameter for 1064 nm wavelength and a constant beam diameter of 50 µm.
This paper pays particular attention to the influence of the laser beam diameter on damage resistance. All-silica fiber types (LEONI) with different core diameters (100–600 µm) were investigated using beam diameters in a range from 30 µm to 100 µm. For comparison experiments on fused silica preform material (Heraeus F300) were performed. On one hand, surface LIDT of fused silica preform material decreases significantly with increasing beam size. A model considering a random distribution of point defects explains the experimental data qualitatively. On the other hand, LIDT of fiber end facets stays constant. White light microscopy results suggest that the point defect density on fiber end facets is lower compared to the preform surface due to an excellent surface polish quality.
The surface of a titanium alloy (Ti6Al4V) implant material was covered with a bioactive calcium alkali phosphate ceramic with the aim to accelerate the healing and to form a stronger bond to living bone tissue. To fix the ceramic powder we used a femtosecond laser, which causes a thin surface melting of the metal. It is a requirement to prove that the laser irradiation would not reduce the lifetime of implants. Here we present the results of mechanical stability tests, determined by the rotating bending fatigue strength of sample rods. After describing the sample surfaces and their modifications caused by the laser treatment we give evidence for an unchanged mechanical stability. This applies not only to the ceramic fixation but also to a comparatively strong laser ablation.
The formation of laser-induced periodic surface structures (LIPSS) on two different silica polymorphs (single-crystalline synthetic quartz and commercial fused silica glass) upon irradiation in air with multiple linearly polarized single- and double-fs-laser pulse sequences (τ = 150 fs pulse duration, λ = 800nm center wavelength, temporal pulse separation Δt < 40 ps) is studied experimentally and theoretically. Two distinct types of fs-LIPSS [so-called low-spatial-frequency LIPSS (LSFL) and high-spatial-frequency LIPSS (HSFL)] with different spatial periods and orientations were identified. Their appearance was characterized with respect to the experimental parameters peak laser fluence and number of laser pulses per spot. Additionally, the 'dynamics' of the LIPSS formation was addressed in complementary double-fs-pulse experiments with varying delays, revealing a characteristic change of the LSFL periods. The experimental results are interpreted on the basis of a Sipe-Drude model considering the carrier dependence of the optical properties of fs-laser excited silica. This new approach provides an explanation of the LSFL orientation parallel to the laser beam polarisation in silica—as opposed to the behaviour of most other materials.
Optical multimode fibers made of fused silica are widely used for transmission of high power laser pulses. Bending of fibers creates mechanical stress inside the material. The bend stress of a fiber can be calculated from bend radius, geometrical fiber parameters and Young's Modulus of the fiber core material and reaches typically values of 220 MPa. A thermo-elastic model of Kusov et al. predicts a quadratic dependence of laser-induced damage threshold fluence with applied stress.
In the present study, fiber preform material F300 (Heraeus) was loaded mechanically with pressures up to 220 MPa representing 20% of the pressure resistance of fused silica. Bulk laser-induced damage thresholds (LIDT) were evaluated using a longitudinal multimode Q-switched Nd:YAG laser (1064 nm) at a pulse duration of 12 ns with polarization states parallel and perpendicular to the stress direction. LIDT of fused silica samples of about 700 J/cm2 were found. LIDT did not show a dependence on mechanical pressure and polarization state which is a consequence of the small ratio of maximum applied stress (220 MPa) to Young's Modulus of fused silica (72.5 GPa).
The 125-fs laser ablation behaviour (800 nm) of aluminium and anodic oxide coatings on an AlMgSi1 alloy was investigated. The multi-pulse ablation threshold of aluminium at 1.2 J cm-2 was less than that of the oxides of 23 J cm-2. Aluminium exhibited a single pulse modification (melting) threshold of 0.3 J cm-2. These values derived from an evaluation of the crater geometry coincided with on-line acoustic measurements. The detected microphone voltage amplitude increased linearly with the laser fluence. The morphology of the ablation craters on aluminium indicated melt formation and displacement of a homogeneous melt phase due to the recoil action of the expanding metal vapour. The laser-processed ceramic oxide phases, on the other hand, showed a spongy resolidified melt layer, which denotes a collocated in-depth formation both of a melt and a gas phase. These phenomena are discussed in terms of the relative dominance of penetration depth of laser light and heat affected zones in the investigated materials with strongly varying optical and thermodynamical properties.
Curved substrates can be micro-structured by laser ablation, which is not possible with standard lithographic methods. The novel femtosecond-pulse laser technique allows the production of defined and reproducible micro-perforations of originally analyte-impermeable membranes. The trans-membrane analyte flux can be controlled both by the variation of the laser focus diameter resulting in different areas of single perforations, and the number of perforations in arrays on small membrane areas. This leads to a higher degree of variability as well as reproducibility of the diffusion qualities of sensor membranes, and marks the main innovation with this technique compared to the hand-made mechanical perforation by specially grinded needles used up to now. Touchless micro-perforation of small membrane areas with negligible heat damage of the structures adjacent to the perforation allows the application of analyte door membranes directly onto curved surfaces of miniaturized needle-sensors assigned for in vivo glucose monitoring, for the first time.
Laser cleaning of delicate biological composite materials such as ancient parchment manuscripts from the 15th and 16th century and printed paper from the 19th century is demonstrated with an ultraviolet excimer pulsed laser at 308 nm. Laser fluence levels must stay below the ablation and destruction threshold of the parchment or paper substrate, and have to surpass the threshold of the contaminant matter. Foreign layers to be removed must exhibit a higher optical density than the artifact substrates. Synthetic carbonaceous dirt modelled by water-soluble black crayons showed a characteristically weak featureless laser-induced plasma spectroscopy spectrum near the noise limit. It turned out that laser-induced plasma spectroscopy is of limited use in monitoring halting points (or etch-stops) because it relies on the destruction not only of the laterally inhomogenously distributed contaminant but also of pigment phases on a microscopically rough parchment substrate. Laser-induced fluorescence spectroscopy, however, promises to be a valuable non-destructive testing technique for etch-stop monitoring.
We report measurements of the optical breakdown threshold and ablation depth in dielectrics with different band gaps for laser pulse durations ranging from 5 ps to 5 fs at a carrier wavelength of 780 nm. For tau <100 fs, the dominant channel for free electron generation is found to be either impact or multiphoton ionization (MPI) depending on the size of the band gap. The observed MPI rates are substantially lower than those predicted by the Keldysh theory. We demonstrate that sub-10-fs laser pulses open up the way to reversible nonperturbative nonlinear optics (at intensities greater than 1014 W/cm2 slightly below damage threshold) and to nanometer-precision laser ablation (slightly above threshold) in dielectric materials.
Ablation experiments employing Ti:sapphire laser pulses with durations from 30 to 340 fs (centre wavelength 800 nm, repetition rate 1 kHz) were performed in air. Absorbing filters (Schott BG18 and BG36) served as targets. The direct focusing technique was used under single- and multi-pulse irradiation conditions. Ablation threshold fluences were determined from a semi-logarithmic plot of the ablation crater diameter versus laser fluence. The threshold fluence decreases for a shorter pulse duration and an increasing number of pulses. The multi-pulse ablation threshold fluences are similar to those of undoped glass material (~1 J cm-2). That means that the multi-pulse ablation threshold is independent on the doping level of the filters. For more than 100 pulses per spot and all pulse durations applied, the threshold fluence is practically constant. This leads to technically relevant ablation threshold values.
A first investigation on the ablation of composite materials like carbon and silicon-carbide reinforced alumo- and borosilicate glasses by 300 fs laser pulses (620 nm) in comparison to experiments with 17 ns pulse excimer laser (308 nm) treatment is presented. In all composites, femtosecond laser scans with a fluence of less than 2 J cm-2 produce well defined cuts with smooth side walls in contrast to the nanosecond laser result where extremely incongruent ablation is observed. Visible lasers should not be applicable because SiC and the glasses are practically transparent. Visible subpicosecond pulses of high intensity in the TW cm-2 range allow multi-photon absorption accompanied by incubation phenomena. The morphology of the groove edges reveal the contrasting ablation thresholds and rates of the fibre and glass materials. The ablation thresholds of the transparent components, i.e. the glass matrices and SiC, are about one order of magnitude greater than that of carbon which is ~ 0.15 J cm-2. Incubation effects are important for the absorption mechanisms in the transparent materials. When a critical number of pulses has not been reached at the SiC-glass composites, only the glass is preferentially ablated, and the fibres remain intact. This is in contrast to the C-glass composites where the ablation behaviour is opposite.
High-power lasers in industrial and R & D applications raise the general problem of reliability and degradation of optical components. A systematic study of nonlinear interaction of various transparent dielectric materials as e.g. glasses, fused silica, and polymers, with laser-pulses in the intensity range of up to 1013 W cm-2 is presented. On the other hand, femtosecond-pulse laser processing in the visible spectral range (300 fs; 620 nm, ~ 2 eV) allows precise microstructuring of transparent dielectrics without disruption of the remnant material. Damage and ablation threshold fluences occur above 1.2 J cm-2 at both silicate glasses and fused silica. Two different photon absorption mechanisms have been observed. The first occurs during the initial laser pulses in the incubation range. There, multiphoton absorption results in moderate energy volume densities. These are sufficient to generate morphological changes and optically active defect sites (colour centres) which provide a much higher absorptivity relevant for the second mechanism. It results in gasification without participation of melt.
High-power optical multimode fibers are essential components for materials processing and surgery and can limit the performance of expensive systems due to breakdown at the end faces. The aim of this paper is the determination of laser-induced damage thresholds (LIDT) of fibers (FiberTech) and preforms (Heraeus Suprasil F300). Preforms served as models. They were heated up to maximum temperatures of 1100, 1300 and 1500°C and cooled down to room temperature at rates of 10 K min-1 (oven) and ~105 K min-1 (quenched in air) to freeze in various structural states simulating different conditions similar to a drawing process during the production of fibers. Single- and multi-pulse LIDT measurements were done in accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were used. For the preforms, LIDT values (1-on-1) ranged from 220 to 350 J/cm² (1064 nm) and from 80 to 110 J/cm² (532 nm), respectively. A multi-pulse impact changed the thresholds to lower values. The LIDT (1064 nm wavelength) of the preforms can be regarded as a lower limit for those of the fibers.
Optical multimode fibers are applied in materials processing (e.g. automotive industry), defense, aviation technology, medicine and biotechnology. One challenging task concerning the production of multimode fibers is the enhancement of laser-induced damage thresholds. A higher damage threshold enables a higher transmitted average power at a given fiber diameter or the same power inside a thinner fiber to obtain smaller focus spots.
In principle, different material parameters affect the damage threshold. Besides the quality of the preform bulk material itself, the drawing process during the production of the fiber and the preparation of the fiber end surfaces influence the resistance. Therefore, the change of the laser-induced damage threshold of preform materials was investigated in dependence on a varying thermal treatment and preparation procedure.
Single and multi-pulse laser-induced damage thresholds of preforms (F300, Heraeus) were measured using a Q-switched Nd:YAG laser at 1064 nm wavelength emitting pulses with a duration of 15 ns, a pulse energy of 12 mJ and a repetition rate of 10 Hz. The temporal and spatial shape of the laser pulses were controlled accurately.
Laser-induced damage thresholds in a range from 150 J cm-2 to 350 J cm-2 were determined depending on the number of pulses applied to the same spot, the thermal history and the polishing quality of the samples, respectively.
High-power optical multimode fibers are essential components for materials processing
and surgery and can limit the reliability of expensive systems due to breakdown at the end faces.
The breakdown threshold of fibers is determined by intrinsic materials properties and parameters of
the technology applied. The aim of this paper is the identification of technological parameters that
are crucial for the fiber quality.
Fibers were drawn from preforms of Heraeus SWU with core material F300 and a low amount of
OH-. Both, the cladding (fluorine doped SiO2) to core diameter ratio (CCDR) and the drawing speed
were varied. CCDR values between 1.05 and 1.4 were used. Afterwards, the laser-induced damage
thresholds (LIDT) of the fibers were determined. For comparison, also samples from preforms,
which underwent different thermal treatments above the transition temperature, were tested with
respect to their damage resistivity. Single and multi pulse LIDT measurements were done in
accordance with the relevant ISO standards. Nd:YAG laser pulses with durations of 15 ns (1064 nm
wavelength) and 8.5 ns (532 nm) at a repetition rate of 10 Hz were utilized. For the fibers, LIDT
values (1-on-1, 1064 nm and 532 nm) increased with growing CCDR and with decreasing drawing
velocities.
Cleaning of paper is a challenging task due to the fact that a contamination should be removed and a fragile organic original material has to be preserved. Pulsed laser cleaning of artificially soiled Whatman© filter paper samples serving as models for historical paper was performed. Different cleaning strategies employing 8-ns laser pulses at 532 nm wavelength were applied to clean paper avoiding undesired effects like discoloration (yellowing) and mechanical deterioration of the substrate. Multi shot experiments with low-energy pulses were compared with single pulse investigations utilizing high pulse energies achieving a constant energy load incident on the samples in both cases. The cleaning efficiency and possible yellowing effects were evaluated by means of a multi spectral imaging system. An extensive microscopic analysis of the cleaned parts of the samples provided insight into the remaining soiling on the surface and in the bulk of the paper material after laser treatment. As a reference, a hard and a soft eraser were used to clean the samples.
The influence of different laser pulse lengths on the removal of a polymer layer from metal substrates was investigated. As model systems, doped poly(methylmetacrylate) (PMMA) on titanium and tungsten substrates were selected.
The ablation threshold and irradiation spot morphology of titanium and tungsten were compared for femtosecond (fs) and nanosecond (ns) laser irradiation and different pulse numbers. Nanosecond laser treatment resulted in a non-homogeneous surface morphology for both titanium and tungsten substrates. Femtosecond irradiation of tungsten revealed a homogeneous ablation spot with little changes in the surface morphology. For titanium, the formation of columnar structures within the irradiation spot was observed.
Two different dopant concentrations were used for PMMA to achieve an equal linear absorption coefficient for the femto- and nanosecond laser wavelengths of 790 and 1064 nm. The best results were achieved for the removal of doped PMMA by femtosecond laser irradiation, where only a minimal modification of the metal surface was detected. In the case of nanosecond laser exposure, a pronounced change of the structure was observed, suggesting that damage-free cleaning of the selected metal may only be possible using femtosecond laser pulses. Different experimental parameters, such as laser fluence, pulse repetition rate and sample speed were also investigated to optimize the cleaning quality of doped PMMA from tungsten substrates with femtosecond laser pulses.
A new approach is presented to quantify the so-called "heat affected zone" (HAZ) during
femtosecond laser pulse processing. Ablation of titanium nitride (TiN) thin films (~3 μm
thickness) by multiple femtosecond laser pulses (τ=130 fs, λ=800 nm) in air environment was
studied by means of two different surface analytical methods both being sensitive to chemical
alterations at the surface. Scanning Auger electron microscopy was applied for a visualization of the
spatial distribution of specific elements (Ti, O) within the laser-modified areas. The chemical state
of the irradiated surface was revealed by complementary x-ray photoelectron spectroscopy. Both
methods were used for a depth-profiling chemical analysis (tracking the elements Ti, N, O, and C)
using an Ar-ion beam for surface sputtering. In a narrow laser fluence range slightly below the
ablation threshold of TiN significant superficial oxidation can be observed leading to the formation
of substoichiometric TiO2-x. At fluences above the ablation threshold, an increased titanium
concentration is observed within the entire ablation craters. Following upon sputter removal the
elemental distribution into the depth of the nonablated material, the results allow an estimation of
the heat-affected zone for femtosecond laser ablation in air environment. According to our analyses,
the HAZ extends up to a few hundreds of nanometers into the nonablated material.
For pulse laser materials processing often optical step index and gradient index multimode fibers with core diameters ranging from 100 to 600 μm are used. The design of a high power fiber transmission system must take into account limitations resulting from both surface and volume damage effects. Especially, breakdown at the fiber end faces and self-focusing in the fiber volume critically influence the fiber performance. At least operation charts are desirable to select the appropriate fiber type for given laser parameters.
In industry-relevant studies the influence of fiber core diameter and end face preparation on laser-induced (surface) damage thresholds (LIDT) was investigated for frequently used all-silica fiber types (manufacturer LEONI). Experiments on preform material (initial fiber material) and compact specimens (models of the cladding and coating material) accompanied the tests performed in accordance with the relevant LIDT standards ISO 21254-1 and ISO 21254 2 for 1-on-1 and S-on-1 irradiation conditions, respectively. The relation beam diameter vs. LIDT was investigated for fused silica fibers. Additionally, laser-induced (bulk) damage thresholds of fused silica preform material F300 (manufacturer Heraeus) in dependence on external mechanical stress simulating fiber bending were measured. All experiments were performed with 10-ns laser pulses at 1064 and 532 nm wavelength with a Gaussian beam profile.
A new technique to fix bioceramic powder on a titanium alloy by using femtosecond laser pulses is presented. It is shown that gentle fixation of a bioactive dielectric material on a metallic model implant is successful. This is potentially a new tool for the improvement of bone prostheses. An advantage of the ultrashort pulses is the very low heat influx into the whole sample. There is only a very thin interaction zone during the fixing, which is the metal surface in contact with the ceramic layer. Neither the fixed ceramic particles nor the major part of the metal suffer any modification. The stability of the model implant (ceramic on metal) is investigated by rotating bending fatigue tests. No indication of a reduction of the mechanical stability compared to untreated metallic reference samples was found.
For many applications, optical multimode fibers are used for the transmission of powerful laser radiation. High light throughput and damage resistance are desirable. Laser-induced breakdown at the end faces of fibers can limit their performance. Therefore, the determination of laser-induced damage thresholds (LIDT) at the surface of fibers is essential.
Nanosecond (1064 nm and 532 nm wavelength) single-shot LIDT were measured according to the relevant standard on SiO2 glass preforms (Suprasil F300) as basic materials of the corresponding fibers. For 10 kinds of fused silica fibers (FiberTech) with core diameters between 180 µm and 600 µm, an illumination approach utilizing a stepwise increase of the laser fluence on a single spot was used. For both wavelengths, the LIDT values (0% damage probability) obtained by means of the two methods were compared. The influence of surface preparation (polishing) on damage resistance was investigated. For equal surface finishing, a correlation between drawing speed of the fibers and their surface LIDT values was found. In addition to the surface measurements, bulk LIDT were determined for the preform material.
Single and multi pulse laser-induced damage thresholds (LIDT) of core, cladding, and coating materials of high-power
optical multimode fibers were determined in accordance with ISO 11254 for 532 nm and 1064 nm wavelength in the 10-ns
pulse duration regime with spatial Gaussian beam shape. For all-silica fibers, LIDT increases with rising core diameter in a range between 100-600 µm for a constant cladding-core ratio of 1.2. The damage resistance of the low refracting cladding (0.3 % fluorine doped fused silica) is comparable to the undoped SiO2 core. Coating materials show significantly lower LIDT than light-guiding parts of the fibers.
Femtosecond lasers provide a novel method of attaching bioceramic material to a titanium alloy, thereby improving the quality of bone implants. The ultrashort 30 fs laser pulses (790 nm wavelength) penetrate a thin dip-coated layer of fine ceramic powder, while simultaneously melting a surface layer of the underlying metal. The specific adjustment of the laser parameters (pulse energy and number of pulses per spot) avoids unnecessary melting of the bioactive calcium phosphate, and permits a defined thin surface melting of the metal, which in turn is not heated throughout, and therefore maintains its mechanical stability. It is essential to choose laser energy densities that correspond to the interval between the ablation fluences of both materials involved: about 0.1-0.4 J cm-2. In this work, we present the first results of this unusual technique, including laser ablation studies, scanning electron microscopy and optical microscope images, combined with EDX data.
Bone implants made of metal, often titanium or the titanium alloy Ti6Al4V, need to be surface treated to become bioactive. This enables the formation of a firm and durable connection of the prosthesis with the living bone. We present a new method to uniformly cover Ti6Al4V with a thin layer of ceramics that imitates bone material. These calcium alkali phosphates, called GB14 and Ca10, are applied to the metal by dip coating of metal plates into an aqueous slurry containing the fine ceramic powder. The dried samples are illuminated with the 790 nm radiation of a pulsed femtosecond laser. If the laser fluence is set to a value just below the ablation threshold of the ceramic (ca. 0.4 J/cm²) the 30 fs laser pulses penetrate the partly transparent ceramic layer of 20–40 µm thickness. The remaining laser fluence at the ceramic–metal interface is still high enough to generate a thin metal melt layer leading to the ceramic fixation on the metal. The laser processing step is only possible because Ti6Al4V has a lower ablation threshold (between 0.1 and 0.15 J/cm²) than the ceramic material. After laser treatment in a fluence range between 0.1 and 0.4 J/cm², only the particles in contact with the metal withstand a post-laser treatment (ultrasonic cleaning). The non-irradiated rest of the layer is washed off. In this work, we present results of a successful ceramic fixation extending over larger areas. This is fundamental for future applications of arbitrarily shaped implants.
The formation of laser-induced periodic surface structures (LIPSS) upon irradiation of fused silica with multiple irradiation sequences consisting of five Ti:sapphire femtosecond (fs) laser pulse pairs (150 fs, 800 nm) is studied experimentally. A Michelson interferometer is used to generate near-equal-energy double-pulse sequences with a temporal pulse delay from -20 to +20 ps between the cross-polarized individual fs-laser pulses (~0.2 ps resolution). The results of multiple double-pulse irradiation sequences are characterized by means of Scanning Electron and Scanning Force Microscopy. Specifically in the sub-ps delay domain striking differences in the surface morphologies can be observed, indicating the importance of the laser-induced free-electron plasma in the conduction band of the solids for the formation of LIPSS.
Cleaning of artificially soiled paper using nanosecond, picosecond and femtosecond laser pulses
(2010)
Cleaning of cultural assets, especially fragile
organic materials like paper, is a part of the conservation
process. Laser radiation as a non-contact tool offers
prospects for that purpose. For the studies presented here,
paper model samples were prepared using three different paper
types (pure cellulose, rag paper, and wood-pulp paper).
Pure cellulose serves as reference material. Rag and woodpulp
paper represent essential characteristics of the basic
materials of real-world artworks. The papers were mechanically
soiled employing pulverized charcoal. Pure and artificially soiled paper samples were treated with laser pulses of
28 fs (800 nm wavelength) and 8–12 ns (532 nm) duration in
a multi pulse approach. Additionally, the cellulose reference
material was processed with 30 ps (532 nm) laser pulses.
Damage and cleaning thresholds of pure and soiled paper
were determined for the different laser regimes. Laser working
ranges allowing for removal of contamination and avoiding
permanent modification to the substrate were found.
The specimens prior and after laser illumination were characterized
by light-optical microscopy (OM) and scanning
electron microscopy (SEM) as well as multi spectral imaging
analysis. The work extends previous nanosecond laser
cleaning investigations on paper into the ultra-short pulse
duration domain.
Single- and two-color double-fs-pulse experiments were performed on titanium to study the dynamics of the formation of laser-induced periodic surface structures (LIPSS). A Mach-Zehnder inter-ferometer generated polarization controlled (parallel or cross-polarized) double-pulse sequences in two configurations – either at 800 nm only, or at 400 and 800 nm wavelengths. The inter-pulse delays of the individual 50-fs pulses ranged up to some tens of picoseconds. Multiple of these single- or two-color double-fs-pulse sequences were collinearly focused by a spherical mirror to the sample surface. In both experimental configurations, the peak fluence of each individual pulse was kept below its respective ablation threshold and only the joint action of both pulses lead to the formation of LIPSS. Their resulting characteristics were analyzed by scanning electron microscopy and the periods were quantified by Fourier analyses. The LIPSS periods along with the orientation allow a clear identification of the pulse which dominates the energy coupling to the material. A plasmonic model successfully explains the delay-dependence of the LIPSS on titanium and confirms the importance of the ultrafast energy deposition stage for LIPSS formation.
A great number of Central Asian wall paintings, archeological materials, architectural fragments, and textiles, as well as painting fragments on silk and paper, make up the so called Turfan Collection at the Asian Art Museum in Berlin. The largest part of the collection comes from the Kucha region, a very important cultural center in the third to ninth centuries. Between 1902 and 1914, four German expeditions traveled along the northern Silk Road. During these expeditions, wall paintings were detached from their original settings in Buddhist cave complexes. This paper reports a technical study of a wall painting, existing in eight fragments, from the Buddhist cave no. 40 (Ritterhöhle). Its original painted surface is soot blackened and largely illegible. Grünwedel, leader of the first and third expeditions, described the almost complete destruction of the rediscovered temple complex and evidence of fire damage. The aim of this case study is to identify the materials used for the wall paintings. Furthermore, soot deposits as well as materials from conservation interventions were of interest. Non-invasive analyses were preferred but a limited number of samples were taken to provide more precise information on the painting technique. By employing optical and scanning electron microscopy, energy dispersive X-ray spectroscopy, micro X-ray fluorescence spectroscopy, X-ray diffraction analysis, and Raman spectroscopy, a layer sequence of earthen render, a ground layer made of gypsum, and a paint layer containing a variety of inorganic pigments were identified.
This Conference Proceedings volume contains a selection of the contributions presented in Symposium C “Laser-material interactions for tailoring future applications” organized during the annual Spring Meeting of the European Materials Research Society (E-MRS) held from May 2nd to 6th 2016 in the Lille Grand Palais, France.
Until the end of the 1980s many wooden artworks underwent surface treatment by liquid preservatives, e.g. Hylotox-59. DDT (dichlorodiphenyltrichloroethane) crystal structures are formed on the wooden surfaces by the "blooming" of chlorine compounds by time. In addition to an aesthetic disturbance, it is assumed that DDT represents a health risk. Therefore, the removal of DDT crystals from the surfaces is requested. Contaminated wood with natural biocide ageing, gilded and wood carved elements and wooden samples with paint layers were provided by the Schlossmuseum Sondershausen, Germany. Laser cleaning on selected surface areas on the objects was done by means of femtosecond and nanosecond laser pulses. For the same object, cleaning results using 30-fs laser pulses at 800 nm wavelength are compared to findings utilizing 10-ns laser pulses at 1064 nm wavelength. Before and after laser treatment, chlorine measurements at the same surface position were done by X-ray fluorescence analysis (XRF) as an indicator for the presence of DDT. In this way, pointwise chlorine depletion rates can be obtained for the different pulse duration regimes and wavelengths. Additionally, the object surfaces were examined using optical microscopy and multi spectral imaging analysis.
The cleaning of aged silk fibers poses a common challenge in the conservation of textiles, since traditional cleaning techniques often yield unsatisfactory results or even harm objects. In this regard, cleaning objects with laser radiation is a promising addition to the range of available methods. Due to it being contactless, even brittle and touch-sensitive objects with disfiguring or harmful soiling could potentially be cleaned and therefore made accessible for research and presentation. Examples of treatment have sometimes shown spectacular results. Still there is some skepticism concerning the safety of this treatment for textile materials, which has been strengthened through previous 532 nm wavelength nanosecond laser cleaning studies on silk fibers. Taking these published results into account, the range of examined laser parameters has been extended in this study, from 532 nm nanosecond laser to 1064 nm nanosecond and even 800 nm femtosecond laser, reevaluating the effect of this treatment on the fibers. The physicochemical processes taking place on the silk fibers when cleaning with lasers are complex and still not fully understood. The aim of this project was therefore to bring more clarification about potential effects of those processes on the condition of silk samples treated with a set of different parameters for wavelength, pulse duration, energy density and number of pulses per spot. It also looks at the influence of the presence of soiling on the results. The analysis of potential effects was then carried out using statistical methods and advanced analytics. Scanning electron microscopy, Fourier-transform infrared spectroscopy and colorimetry technology provided the required insights to better assess the effects. Results show that laser cleaning of silk fibers, like most other conventional cleaning techniques, is not completely without risk, but knowing what the possible effects are helps making decisions on whether the benefits of the technique used justify these risks.
In this study, femtosecond laser-induced sub-micrometer structures are generated to modify polyethylene (PE) surface topographies. These surfaces were subjected to bacterial colonization studies with Escherichia coli and Staphylococcus aureus as test strains. The results reveal that the nanostructures do not influence S. aureus coverage, while the adhesion of E. coli is reduced.