Online (passive) thermographic inspection of overlap joints of aluminium and zinc coated steel sheets made by cold metal Transfer weld brazing process was explored. Different experimental Trials were conducted for demonstrating the feasibility of thermographic inspection to detect the porosities, improper weld bead and to differentiate the pre weld temperature. The whole process was monitored using infrared cameras in different wavelength region.
Image analysis algorithms were developed to reconstruct the thermal images that contain the signatures of the weld defects and to extract the pre weld temperature and ist evolution with distance from the centre of the weld torch. Post-weld radiography lends strong Support to the observations.
In this study, the feasibility of using non-contact Infrared thermography as a potential tool to monitor the CMT welding process is explored. The presence of internal defects such as porosity, lack of filler material deposition and formation of improper weld bead produce perturbations in the surface temperature which can be identified using an Infrared thermography technique. We present recent results obtained from online monitoring of the the dissimilar joining using CMT weld brazing of Aluminum and Steel using a transmission mode measurement approach. The effect of loss of zinc coating on the weldability of the cold metal transfer joining of aluminum to galvanised steel was investigated. A correlation between measured online thermal indications with the weld anomalies is successfully attempted and the results are compared with the conventional post-weld NDT inspection methods.
In-line laser thermography for crack detection at elevated temperature: A Numerical modeling study
(2016)
The detection and characterization of cracks prior to damage is a technologically and economically highly significant task and is of very importance when it comes to safety-relevant structures. The evaluation of a components life is closely related to the presence of cracks in it. Laser thermography has already high capability for the detection of surface cracks and for the characterization of the geometry of artificial surface flaws in metallic samples. Crack detection in metallic samples at high temperature is highly significant in present manufacturing scenario. During the casting process of billets, surface cracks form, due to the suboptimal cooling rates. These cracks reduce value of the billet and must be removed using machining process after cooling. This secondary process increases cost of manufacturing. In this work we developed a heat transfer model for laser thermography to study the thermal contrast variation with increase in surface temperature using finite element method (FEM). Here we are mainly concentrating the capability of the scanning laser thermography in crack detection which are in elevated temperature and numerical modeling study of thermal contrast variation of crack with respect increase in metal surface temperature. This study is important to prove the capability of laser thermography for crack detection in elevated temperature. Since we are using High power CW Laser to local heating of the metal surface which can give relatively high thermal contrast even at elevated temperature compare to other heating source. Here we are modeled and simulated 2D laser scanning across a surface breaking crack and developed an algorithm to produce the vicinity of crack. The algorithm we developed applied for various surface temperature data. And validated the credibility of the algorithm with experimental data.
The aim of this work is to illustrate the contribution of signal processing techniques in the field of Non-Destructive Evaluation. A component’s life evaluation is inevitably related to the presence of flaws in it. The detection and characterization of cracks prior to damage is a technologically and economically significant task and is of very importance when it comes to safety-relevant measures. The Laser Thermography is the most effective and advanced thermography method for Non-Destructive Evaluation. High capability for the detection of surface cracks and for the characterization of the geometry of artificial surface flaws in metallic samples of laser thermography is particularly encouraging. This is one of the non- contacting, fast and real time detection method. The presence of a vertical surface breaking crack will disturb the thermal footprint. The data processing method plays vital role in fast detection of the surface and sub-surface cracks.
Currently in laser thermographic inspection lacks a compromising data processing algorithm which is necessary for the fast crack detection and also the analysis of data is done as part of post processing. In this work we introduced a raw data based image processing algorithm which results precise, better and fast crack detection. The algorithm we developed gives better results in both experimental and modeling data. By applying this algorithm we carried out a detailed investigation Variation of thermal contrast with crack parameters like depth and width. The algorithm we developed is applied for various surface temperature data from the 2D scanning model and also validated credibility of algorithm with experimental data.
The detection of cracks before the failure is highly significant when it comes to safety-relevant structures. Crack detection in metallic samples at high surface temperature is one of the challenging situation in manufacturing industries.
Laser thermography has already proved its detection capability of surface cracks in metallic samples at room temperature. In this work a continuous wave (CW) laser use to generate a laser, which is using to scan the metal surface with notch.
The corresponding heat distribution on the surface monitored using infrared thermal (IR) camera. A simplified 3D model for laser thermography is developed and validated with experimental results. A dedicated image processing algorithm developed to improve the detectability of the cracks. To understand the dependency of surface temperature, laser power, laser scanning speed etc. in defect detection, we carried out parametric studies with our validated model. Here we Report the capability of laser thermography in crack detection at elevated temperature.