Carbohydrate films on gold based on dimannoside thiols (DMT) were prepared, and a complementary surface chemical analysis was performed in detail by X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), near-edge X-ray absorption fine structure (NEXAFS), FT-IR, and contact angle measurements in order to verify formation of ω-carbohydrate-functionalized alkylthiol films. XPS (C 1s, O 1s, and S 2p) reveals information on carbohydrate specific alkoxy (C–O) and acetal moieties (O–C–O) as well as thiolate species attached to gold. Angle-resolved synchrotron XPS was used for chemical speciation at ultimate surface sensitivity. Angle-resolved XPS analysis suggests the presence of an excess top layer composed of unbound sulfur components combined with alkyl moieties. Further support for DMT attachment on Au is given by ToF-SIMS and FT-IR analysis. Carbon and oxygen K-edge NEXAFS spectra were interpreted by applying the building block model supported by comparison to data of 1-undecanethiol, poly(vinyl alcohol), and polyoxymethylene. No linear dichroism effect was observed in the angle-resolved C K-edge NEXAFS.
We investigated the ageing of amine-terminated
self-assembled monolayers (amine-SAMs) on different silica
substrates due to exposure to different ambient gases,
pressures, and/or temperatures using time-of-flight secondary
ion mass spectrometry (ToF-SIMS) with principal component
analysis and complementary methods of surface
analysis as X-ray photoelectron spectroscopy (XPS) and
near edge X-ray absorption fine structure (NEXAFS). The
goal of this study is to examine the durability of primary
amine groups of amine-SAMs stored in a user laboratory
prior to being used as supports for biomolecule immobilization
and other applications. We prepared amine-SAMs on
the native oxides of silicon wafers and glass slides using 3-
aminopropyl triethoxysilane, by using optimized conditions
such as anhydrous organic solvent and reaction time scale of
hours to avoid multilayer growth. Selected commercial
amine-SAM slides have been investigated, too. When the
amine-SAMs are exposed to air, oxygen incorporation
occurs, followed by formation of amide groups. The formation
of oxygen species due to ageing was proved by ToFSIMS,
XPS, and NEXAFS findings such as CNO- secondary
ion emission at m/z 42, observation of the N 1s HNC=O
component peak at 400.2400.3 eV in XPS, and, last but not
least, by formation of a π*(HNC=O) resonance at 401 eV in
the N K-edge X-ray absorption spectrum. It is concluded
that the used multi-method approach comprising complementary
ToF-SIMS, XPS, and NEXAFS analyses is well
suited for a thorough study of chemical aspects of ageing
phenomena of amine-SAM surfaces.
Functionalised surfaces are of interest in many fields, e.g. in biomedicine, materials science and molecular electronics. In this study a series of self-assembled aliphatic and aromatic monolayers on gold substrates with terminal amino groups was investigated. Four different thiol molecules were used: aliphatic 11-aminoundecane-1-thiol (AUDT), aromatic 4-aminobenzenethiol (ABT) and aromatic ω-amino thiols with an alkyl spacer as 4-aminophenylbutane-1-thiol (APBT) and 3-(4''-amino-1,1':4',1''-terphenyl-4-yl)propane-1-thiol (ATPT). Evaluation of N 1s XPS data revealed that on the aromatic self-assembled monolayers (SAMs) amino groups exist preferentially as primary amines, whereas on the aliphatic SAM protonated and/or hydrogen-bonded amines are the major species. This result is crosschecked by N K edge near edge X-ray absorption fine structure (NEXAFS) spectroscopy and can be rationalised by the different basicity of aliphatic and aromatic amines.
The chemical composition of the functional surfaces of substrates used for microarrays is one of the important parameters that determine the quality of a microarray experiment. In addition to the commonly used contact angle measurements to determine the wettability of functionalized supports, X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) are more specific methods to elucidate details about the chemical surface constitution. XPS yields information about the atomic composition of the surface, whereas from ToF-SIMS, information on the molecular species on the surface can be concluded. Applied on printed DNA microarrays, both techniques provide impressive chemical images down to the micrometer scale and can be utilized for label-free spot detection and characterization. Detailed information about the chemical constitution of single spots of microarrays can be obtained by high-resolution XPS imaging.
We present a new synchrotron X-ray photoelectron spectroscopy strategy for surface chemical analysis of materials. Our approach is based on the acquisition of photoelectron spectra at constant kinetic energies with the help of a tunable synchrotron X-radiation source. This ensures both constant and tunable information depth for all elements in a very thin organic layer. Many of the problems known to XPS depth profiling using laboratory equipment are thereby avoided. Using our methodology, the 95% information depth, z95%, can be tuned down to about 0.7 nm in organic materials. The upper limit in our study at the HE-SGM monochromator dipole magnet beamline at the synchrotron radiation source BESSY II is about 4.3 nm. Elemental quantification is achieved through relative sensitivity factors (RSF) specific to the measurement conditions, determined either with the help of calculated photoionization cross sections and inelastic mean free paths or experimentally. The potential of the technique is demonstrated for the in-depth analysis of plasma deposited nitrogen-rich organic thin films used in biomedical applications.
Nitrogen rich plasma polymer films (L-PPE:N) were prepared by low-pressure RF plasma using a 1:1 mixture of ethylene and ammonia and aged for 345 d in four different ambient conditions: (i) at room temperature (RT) in air; (ii) at RT in nitrogen; (iii) at -20?°C in air and; (iv) at –20 °C in nitrogen. The films were analyzed by X-ray photoelectron spectroscopy (XPS) and by time-of-flight secondary ion mass spectrometry (ToF-SIMS) at various intervals over the duration of the experiment. The ageing of primary amines, NH2, was followed by chemical derivatization with 4-trifluoromethyl benzaldehyde. Storage at –20 °C, mostly independently of ambient atmosphere, slowed down ageing to almost undetectable levels as evaluated by the analytical methods used for this study.
The determination of amino groups on surfaces capable of binding biomolecules is important for the understanding and optimization of technologically relevant coupling processes. In this study, three different types of amino-functionalized model surfaces, amino thiolate on Au, amino siloxane on Si, and polyethylene (PE) foils and films reacted with 1,2-diaminoethane (DAE) were derivatized with 3,5-bis(trifluoromethyl)phenyl isothiocyanate. Subsequently, these samples were analyzed by chemical derivatization X-ray photoelectron spectroscopy (CD-XPS) and near-edge X-ray absorption fine structure spectroscopy (NEXAFS). The determination of amino groups by this analytical approach allows gaining insight into the availability of groups on surfaces that can actually serve as attachment sites for biomolecules in technical applications. In the case of the amino thiolate on Au, almost 90% of the expected amino groups were detected by CD-XPS. Investigation of the amino siloxane films revealed lower yields for the derivatization reaction in the order of 30%. The lowered reaction yields are thought to be due to interactions between the amino siloxane`s amino and silanol groups or the underlying substrate, making them inaccessible to the derivatization agent. The aminated PE samples are characterized by a complex surface chemistry and structure, and reaction yields of the derivatization reaction cannot be unequivocally derived. However, 1-3% of the total carbon atoms in the surface layer were found to be bound to amino groups accessible to the derivatization agent. It can be concluded that, depending on the detailed character of the investigated amino-terminated surface, the amount of amino groups accessible to CD-XPS can be substantially lower than the total amount of amino groups present at the surface.
A first inter-laboratory comparison was conducted to demonstrate and document the capability of interested laboratories to measure the fraction of C—OH species on a plasma oxidised poly(propylene) sample by using a chemical derivatisation XPS approach. This report presents the results from that inter-laboratory comparison and includes the data received for the measured values and their associated standard deviations of laboratory means, at a 95% confidence level. The measurements were guided by a protocol developed within the group before and summarised shortly in the paper. Standard deviations that may characterise the state-of-the-art for the nominally simple and rather often practised case of TFAA chemical derivatisation XPS of C—OH species on a plasma oxidised polyolefin surface are calculated following ISO 5725-2:1994. The main conclusion is that the associated degree of equivalence reached by the participating laboratories in this comparison is still low. Further research to improve chemical derivatisation XPS protocols is mandatory.
The wettability of the surfaces inside the microchannels of a microfluidic device is an important property considering a liquid flows through them. Contact angle measurements usually applied to test the wettability of surfaces cannot be used for an analysis of microchannel walls within microfluidic devices. A workaround is the use of surface analytical methods, which are able to reach points of interest in microchannels and may provide information on the surface chemistry established there. In calibrating these methods by using flat polymer wafers, where the contact angle can be measured as usual, data measured in real microchannels can be evaluated in terms of wetting properties. Reference wafers of bisphenol-A polycarbonate, a polymeric material that is often used in fluidic microdevice fabrication, were treated under different oxygen plasma conditions. The modified surfaces were characterized by using XPS, time of flight (ToF)-SIMS and atomic force microscope (AFM). Surface chemistry and surface topography have been correlated with contact angle measurements. In addition, effects of ageing or rinsing after plasma treatment have also been investigated.
Methods for characterization of epoxy-functionalized substrates used for microarray applications, prepared by silanization with 3-glycidoxypropyltrimethoxysilane, have been developed. Contact angle measurements, X-ray photoelectron spectroscopy, time of flight secondary ion mass spectrometry and fluorescence based methods have been applied to investigate these epoxy-functionalized microarray substrates. The surface density of epoxy-functionalized glass slides was investigated by fluorescence labeling of surface species utilizing Rhodamine 110 as fluorescence probe.