The influence of heat treatment on pit corrosion needs to be considered to guarantee reliability and safety during the injection of compressed emission gasses – mainly containing CO2 – into deep geological layers (CCS-technology, Carbon Capture and Storage). In laboratory experiments different heat treated steels used as injection pipe with 13% Chromium and 0.46% Carbon (X46Cr13, 1.4034) as well as 0.2% Carbon (X20Cr13, 1.4021) were tested. Also X5CrNiCuNb16-4 (1.4542) was investigated as typical steel used for geothermal pumps. Keeping stable environmental conditions in laboratory experiments the samples were exposed to the distinct synthetic aquifer environment saturated with technical CO2 at a flow rate of 3 l/h for up to 6 months.
Independent of the exposure time the least amount of pits is found on hardened steels with martensitic microstructure where X5CrNiCuNb16-4 shows fewer pits than X46Cr13 and X20Cr13.
Regarding steels with similar Cr-content the higher Ccontent in 1.4034 results in fewer pits compared to 1.4021.
In practice usually thin-walled cylindrical silos are supported locally at the bottom rim of the shell. In this area a stress concentration may occur, which is responisble for buckling of the shell. In the currently applied codes, there is no information, how to analyze the load-bearing capacity of theselocally supported shells. In this paper, a new design formula is given for determining the load-bearing capacity.
Structuring of dielectric and metallic materials with ultrashort laser pulses between 20 fs and 3 ps
(1997)
Laser-micromachining of barium aluminum borosilicate glass, fused silica and stainless steel has been extended down to a pulse duration of 20 fs generated by a Ti:sapphire laser system at a wavelength of 0.8 micrometer. A systematic study shows that, below 100 fs, an enhanced precision and a substantial decrease of the ablation threshold fluence in comparison to pulse laser processing with pulses in the picosecond and nanosecond range could be achieved. The physical mechanism and the technical relevance of this novel microtechnology is discussed.