Schlagworte
- Buoyancy (1)
- CO2- and Nd:YAG laser (1)
- Corrosion resistance (1)
- Electromagnetic weld pool control (1)
- High strength steels (1)
- Higher manganese content (1)
- Laser beam welding (1)
- Laser welding (1)
- Lorentz force (1)
- Marangoni convection (1)
An oscillating (AC) magnet field was used to suppress porosity formation and to stabilize the surface of the weld pool in bead-on-plate partial penetration 4.4 kW Nd:YAG laser beam welding of AW-5754 plates in PA position. The magnet was mounted on the laser welding head. The magnet field (up to 0.4 T and 10 kHz) was oriented perpendicular the welding direction.
The analysis of the weld cross-sections and x-ray images shows a drastic reduction (up to 90%) of porosity contents in the welds. The observed effects can be explained in terms of electromagnetically (EM)
induced 'Archimedes' forces as well as the EM stirring flow in the weld pool. Moreover, usage of AC magnetic fields results in a significant reduction (up to 50%) of the surface roughness of the welds. This effect can be explained in terms of electromagnetic (EM)
contribution to the surface tension (the Garnier-Moreau effect)
A three-dimensional turbulent steady state numerical model was used to investigate the influence of a stationary magnetic field during partial penetration high power laser beam keyhole welding of thick aluminum parts. COMSOL Multiphysics was used to calculate the three-dimensional heat transfer, fluid dynamics and electromagnetic field equations. Thermo-capillary (Marangoni) convection at the upper weld pool surface, natural convection due to gravity and latent heat of solid-liquid phase transition were taken into account. It shows that the application of steady magnetic fields produces a braking Lorentz force in the melt based on the Hartmann effect. The flow pattern in the weld pool and also the temperature distribution and associated weld pool geometry thus change significantly. Convective flows in the melt can effectively be suppressed and the influence of thermo-capillary flow is diminished to a thin surface layer.
Thick-walled pipes made of steel are the basis of a large number of components in mechanical and installation engineering, e.g. for hydraulic components, in power station technology or in the petroleum industry. Particularly when strict positional and shape tolerances are demanded, the classical manufacturing process is chip-producing machining from the solid material. However, this is time-intensive and material-intensive. The laser/GMA hybrid processes with modern high-power lasers are a suitable alternative. With these processes, it is currently possible to weld components with a wall thickness up to approx. 15 mm with little distortion in one pass. However, in initial experiments, solidification cracks with longitudinal and vertical orientations in relation to the welding direction, so-called central line cracks, were established in welds on pipes. Within the framework of a research project, it was possible to determine the cause of the cracking and to find measures in order to avoid it. The technical boundary conditions could be complied with in this respect. The article gives an overview of the research project and the essential results.
In the rough conditions in the fabrication of automobile bodies, it is not always possible to avoid welding-induced imperfections such as cracks during the resistance spot welding of high-strength steels. In this respect, the influence of such cracks on the fatigue strength particularly of modern high-strength austenitic steels is not sufficiently well-known at present. The influence of welding cracks with various positions and formations was therefore investigated within the framework of this paper. In this case, the analysis of the standardised stiffness courses of specimens and the comparison of the numbers of failure stress cycles served to prove that the surface cracks produced without any spatter in the centre, interfacial region and peripheral region of the weld nugget do not have any negative influence on the fatigue strength of the high-strength austenitic material investigated here. Specimens which were manufactured with welding spatter and exhibit cracks in the peripheral region show considerably higher numbers of failure stress cycles than crack-free reference specimens.