Filtern
Erscheinungsjahr
Dokumenttyp
Sprache
- Englisch (33)
Schlagworte
- Defects (33) (entfernen)
Organisationseinheit der BAM
- 6 Materialchemie (9)
- 8 Zerstörungsfreie Prüfung (9)
- 6.4 Materialinformatik (7)
- 8.5 Röntgenbildgebung (7)
- 9 Komponentensicherheit (4)
- 9.4 Integrität von Schweißverbindungen (4)
- 5 Werkstofftechnik (3)
- 5.1 Mikrostruktur Design und Degradation (3)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
Eingeladener Vortrag
- nein (7)
A new titanium alloy improving the operation of implants additively manufactured and including laterally closed lattice structures is proposed. The new alloy possesses an increased affinity to the bone. The measured bone–interface implant (BII) of less than 10 mm and bone–implant contact (BIC) of 95% demonstrated an excellent osseointegration. Furthermore, since additive manufacturing naturally leads to a high-roughness surface finish, the wettability of the implant is increased. The combination of these factors is pushing ossification beyond its natural limits. In addition, the quality and speed of the ossification and osseointegration in/around laterally closed lattice implants open the possibility of bone spline key of prostheses. This enables the stabilization of the implant into the bone while keeping the possibility of punctual hooks allowing the implant to be removed more easily if required.
The different defect types on SiC samples are measured with various measurement methods including optical and tactile methods. The defect types investigated include particles, carrots and triangles and they are analyzed with imaging ellipsometry, coherent Fourier scatterometry and atomic force microscopy. Each of these methods measures different properties of the defects and they all together contribute to a complete analysis.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. Recent experimental studies show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams in combination with density functional theory provide a natural route to study these chemically driven defects. Our results show, however, that direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation. Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe-Nb solid solutions and to identify in a joint study with experiments conditions in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
Understanding segregation to grain boundaries, and eventually their defect phase diagrams, is critical to enable rational grain boundary engineering for alloys design. Here, we discuss the progress and challenges one may face when generating such a database of defect-solute interactions, in the context of studying of grain boundary segregation of solutes and impurities in Fe GBs. To compute the large number of relevant defect-solute interactions we have performed high-throughput ab initio calculations using efficient and highly automated workflows using pyiron. We study has been performed across a representative set of coincident-site-lattice (CSL) type tilt GBs. Based on the large ab-initio datasets, we extract and analyse the chemical and structural trends observed in the solute segregation behaviour across the periodic table. The features which are most important in evaluating site segregation are presented and discussed.
Thermodynamic bulk phase diagrams have become the roadmap used by researchers to identify alloy compositions and process conditions that result in novel materials with tailored microstructures. On the other hand, recent progress in experimental atomic-scale characterization techniques allows one to study the local chemical composition at individual defects such as interfaces, grain boundaries, dislocations and surfaces. They show that changes in the alloy composition can drive not only transitions in the bulk phases present in a material, but also in the concentration and type of defects they contain. Defect phase diagrams, using chemical potentials as thermodynamics variables, provide a natural route to study these chemically driven defects. Our results show, however, that the direct application of thermodynamic approaches can fail to reproduce the experimentally observed defect formation.
Therefore, we extend the concept to metastable defect phase diagrams to account for kinetic limitations that prevent the system from reaching equilibrium. We use ab initio calculations based on density functional theory to quantify the extension of regions where defect formation is expected. We successfully applied this concept to explain the formation of large concentrations of planar defects in supersaturated Fe2Nb Laves phases. In addition, we identify in a joint study with experiments conditions and structures in Mg-Al-Ca alloys for defect phase occurrence. The concept offers new avenues for designing materials with tailored defect structures.
X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, they can detect objects with size above a few wavelengths of the radiation.
Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads.
The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models.
We hereby show the application of non-destructive X-ray refraction radiography (SXRR, 2D mapping also called topography) to problems in additive manufacturing:
1) Porosity analysis in PBF-LM-Ti64. Through the use of SXRR, we could not only map the (very sparse) porosity distribution between the layers and quantify it, but also classify, and thereby separate, the filled porosity (unmolten powder) from the keyhole and gas pores (Figure 1).
2) In-situ heat treatment of laser powder bed fusion PBF-LM-AlSi10Mg to monitor microstructure and porosity evolution as a function of temperature (Figure 2). By means of SXRR we indirectly observed the initial eutectic Si network break down into larger particles as a function of increasing temperature. We also could detect the thermally induced porosity (TIP). Such changes in the Si-phase morphology upon heating is currently only possible using scanning electron microscopy, but with a much smaller field-of-view. SXRR also allows observing the growth of some individual pores, usually studied via X-ray computed tomography, but again on much smaller fields-of-view.
Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the defect distribution and the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.
Critical defects, also known as device killers, in wide bandgap semiconductors significantly affect the performance of power electronic devices. We used the methods imaging ellipsometry (IE) and white light interference microscopy (WLIM) in a hybrid optical metrology study for fast and non-destructive detection, classification, and characterisation of defects in 4H–SiC homoepitaxial layers on 4H–SiC substrates. Ellipsometry measurement results are confirmed by WLIM. They can be successfully applied for wafer characterisation already during production of SiC epilayers and for subsequent industrial quality control.
What is meant by ‘Micro Non-Destructive Testing and Evaluation’? This was the central subject of debate in this Special Issue.
At present, sub-millimeter-size components or even assemblies are pervading the industrial and scientific world. Classic examples are electronic devices and watches (as well as parts thereof), but recent examples encompass additively manufactured lattice structures, stents, or other microparts. Moreover, most assemblies contain micro-components. Testing such components or their miniaturized parts would fit well within the topic of micro non-destructive testing and evaluation.
In all cases, performance and integrity testing, quality control, and dimensional tolerances need to be measured at the sub-millimeter level (ideally with a spatial resolution of about a micron); most of the time, such features and components are embedded in much larger assemblies, which also need to be taken into account. The solution to this dilemma (i.e. measuring large parts with high resolution) depends on the part and on the problem under consideration.
Another possible definition of micro non-destructive testing and evaluation can relate to the characterization of micro-features (e.g., the microstructure) in much larger specimens, such as damage in concrete cores or porosity in additively manufactured components. A further aspect is the use of microscopic probes to evaluate macroscopic properties. This is the case, for instance but not at all exclusively, in the use of diffraction techniques to determine macroscopic stress.
The splits between testing and characterization at the micro-level (or of micro parts) from one side and handling of macroscopic assemblies on the other represent a great challenge for many fields of materials characterization. On top of that, including the use of microscopic methods to test integrity would add a further level of complexity.
Imaging, mechanical testing, non-destructive testing, measurement of properties, structural health monitoring, and dimensional metrology all need to be re-defined if we want to cope with the multi-faceted topic of micro non-destructive testing and evaluation.
The challenge has already been accepted by the scientific and engineering communities for a while but is still far from being universally tackled. This Special Issue yields an interesting answer to the questions posed above. It presents the progress made and the different aspects of the challenge as well as at indicates the paths for the future of NDT&E.