Experimental and analytical investigation of the TMF-HCF lifetime behavior of two cast iron alloys
(2017)
The combined loading Thermomechanical Fatigue (TMF) with High Cycle Fatigue (HCF) has been experimentally investigated for two cast iron alloys. Both alloys contain globular graphite nodules but the first one has a ferritic structure while the second one has an austenitic crystal structure. In particular, the influences of the HCF frequency, of the HCF loading amplitude and of the location of the superposed HCF cycles have been investigated. It was observed that the HCF frequency has a limited impact on the fatigue life. On the other side, the HCF-strain amplitude has a highly non-linear influence on the fatigue life. The experimental results can be understood in terms of a fracture mechanics based damage mechanism: Cracks quickly initiate due to the TMF loading and the growth of the cracks up to a few mm controls the fatigue life. If HCF-loading cycles are superposed, cyclic crack propagation dramatically accelerates after a threshold has been reached. This threshold is regarded as controlling the fatigue life reduction. The previous ideas have been expressed in a model that can be very simply applied to estimate the fatigue life reduction ratio due to the superposed HCF cycles. It only contains two adjustable parameters and can be combined with any TMF life assessment model.
A cross-section sample of the friction film formed on top of a disc during a brake testing procedure against Polymer Matrix Composite pads was made using a Focused Ion Beam (FIB). The FIB-cut sampled the "third body" magnetite layer and the upper part of the cast iron disc containing a graphite flake. Images of the sample examined in a Energy Filtered Transmission Electron Microscope captured an instant view of the important role of the graphite flakes in magnetite formation, where few layer graphene batches interacted with the iron border promoting cracking and oxidation along the graphite–iron interface. The resulting nano-scale interlayer of magnetite and strongly disordered graphite formed a third body which yielded adequate brake performance.
The tribological behaviour of unfilled thermoplastic polyurethane (TPU) and a polymer sphere filled (TPUG) thermoplastic polyurethane have been studied under oscillating sliding condition against cast iron as a counterpart. In the case of unfilled TPU, the wear mechanisms are dominated by particle detachment and roll formation. In principle, TPUG also showed a similar wear mechanism as that of unfilled TPU; in addition, particle pull-out and delamination are also observed. Wear volume of TPUG was significantly higher than that for the unfilled TPU and this is attributed to the different material removal processes taking place in the material during sliding. The polymer spheres as a filler material deteriorated the wear resistance of TPU because of improper adhesion and bonding of filler in the TPU matrix and therefore it contributed to more wear. In case of TPU the friction behaviour was strongly dependant on the temperature and surface roughness of the counter body. The results showed that below the glass transition temperature higher friction values are observed with higher counter body surface roughness. However, above the glass transition temperature, higher friction values are observed with a smoother surface roughness of the counter body. In case of TPUG, the friction behaviour was not significantly dependent on surface roughness of the counter body.
TMF tests were carried out on EN-GJSA-XNiSiCr35-5-2 at constant minimum temperature (400 °C) and varying maximum temperatures (Tmax = 700 °C, 800 °C, 900 °C) with hold times of 180 s at Tmax and two phase angles (in-phase (IP), 180° out-of-phase (OP)). The results showed a comparable strength under OP- and IP-TMF loading. At Tmax = 700 °C and 900 °C, the lifetime in IP-tests was slightly longer than that of OP-tests, while it is vice versa at Tmax = 800 °C. The IP-tests at Tmax = 900 °C showed a similar lifetime as OP-tests at Tmax = 700 °C and 800 °C, which was unexpected for such a high testing temperature. All IP-tests at Tmax = 900 °C showed a continuous cyclic softening from the beginning on, which was different from all other testing conditions. Complementary metallographic investigations indicated that under this test condition, intergranular creep damage is present in the volume of the test pieces.
The fatigue behaviour of cast iron is usually investigated on machined specimens. Components of cast iron, however, have a casting skin; therefore the investigation of the influence of the casting skin on the lifetime is of interest. To study this influence isothermal fatigue tests were carried out on heat-resisting spheroidal graphite cast iron EN GJS SiMo 4.05 in 4–point-bending set-up at 400 °C. Specimens with and without casting skin were investigated comparatively. The number of cycles to failure was significantly lower for specimens with casting skin. Metallographic investigations underline the reduction of lifetime caused by casting skin.