- Nano powder (8) (entfernen)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (4)
Im Rahmen des 2. BAM-Akademie Info-Tages "Nano or not Nano" wurde die OECD TG 124 "Volume Specific Surface Area of Manufactured Nanomaterials" vorgestellt.
Der Vortrag beschreibt die Bestimmung der spezifischen Oberfläche von dispersen und/oder porösen Pulvern mittels Gasadsorption nach dem BET-Verfahren.
Es wird auf die Anwendbarkeit der Methode eingegangen und es werden praktische Hinweise zur Probenvorbereitung und Messung von Nanomaterialien gegeben.
Particle size determination of a commercially available CeO2 nano powder - SOPs and reference data
(2023)
Compilation of detailed SOPs for characterization of a commercially available CeO2 nano powder including
- suspension preparation (indirect and direct sonication),
- particle size determination (Dynamic Light Scattering DLS and Centrifugal Liquid Sedimentation CLS) with reference data, respectively.
For sample preparation and analysis by Scanning Electron Microscopy (SEM) of this powder see related works (submitted, coming soon).
Im Vortrag werden das Messprinzip des Zentrifugen-Sedimentationsverfahrens erläutert und die Anforderungen der zugrundeliegenden Normen diskutiert. Es schließen sich umfangreiche Ausführungen zur praktischen Durchführung der Messung, insbesondere auch zu den vorbereitenden Arbeiten, sowie zur Auswertung der Rohdaten an. Gezeigt werden die Validierung sowie ein Beispiel zur regelmäßigen Verifizierung des Verfahrens. Nach Beispielen und Vergleichen zu Ergebnissen mit anderen Messverfahren, wird das Verfahren in einer Zusammenfassung bewertet.
Im Rahmen des 2. BAM-Akademie Info-Tages "Nano or not Nano" wurde die OECD TG 124 "Volume Specific Surface Area of Manufactured Nanomaterials" vorgestellt. Der Vortrag beschreibt detailliert das Messverfahren der He-Gaspyknometrie zur Bestimmung der Skelettdichte von Pulvern und geht auf Anwendbarkeit, Besonderheiten bei Nanopulvern und wichtige Einstellparameter für die Messung ein.
This paper describes experiences and results of experiments with several metallic dusts within the nanometer range. The nano dusts (aluminium, iron, zinc, titanium and copper) were tested in a modified experimental setup for the test apparatus 20 L-sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was already introduced in earlier papers by the authors. It was designed to allow the determination of safety characteristics of nano powders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). Furthermore the influence of passivation on explosion behaviour is investigated and additional tests with deposited dust were carried out to describe the burning behaviour of all dusts. For a better characterisation all samples were tested with a simultaneous thermal analysis (STA). To minimise the influence of oxidation all samples were handled at inert conditions until shortly before ignition or start of the test respectively.
This paper describes experiences and results of experiments with several metallic dusts within the nanometer range. The nano dusts (aluminium, .iron, zinc, titanium and copper) were tested in a modified experimental Setup for the test apparatus 20-L sphere (also known as 20-L Siwek Chamber), that enables the test samples to be kept under inert atmospheric conditions nearly until ignition. This setup was already introduced in earlier papers by the authors. It was designed to allow the determination of safety characteristics of nano powders under most critical circumstances (e.g. minimisation of the influence of oxidation before the test itself). Furthermore the influence of passivation on explosion behaviour is investigated and additional tests with deposited dust were carried out to describe the burning behaviour of all dusts. For a better characterisation all samples were tested with a simultaneous thermal analysis (STA). To minimise the influence of oxidation all samples were handled at inert conditions until shortly before ignition or start of the test respectively.