Comparison of the material parameters of polyethalene grades with the test performance behaviour of packagings for the transport of dangerous goods in relation to the pre-storage time with 55% nitric acid
- The material parameters melt flow rate (MFR), density (D), notched impact strength (NIS) at –30°C, stress crack resistance [determined with the Full Notch Creep Test (FNCT)] and resistance to oxidative degradation (Ox) have been selected for a comparison of polyethylene grades in the European standard EN 15507. These parameters have a relationship with design type tests of packagings for the transport of dangerous goods.
This paper presents the results of additional investigations to determine the impact of the pre-storage time of jerricans with 55% nitric acid at 40°C and 23°C on the marginal drop heights in drop tests at –18°C, on the MFR and on the tensile properties. Jerricans made of different polyethylene grades were pre-stored with 55% nitric acid for 21, 42 and 84 days at 40°C and for six months at 23°C.
The tests showed that the NIS values at –30°C of polyethylene grades were not comparable with marginal drop heights determined in drop tests at –18°C.
Pre-damage withThe material parameters melt flow rate (MFR), density (D), notched impact strength (NIS) at –30°C, stress crack resistance [determined with the Full Notch Creep Test (FNCT)] and resistance to oxidative degradation (Ox) have been selected for a comparison of polyethylene grades in the European standard EN 15507. These parameters have a relationship with design type tests of packagings for the transport of dangerous goods.
This paper presents the results of additional investigations to determine the impact of the pre-storage time of jerricans with 55% nitric acid at 40°C and 23°C on the marginal drop heights in drop tests at –18°C, on the MFR and on the tensile properties. Jerricans made of different polyethylene grades were pre-stored with 55% nitric acid for 21, 42 and 84 days at 40°C and for six months at 23°C.
The tests showed that the NIS values at –30°C of polyethylene grades were not comparable with marginal drop heights determined in drop tests at –18°C.
Pre-damage with 55% nitric acid for 21 days at 40°C led to an increase in the marginal drop heights of the jerricans. Altering the test regulations by increasing pre-storage time with 55% nitric acid to 42 days would be an alternative.
The test results demonstrated clearly that pre-storage of the jerricans for six months at 23°C caused a higher increase in the MFR and lower marginal drop heights for the jerricans when compared with pre-stored jerricans for 21 days at 40°C.…
MetadatenAutor*innen: | Margit Weltschev, Ute Niebergall, Jan Werner |
---|
Dokumenttyp: | Zeitschriftenartikel |
---|
Veröffentlichungsform: | Verlagsliteratur |
---|
Sprache: | Englisch |
---|
Titel des übergeordneten Werkes (Englisch): | Packaging technology & science |
---|
Jahr der Erstveröffentlichung: | 2013 |
---|
Verlag: | Wiley |
---|
Verlagsort: | Chichester, UK |
---|
Jahrgang/Band: | 27 |
---|
Erste Seite: | 409 |
---|
Letzte Seite: | 421 |
---|
Freie Schlagwörter: | Drop tests; Nitric acid; Packagings for the transport of dangerous goods; Polyethylene grades; Resistance to oxidative degradation; Tensile properties |
---|
DOI: | 10.1002/pts.2037 |
---|
ISSN: | 0894-3214 |
---|
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
---|
Datum der Freischaltung: | 20.02.2016 |
---|
Referierte Publikation: | Ja |
---|
Datum der Eintragung als referierte Publikation: | 27.06.2013 |
---|