Comparison between material parameters of polyethylene grades and the test performance behaviour of packaging for the transport of dangerous goods

  • For the characterization and the comparison of polyethylene grades used for the manufacture of packaging and intermediate bulk container, the following parameters are required: melt flow rate (MFR), density (D), low-temperature notched impact strength, full notch creep test (FNCT) and increase of MFR by molecular degradation (resistance to oxidative degradation). The relationship between these material parameters determined on the basis of specimens prepared from compression-moulded sheets of polyethylene grades and the test behaviour of packaging has been investigated in several tests. The environmental stress crack resistance determined by FNCT represents the impacts from the stacking tests performed with standard liquid wetting solution (without pre-storage) and with normal butyl-acetate-saturated wetting solution (pre-storage with normal butyl acetate). Resistance to molecular degradation by the determination of MFR increase is related to the impacts in drop tests and stackingFor the characterization and the comparison of polyethylene grades used for the manufacture of packaging and intermediate bulk container, the following parameters are required: melt flow rate (MFR), density (D), low-temperature notched impact strength, full notch creep test (FNCT) and increase of MFR by molecular degradation (resistance to oxidative degradation). The relationship between these material parameters determined on the basis of specimens prepared from compression-moulded sheets of polyethylene grades and the test behaviour of packaging has been investigated in several tests. The environmental stress crack resistance determined by FNCT represents the impacts from the stacking tests performed with standard liquid wetting solution (without pre-storage) and with normal butyl-acetate-saturated wetting solution (pre-storage with normal butyl acetate). Resistance to molecular degradation by the determination of MFR increase is related to the impacts in drop tests and stacking tests performed after pre-storage for 21 days with standard liquid 55% nitric acid at 40°C. The low-temperature impact strength is directly comparable with the impacts in drop tests at -18°C performed without pre-storage and after pre-storage with 55% nitric acid. A partly good relationship was found between the test results and the material parameters. Conditioning the design types with 55% nitric acid for 21 days causes an increase in the marginal drop heights of the design types in drop tests at -18°C when compared with design types without pre-storage. Post-cross-linking of the grades increases stiffness because of the acidic influence.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • Weltschev-2011-Packaging_Technology_and_Science.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Margit Weltschev
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Packaging technology & science
Jahr der Erstveröffentlichung:2011
Verlag:Wiley
Verlagsort:Chichester, UK
Jahrgang/Band:24
Ausgabe/Heft:6
Erste Seite:361
Letzte Seite:371
Freie Schlagwörter:Dangerous goods packaging; Design-type tests; Material parameters; Polyethylene grades
DOI:10.1002/pts.940
ISSN:0894-3214
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:06.06.2011
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.