Hot cracking tests - an overview of present technologies and applications

  • Hot crack prevention in materials production and processing is an essential prerequisite for welded component safety. The causes of hot cracking can ultimately be attributed to the occurrence of metallurgical effects and to structural loads. More than 140 hot cracking test procedures have hitherto been developed for determining the hot cracking resistance. In principle, they are divided in self-restraint and externally loaded hot cracking tests with diverse process variants. Only some of the hot cracking tests are international standardized. Although various factors are known that encourage or prevent hot cracking, it is often not possible even with defined welding conditions to draw immediate conclusions about the hot cracking resistance of a welded component alone from a metallurgical composition of the base and filler materials. Based on an evaluation of the existing theories relating to hot cracking susceptibility assessment, this study summarizes the major hot cracking testHot crack prevention in materials production and processing is an essential prerequisite for welded component safety. The causes of hot cracking can ultimately be attributed to the occurrence of metallurgical effects and to structural loads. More than 140 hot cracking test procedures have hitherto been developed for determining the hot cracking resistance. In principle, they are divided in self-restraint and externally loaded hot cracking tests with diverse process variants. Only some of the hot cracking tests are international standardized. Although various factors are known that encourage or prevent hot cracking, it is often not possible even with defined welding conditions to draw immediate conclusions about the hot cracking resistance of a welded component alone from a metallurgical composition of the base and filler materials. Based on an evaluation of the existing theories relating to hot cracking susceptibility assessment, this study summarizes the major hot cracking test procedures and highlights the application limits of the test procedures by presenting overviews along with explanations. It shows that weld hot cracking tests can generally be used to rank materials, welding consumables, and welding conditions. The evaluation of hot cracking test results and of their transferability among one another and to real components always requires consideration of the close relationships between metallurgy, welding process, and parameters, respectively, and prevailing restraint conditions.zeige mehrzeige weniger

Volltext Dateien herunterladen

  • 10.1007_s40194-014-0126-y.pdf
    eng

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Thomas KannengießerORCiD, Thomas Böllinghaus
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Welding in the world
Jahr der Erstveröffentlichung:2014
Herausgeber (Institution):International Institute of Welding
Verlag:Springer
Verlagsort:Oxford
Jahrgang/Band:58
Ausgabe/Heft:3
Erste Seite:397
Letzte Seite:421
Freie Schlagwörter:Arc welding; Cracking; Hot cracking; Quality control; Solidification cracking; Weldability tests
DOI:10.1007/s40194-014-0126-y
ISSN:0043-2288
ISSN:1878-6669
Verfügbarkeit des Dokuments:Datei im Netzwerk der BAM verfügbar ("Closed Access")
Datum der Freischaltung:20.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:28.04.2014
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.