Influence of film thickness on laser ablation of hydrogenated amorphous carbon films

  • Single-pulse damage thresholds of hydrogenated amorphous carbon (a-C:H) films were measured for 8-ns laser pulses at 532-nm wavelength. Layer thicknesses from below the optical penetration depth to above the thermal diffusion length (60 nm–13 µm) were examined. After correction of the damage-threshold values for the fraction of energy effectively absorbed by the material, the damage threshold was found to increase linearly with the layer thickness, also for film thicknesses below the optical penetration depth of a-C:H. The threshold fluence reached the bulk value for a layer thickness equal to the thermal diffusion length. The thermal diffusion coefficient was obtained from fitting the experimental data. Several phenomena like graphitization, blistering, exfoliation, and ablation were observed for different fluence regimes and film thicknesses.

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Grazia Daminelli-Widany, Simone Pentzien, Andreas HertwigORCiD, Jörg KrügerORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Applied physics
Jahr der Erstveröffentlichung:2006
Verlag:Springer
Verlagsort:Berlin
Jahrgang/Band:83
Ausgabe/Heft:1
Erste Seite:89
Letzte Seite:94
DOI:10.1007/s00339-005-3460-5
ISSN:0340-3793
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Nein
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.