Simulation of creep damage in a Cu polycrystal under multiaxial loading
- The stress States of components under Service conditions differ in general from the loading conditions that are routinely applied during material testing. When data that results, e.g., from uniaxial testing should be used for lifetime assessment, a good understanding of the failure behaviour in dependence of the stress state is necessary. For polycrystalline materials under high temperature loading, the development of creep damage is one important factor that limits a component’s lifetime. For cases where creep damage is related to the nucleation and growth of grain boundary cavities, the local normal stress acting on a grain boundary has been found to have a strong influence on the damage development. Hence, creep damage is usually localized along planes that lie perpendicular to the maximum principal tensile stress.
MetadatenAutor*innen: | Markus Vöse, Bernard FedelichORCiD |
---|
Dokumenttyp: | Beitrag zu einem Tagungsband |
---|
Veröffentlichungsform: | Graue Literatur |
---|
Sprache: | Englisch |
---|
Titel des übergeordneten Werkes (Englisch): | CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures |
---|
Jahr der Erstveröffentlichung: | 2015 |
---|
Erste Seite: | 175 |
---|
Letzte Seite: | 176 |
---|
Veranstaltung: | CREEP 2015 - 13th International conference on creep and fracture of engineering materials and structures |
---|
Veranstaltungsort: | Toulouse, France |
---|
Beginndatum der Veranstaltung: | 31.05.2015 |
---|
Enddatum der Veranstaltung: | 04.06..2015 |
---|
Verfügbarkeit des Dokuments: | Datei im Netzwerk der BAM verfügbar ("Closed Access") |
---|
Datum der Freischaltung: | 20.02.2016 |
---|
Referierte Publikation: | Ja |
---|
Datum der Eintragung als referierte Publikation: | 18.06.2015 |
---|