Femtosecond laser-induced damage of gold films

  • Single- and multi-shot ablation thresholds of gold films in the thickness range of 31–1400 nm were determined employing a Ti:sapphire laser delivering pulses of 28 fs duration, 793 nm center wavelength at 1 kHz repetition rate. The gold layers were deposited on BK7 glass by an electron beam evaporation process and characterized by atomic force microscopy and ellipsometry. A linear dependence of the ablation threshold fluence Fth on the layer thickness d was found for d ≤ 180 nm. If a film thickness of about 180 nm was reached, the damage threshold remained constant at its bulk value. For different numbers of pulses per spot (N-on-1), bulk damage thresholds of ~0.7 J cm-2 (1-on-1), 0.5 J cm-2 (10-on-1), 0.4 J cm-2 (100-on-1), 0.25 J cm-2 (1000-on-1), and 0.2 J cm-2 (10000-on-1) were obtained experimentally indicating an incubation behavior. A characteristic layer thickness of Lc ˜ 180 nm can be defined which is a measure for the heat penetration depth within the electron gas beforeSingle- and multi-shot ablation thresholds of gold films in the thickness range of 31–1400 nm were determined employing a Ti:sapphire laser delivering pulses of 28 fs duration, 793 nm center wavelength at 1 kHz repetition rate. The gold layers were deposited on BK7 glass by an electron beam evaporation process and characterized by atomic force microscopy and ellipsometry. A linear dependence of the ablation threshold fluence Fth on the layer thickness d was found for d ≤ 180 nm. If a film thickness of about 180 nm was reached, the damage threshold remained constant at its bulk value. For different numbers of pulses per spot (N-on-1), bulk damage thresholds of ~0.7 J cm-2 (1-on-1), 0.5 J cm-2 (10-on-1), 0.4 J cm-2 (100-on-1), 0.25 J cm-2 (1000-on-1), and 0.2 J cm-2 (10000-on-1) were obtained experimentally indicating an incubation behavior. A characteristic layer thickness of Lc ˜ 180 nm can be defined which is a measure for the heat penetration depth within the electron gas before electron–phonon relaxation occurs. Lc is by more than an order of magnitude larger than the optical absorption length of α-1 ˜ 12 nm at 793 nm wavelength.zeige mehrzeige weniger

Metadaten exportieren

Weitere Dienste

Teilen auf Twitter Suche bei Google Scholar Anzahl der Zugriffe auf dieses Dokument
Metadaten
Autor*innen:Jörg KrügerORCiD, Daniela Dufft, Robert Koter, Andreas HertwigORCiD
Dokumenttyp:Zeitschriftenartikel
Veröffentlichungsform:Verlagsliteratur
Sprache:Englisch
Titel des übergeordneten Werkes (Englisch):Applied surface science
Jahr der Erstveröffentlichung:2007
Verlag:North-Holland
Verlagsort:Amsterdam
Jahrgang/Band:253
Ausgabe/Heft:19
Erste Seite:7815
Letzte Seite:7819
Freie Schlagwörter:Gold films; Single- and multi-shot ablation; Ti:sapphire laser
ISSN:0169-4332
ISSN:1873-5584
Verfügbarkeit des Dokuments:Physisches Exemplar in der Bibliothek der BAM vorhanden ("Hardcopy Access")
Bibliotheksstandort:Sonderstandort: Publica-Schrank
Datum der Freischaltung:19.02.2016
Referierte Publikation:Ja
Datum der Eintragung als referierte Publikation:21.08.2007
Einverstanden
Diese Webseite verwendet technisch erforderliche Session-Cookies. Durch die weitere Nutzung der Webseite stimmen Sie diesem zu. Unsere Datenschutzerklärung finden Sie hier.