- MgF2 and TiO2 single layers and layer stacks were produced by a spin-coating sol-gel process. The final temperature treatment was carried out at 100 °C. The layers were deposited onto silicon and fused silica substrates and were analysed by means of atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, ellipsometry, and UV-vis transmission spectroscopy. MgF2 and TiO2 single layers have morphological and optical properties comparable with physical vapour deposited layers. By using spectroscopic mapping ellipsometry, a good inter- and intra-sample homogeneity was confirmed. Multiple deposition steps result in a linear increase of layer thickness. Various films were deposited with thicknesses between 25 nm and 350 nm.
It was shown that the low temperature sol-gel process results in films of optical quality. Anti-reflective and high reflective layer stacks consisting of MgF2 and TiO2 were designed and can be produced now by a sol-gel process, whereasMgF2 and TiO2 single layers and layer stacks were produced by a spin-coating sol-gel process. The final temperature treatment was carried out at 100 °C. The layers were deposited onto silicon and fused silica substrates and were analysed by means of atomic force microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy, ellipsometry, and UV-vis transmission spectroscopy. MgF2 and TiO2 single layers have morphological and optical properties comparable with physical vapour deposited layers. By using spectroscopic mapping ellipsometry, a good inter- and intra-sample homogeneity was confirmed. Multiple deposition steps result in a linear increase of layer thickness. Various films were deposited with thicknesses between 25 nm and 350 nm.
It was shown that the low temperature sol-gel process results in films of optical quality. Anti-reflective and high reflective layer stacks consisting of MgF2 and TiO2 were designed and can be produced now by a sol-gel process, whereas the MgF2 layers in the layer stacks contains also traces of MgF2-2xOx.…