Powder based Additive Manufacturing technologies offer huge potential for building parts with almost no geometrical restrictions, but both the process controlling as well as the part properties are strongly dependent on different material characteristics of the material, like the flowability. In this work, different weight percentages of nano-scaled silica dioxide particles (Aerosil®) are admixed to pure polyethylene and polypropylene powder and the resulting flowability is determined. Besides using the Hausner ratio as standardized value, the degree of coverage is introduced as a new characteristic to quantify the powder flowability. The degrees of coverage are compared to the Hausner ratios to allow a discussion and evaluation about the different characteristic values. Additionally, tensile bars consisting of polypropylene are generated to determine the porosity by cross sections and the mechanical part properties by tensile testing. As mechanical part properties, the tensile strength and elongation at break are determined and the effects of different powder flowability on these properties are analyzed.
By Laser Beam Melting of polymers (LBM), parts with almost any geometry can be built directly out of CAD files without the need for additional tools. Thus, prototypes or parts in small series production can be generated within short times. Up to now, no multi-material parts have been built by LBM, which is a major limitation of the technology. To realize multi-material parts, new mechanisms for depositing different polymer powders as well as a new irradiation strategy are needed, by which polymers with different melting temperatures can be warmed to their specific preheating temperatures and be molten simultaneously. This is achieved by simultaneous laser beam melting (SLBM). In the process, two different materials are deposited next to each other and preheated a few degrees below their melting temperatures by infrared emitters and laser radiation (λ = 10.60 µm), before in the last step the two preheated powders are molten simultaneously by an additional laser (λ = 1.94 µm). So far, multi-material tensile bars have been realized and analyzed regarding their boundary zone between both materials. The experiments showed that the temperature gradients in the boundary zone and along the building direction seem to be of great importance for the process stability and the resulting part properties. Therefore, a detailed analysis of the occurring temperature gradients during the process is needed to identify adequate process adjustments regarding the temperature controlling. To analyze the temperature gradients, thermocouples positioned inside the powder bed are used. By varying the temperature of the building platform, the influence of different temperature gradients on the resulting part properties is shown.