Precisely aligned arrays of sharp tip structures on top of elongated pillars were realized by using an improved fabrication process including an additional inductively-coupled-plasma reactive-ion etching step. Arrays of n-type and p-type silicon with 271 tips have been fabricated and investigated. Those structures have a total height of 5–6 µm and apex radii less than 20nm. Integral field emission measurements of the arrays yielded low onset-fields in the range of 8–12V=µm and field enhancement factors between 300 and 700. The I-E curves of n-type structures showed the usual Fowler-Nordheim behaviour, whereas p-type structures revealed a significant saturation region due to the limited number of electrons in the conduction band and a further carrier depletion effect caused by the pillar. The maximum integral current in the saturation region was 150 nA at fields above 30V=µm. An excellent stability of the emission current of less than ± 2% fluctuation was observed in the saturation region. For n-type Si a maximum integral current of 10 µA at 24V=µm and an average current stability with a fluctuation of ± 50% were measured.