Arrays of black silicon field emission pillar structures were fabricated on p-type silicon substrates. Two types of samples with the same number of pillars (arrays of 10 × 10) but different pillar heights (8 and 20 μm) were prepared as well as a black silicon reference sample without pillars. The field emission properties of these cathodes were investigated both by means of integral current-voltage measurements and by field emission scanning microscopy. Samples with a pillar height of 20 μm revealed onset fields as low as 6.4 V/μm, field enhancement factors up to 800, and emission currents up to 8 μA at an applied field of 20 V/μm. Due to the p-type material, a saturation of the emission current for fields above 11 V/μm was observed. This saturation leads to a stable operation with a current fluctuation of less than ±8%. It was found that samples with a pillar height of 20 μm showed improved emission characteristics compared to samples with a pillar height of 8 μm or without pillars. The voltage maps revealed an increased emission homogeneity after a “burn-in” sequence of the sample. The current map showed that a few of the pillars dominate the emission. Integral current stability measurements were performed under different vacuum pressures, in order to investigate altered emission behavior and a potential degradation of the emitters. At pressures above 10−6 mbar, the sample starts to degrade irreversibly. Nevertheless, even after a harsh treatment over 30 min at 5 × 10−5 mbar and at an applied field of 23 V/μm, the cathode was still operating, and did not fail during further operation over 20 h at 5 × 10−8 mbar and at an applied field of 28 V/μm.
Precisely aligned high-aspect-ratio (HAR) silicon tip arrays were fabricated using enhanced reactive ion etching with an inductively-coupled-plasma followed by a sharpening oxidation. A gold thin film was then sputtered only on the tips of the HAR structures. Field-emission (FE) properties from Au-coated HAR p-Si tip array cathodes have been systematically investigated by means of field emission scanning microscopy (FESM). A rather high efficiency of the HAR Si structures (71% at 550 V), but limited homogeneous FE with currents of 1-600 nA might be correlated with the varying geometry of the tips and the presence of oxides. I-V measurements of single Au-coated HAR emitters revealed activation effects and the saturation current region at 3 nA. An increase of the saturation current by 4 orders of magnitude was observed during 20 hours of conditioning at constant voltage, which finally resulted in nearly reproducible FN curves with a ß-factor of 473. An excellent stability of the emission current of less than 1 % was obtained during the additional long-time conditioning at constant voltage. Optical switching under halogen lamp illumination resulted in at least 2 times higher saturation currents and showed a linear dependence of the FE current on the light color temperature.