In this contribution we report on field emission (FE) cathodes based on thin-film LED-technology and surface texturing. The FE cathode can be used both as an n-GaN cathode with an electrical contact at the top side metallization as well as a pn-GaN diode contacting only the p-GaN layer at the bottom side of the structure. The local and integral FE properties of the textured surface of the LED structure were investigated. For n-GaN an integral emission current up to 1.0 μA at an electric field of 19 V/μm was achieved. The pn-GaN diode measurements showed an integral current saturation behavior with two orders of magnitude lower FE currents. Regulated voltage scans obtained by FE scanning microscopy revealed a well-distributed emission over the whole cathode area. Measurements under pulsed tunable laser illumination and moderate electric fields indicated charge carrier generation in the buried double-heterostructures at photon energies below 3.5 eV besides normal photoemission above 4.1 eV.
Aligned square arrays of black silicon (b-Si) on top of pillars were fabricated on p-type silicon substrate by a deep-etching step combined with a b-Si process. Two 10×10 arrays with pillar heights of 8 μm and 20 μm and one b-Si reference sample without pillars were investigated. Integral field emission (FE) measurements of the arrays yielded rather low onset-fields between 6.4 V/μm and 13.5 V/μm and field enhancement factors between 430 and 800. The I-V curves showed typical Fowler-Nordheim behavior for low fields, whereas a saturation region was observed at higher fields. The maximum integral current in the saturation region was 8 μA at a field of 20 V/μm. The stability of the emission current was investigated over 3 hours and revealed moderate fluctuations of ± 8% in the saturation region. Voltage scans showed well-aligned FE from nearly all pillars.
Electron sources based on silicon field emitter arrays, produced in processes based on semiconductor technology, are good candidates for a miniaturized X-ray source. A key parameter for this application is the stability of the X-ray photon flux and, thus, the emission current. In the present work we have investigated the influence of the residual gas pressure and a resistor in series on the emission stability of a high aspect ratio n-type silicon emitter array with hybrid extraction electrode. An increase of current fluctuations was found for pressures above 10-6 mbar. High resistances in series to the emitter array alter the emission characteristics, but greatly suppress spikes in the emission current and improve its stability. This, however, strongly depends on the bias point. The field enhancement factor is not affected by the resistance. In a long term measurement the emission current was found to be constant after an initial phase of degradation.
We report on gated p-type Si-tip array cathodes for implementation into field emission electron sources for sensor applications. Arrays of 16 and 100 tips with tip heights of 3 μm and tip radii below 30 nm with integrated gate electrodes concentrically positioned 2 μm below the tip apexes were fabricated using an improved process, which leads to an enhanced isolation layer quality with sufficient breakdown field strengths and low leakage currents. Integral measurements with a fixed grid potential of 400 V showed emission currents up to 35 μA for 100 tips at a cathode voltage of 150 V and an almost negligible parasitic gate current. The array with 16 p-type Si-tips showed a significant stabilization of the emission current in the range of 0.3 - 0.4 μA, for cathode voltages between 90 V and 150 V. The current fluctuation in this saturation regime was measured for 10 minutes and a value of less than ± 1% was observed. No degradation of the cathode was found after 6 hours of operation at a constant cathode voltage of 100 V and a constant grid voltage of 400 V.