Ecological comparison of soldering and sintering as die-attach technologies in power electronics
(2015)
In this study the method of life cycle assessment is used to perform a comparison of two die-attach technologies of power modules: silver sintering and common soldering with a tin–silver–copper solder. The goal of the study is to indicate which die-attach technique is more environmentally friendly. This is important in order to design future electronics more environmentally friendly.
Processing covers the manufacturing of the respective pastes, application of pastes, and mounting as well as the subsequent sintering or soldering, including cleaning of the soldered parts. The last step in the processing is a wire bonding process. The environmental impacts are expressed in CO2-equivalents and ReCiPe points and different variants are discussed: comparisons are made between considered pastes and between a soldered and a sintered power module, including consideration of lifetime. Concerning sintering, the influence of using recycled silver is analyzed more closely. The types of stages included in this life cycle assessment best fit a cradle-to-gate assessment, because usage, recycling, and disposal are not included. The software used is OpenLCA version 1.3.3, created by GreenDelta, and the database used is Ecoinvent version 2.2. In order to fill data gaps, electronics manufacturing companies were contacted, and our own calculations and measurements were applied.
The consideration of the wet film thicknesses of the soldering system and sintering system, respectively, results in very similar CO2-equivalent emissions for sinter paste and solder paste. Comparing the soldered power module to the sintered one shows minor to significant differences between the two systems which could easily be changed when changing circumstances and assumptions. But when considering the respective lifetimes of the joining technologies, sintering technology is clearly preferable to the conventional soldering technology. Using solely recycled silver for manufacturing of silver sinter paste reduces the CO2-equivalent emissions of one sintered power module by roughly 40%.
The results clearly show the dependence of outcomes on the initial settings. Consideration of lifetime has an enormous impact on the comparison of soldering technology to sintering technology. But the benefit of this life extension through the use of sintering technology is only useful when a long lifetime is required.
This contribution discusses the integration of polymer planar Bragg grating sensors (PPBG) into carbon fiber reinforced polymer (CFRP) components. For the first time, it is shown that PPBGs based on cyclic olefin copolymers can be integrated into commercial-grade composites, thereby withstanding the demanding production processes. Pre-impregnated fibers are stacked and partially modified to form a sensor pocket. Afterwards, the CFRP specimen containing the optical sensor is cured in a heated mechanical press for 2 hours at a pressure of 7 bar and a temperature of 120 °C. A subsequent evalutaion of the sensor signal shows a Bragg wavelength shift of 1236 pm and a decline in signal amplitude of -2 dB. Three-point flexural tests of the cured sample reveal a linear behavior of the sensor signal towards external loads. The determined sensitivity in dependence of the CFRP specimen's maximum central deflection is -112 pm/mm, while correlation to the applied force results in a sensitivity of -5 pm/N.