A quantitative experimental assessment of flame retardancy by the heat shielding in epoxy layered silicate nanocomposite (EP/TPPMMT) is presented. Online heat flux measurements and temperature monitoring within the specimen are performed during the burning in the cone calorimeter. For EP the surface layer equals a pyrolysis front. The reradiation by the hot surface corresponds to the fourth power of the pyrolysis temperature. The surface reradiation (around 10 kW m-2) is thus fairly invariable over burning time and different external heat fluxes. Further, the thermal feedback of the flame is approximated to 20 kW m-2 for both EP and EP/TPPMMT and invariable over different irradiations. Thus the net heat fluxes transformed to the fuel release rate within the pyrolysis front of EP are increased to 45–80 kW m-2 when irradiations of 35–70 kW m-2 are applied. For a residue-forming EP/TPPMMT the surface temperature and thus the reradiation (42–68 kW m-2) crucially increases compared to EP and with increasing irradiation. The net heat fluxes are reduced to 13–22 kW m-2 accordingly. This quantitative assessment of the heat shielding in EP/TPPMMT goes along with proportional and consistent improvement in the fire performance, such as the pyrolysis front velocity, the heat release rate (HRR) characteristics such as averaged and quasi-steady-state HRR and the peak HRR (PHRR). The heat shielding is proven to be the only major flame retardancy effect occurring in nanocomposites based on non-charring polymers.
Tetraphenylphosphonium modified layered silicate epoxy nanocomposite (EP/TPPMMT) combined with low-melting silicate glass, Ceepree (CP) is investigated by thermal analysis, flammability tests and cone calorimeter at different heat fluxes. Adding CP and TPPMMT does not change the pyrolysis apart from increasing inorganic residue. The total heat evolved (THE) is changed insignificantly, as neither relevant additional carbonaceous charring nor flame inhibition occurs. However, flame retardancy is clearly observed due to an inorganic-carbonaceous surface protection layer. The peak heat released rate (PHRR) is reduced by around 3242% when 5 wt% TPPMMT is added, and 5163% when 10 wt% CP is added. PHRR reduction less than expected is observed when both additives are combined. The reduction is greater than that achieved by using TPPMMT but less than when only CP is used. The morphology of fire residue is investigated by scanning electron microscope on different length scales and turns out to be the key to understanding the efficiency of flame retardancy. The fire residue of EP/CP shows a layered structure, whereas separated columns limit the barrier properties for EP/5%TPPMMT on the micrometer scale. Columns dominating the fire residue structure of EP/5%TPPMMT/10%CP deteriorate the fire retardancy, whereas a more integral structure at the top of the residue causes the improvement over EP/5%TPPMMT. POLYM. ENG. SCI., 2012. © 2011 Society of Plastics Engineers
Tetraphenyl phosphonium-modified layered silicate (LS) and low-melting phenylsiloxane glass (G) are combined for more efficient halogen-free flame retardancy in epoxy resin (EP_LSG). Particularly, the peak heat release rate (PHRR) is decreased (by up to 60%), but levels off at additive concentrations ≥10 wt%. The performance of EP_LSG is compared to EP_LS and EP_G assuming an absolute and a relative flame retardancy effect, respectively, and based on the same amount of each filler and, alternatively, with EP_G containing the same overall amount of filler. EP_LSG behaves close to superposition but shows a strong tendency toward synergism due to a superior structural integrity of the fire residues. Apart from LS, adding G in particular is a promising approach when its content is ≤5 wt%, as is LSG for ≥10 wt%.