Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
Referierte Publikation
- ja (43) (entfernen)
Schlagworte
- Laser beam welding (14)
- Laser metal deposition (6)
- Solidification cracking (6)
- Microstructure (5)
- Additive manufacturing (4)
- Hybrid laser-arc welding (4)
- Laser welding (4)
- 9%Ni steel (3)
- Hybrid laser arc welding (3)
- Mechanical mismatching (3)
- Thermography (3)
- Thick-walled steel (3)
- Additive Fertigung (2)
- Additive Manufacturing (2)
- Critical strain (2)
- Electromagnetic weld pool control (2)
- Full penetration (2)
- Inconel 718 (2)
- LMD (2)
- Matching ferritic welding electrode (2)
- Mechanical properties (2)
- Numerical simulation (2)
- Process monitoring (2)
- Thermografie (2)
- 3D Druck (1)
- 3D printing (1)
- AC magnetic field (1)
- Aluminium (1)
- Artificial Intelligence (1)
- Austenitic stainless steels (1)
- Austenitic welding electrode (1)
- Bending test (1)
- Build-up strategy (1)
- Bulge effect (1)
- Bulging effect (1)
- CFD model (1)
- Circumferential weld (1)
- Clad steels (1)
- Convolutional neural network (1)
- Crater (1)
- Deposition rate (1)
- Direct Energy Deposition (1)
- Direct energy deposition (1)
- Duplex AISI 2205 (1)
- Duplex stainless steel (1)
- Duplex steels (1)
- Edge quality (1)
- Electromagnetic Force (1)
- Electromagnetic stirring (1)
- Electromagnetic support (1)
- Electromagnetic weld pool support (1)
- End crater (1)
- Equivalent heat source (1)
- Ferromagnetic steel (1)
- Ferromagnetic steels (1)
- Fiber laser (1)
- Filler wire mixing (1)
- Finite element analysis (1)
- Finite element method (FEM) (1)
- Fresnel reflection (1)
- Full penetration welding (1)
- Fusion zone size (1)
- GTAW (1)
- Gap bridgeability (1)
- Hardness (1)
- Hartmann effect (1)
- Heat flow (1)
- Heat source models (1)
- High brightness (1)
- High power (1)
- High power laser beam welding (1)
- High-Power Welding (1)
- High-power Laserbeam Welding (1)
- High-power laser beam (1)
- High-power laser beam welding (1)
- High-strength low-alloy steel (1)
- Hot crack (1)
- Hot cracking (1)
- Hybrid Laser-Arc Welding (1)
- IR-Spektroskopie (1)
- IR-spectroscopy (1)
- Imaging (1)
- Impact absorbed energy (1)
- In situ strain (1)
- Keyhole mode welding (1)
- Keyhole stability (1)
- Lamé curves approximation (1)
- Laser Metal Deposition (1)
- Laser Powder Bed Fusion (1)
- Laser Pulver Auftragsschweißen (1)
- Laser beam weliding (1)
- Laser cutting (1)
- Laser hybrid welding (1)
- Laser keyhole welding (1)
- Laser surfacing (1)
- Laser-Pulver-Auftragschweißen (1)
- Lorentz force (1)
- MWIR (1)
- Magnetic field (1)
- Maintenance (1)
- Marangoni flow (1)
- Matching ferritic filler metal (1)
- Mechanical-technological properties (1)
- Melt pool dynamics (1)
- Metal (1)
- Metal mixing (1)
- Microstructure Tensile strength (1)
- Multi-physical modelling (1)
- Multispectral thermography (1)
- NIR (1)
- Natural convection (1)
- Ni-based austenitic filler metal (1)
- Ni-based austenitic welding electrode (1)
- Nickel (1)
- Numerical modeling (1)
- Numerical simulations (1)
- Optical measurement (1)
- Optical measurment technique (1)
- Oscillating magnetic field (1)
- Partial penetration (1)
- Partial penetration welding (1)
- Pipe Welding (1)
- Pipeline steel of grade X120 (1)
- Plasma cutting (1)
- Plume heating (1)
- Post-weld heat treatment (1)
- Preheating (1)
- Process simulation (1)
- Repair and overhaul (1)
- SMAW (1)
- SWIR (1)
- Secondary heat source (1)
- Selective Laser Melting (1)
- Ship building (1)
- Shipbuilding steel (1)
- Simulation (1)
- Software (1)
- Solidification (1)
- Stainless steels (1)
- Strain fields prediction (1)
- Strain rate (1)
- Submerged arc welding (1)
- TES (1)
- Temperature distribution (1)
- Temperature emissivity separation (1)
- Thermal analysis (1)
- Thermal cycles (1)
- Thick materials (1)
- Thick-Walled Steel (1)
- Toughness (1)
- Two-run welding technique (1)
- Vacuum (1)
- Vapor recondensation (1)
- Weld pool (1)
- Weld pool support (1)
- Weld root (1)
- Welding simulation (1)
Organisationseinheit der BAM
The present work deals with the recently confirmed widening of the weld pool interface, known as a bulging effect, and its relevance in high power laser beam welding. A combined experimental and numerical approach is utilized to study the influence of the bulge on the hot cracking formation and the transport of alloying elements in the molten pool. A technique using a quartz glass, a direct-diode laser illumination, a high-speed camera, and an infrared camera is applied to visualize the weld pool geometry in the longitudinal section. The study examines the relevance of the bulging effect on both, partial and complete penetration, as well as for different sheet thicknesses ranging from 8 mm to 25 mm. The numerical analysis shows that the formation of a bulge region is highly dependent on the penetration depth and occurs more frequently during partial penetration above 6 mm and complete penetration above 8 mm penetration depth, respectively. The location of the bulge correlates strongly with the cracking location. The obtained experimental and numerical results reveal that the bulging effect increases the hot cracking susceptibility and limits the transfer of alloying elements from the top of the weld pool to the weld root.
The study deals with the determination of the influence of an externally applied oscillating magnetic field on the melt pool dynamics in high power laser beam and hybrid laser arc welding processes. An AC magnet was positioned under the workpiece which is generating an upward directed electromagnetic force to counteract the formation of the droplets. To visualise the melt flow characteristics, several experiments were carried out using a special technique with mild steel from S355J2 with a plate thickness of up to 20 mm and a quartz glass in butt configuration. The profile of the keyhole and the melt flow were recorded with a highspeed camera from the glass side. Additionally, the influence of the magnetic field orientation to the welding direction on the filler material dilution on laser hybrid welding was studied with variating oscillation frequency. The element distribution over the whole seam thickness was measured with X-ray fluorescence (XRF). The oscillation frequency demonstrated a great influence on the melt pool dynamics and the mixing of the elements of the filler wire. The highspeed recordings showed, under the influence of the magnetic field, that the melt is affected under strong vortex at the weld root, which also avoids the formation of droplets.
the joints throughout the structure. The flat units are constituted by butt welded flat plates, on which longitudinal T-welded reinforcements are placed to rigidize the structure. Among the different welding technologies, Hybrid Laser Arc Welding (HLAW) is becoming a mature process, profitable and highly productive. In addition, more innovative welding equipment are being developed nowadays, offering greater work flexibility, and raising expectations of achieving better quality, and economic viability. Another key point of HLAW to keep in mind is that structural distortions are reduced, resulting in decreasing the cost and time of straightening work.
In the present contribution, the influence of HLAW parameters on the quality of fillet joints of naval steel has been analysed. Experimental HLAW tests were performed with a high power disk laser to join EH36 naval steel plates, with a T configuration. The influence of different processing parameters has been analysed, as the laser power, welding speed, wire feed rate and the configuration of the HLAW processes (including head angle and laser/arc leading process). In addition, FEM simulations were carried out in order to estimate residual stresses and distortion of welded part. The distortion values provided by FEM presented excellent agreement with the measured experimental results. To evaluate the welds, non destructive tests including X-ray tests, metallographic analysis of cross sections, and microhardness mapping tests were performed.
Full penetration 8 mm T welds were obtained for the first time at an industrially applicable 2F position with a reasonable HLAW head angle, in one single step without sealing root, and using zero gap square groove Edge preparation. The present contribution presents welding rates up to 2.2 m/min for 2F T-joints of this steel thickness, a much higher processing velocity than previously reported for industrial applications.
The stability of the keyhole decreases for deep penetrated high-power laser beam welding. The keyhole tends to collapse with increasing laser power and e.g. keyhole induced porosity can occur. This study deals with the observation of the keyhole during high-power laser beam welding in partial penetration mode by means of a high-speed camera. A butt configuration of 25 mm thick structural steel and transparent quartz glass was used for the experiments. An oscillating magnetic field was applied perpendicular to the welding direction on the root side of the steel plate. The keyhole was highlighted with a coaxial diode laser. It was ascertained that the stability of the keyhole and the weld penetration depth were increased by applying an oscillating magnetic field with an oscillating frequency of 1.2 kHz and a magnetic flux density of 50 mT.
The present contribution is the first research reporting full penetration HLAW joints in 15 mm thick EH36 steel butt T-welds with square grooves on 2F welding position by single-sided welding. The effects of welding parameters were investigated to increase the quality of the joints.
Conditions leading to defect-free full penetration welds fulfilling naval regulations includes a laser power of 12.5 kW, a welding speed of 1.6 m/min and the vertical laser offset distance from the flange of 1 mm. Advanced characterization of selected welds included a microstructural identification by optical microscopy, SEM, and XRD, revealing the presence of acicular, polygonal and Widmanstätten ferrite, lath martensite, and some retained austenite at FZ. Hardness and microhardness mapping tests showed values of 155 HV at base metal and 200 to 380 HV at the fusion zone connecting the web to the flange.
Im Rahmen des Themenfeldprojektes „Process Monitoring of AM“ (ProMoAM) evaluiert die Bundesanstalt für Materialforschung und -Prüfung (BAM) gegenwärtig die Anwendbarkeit verschiedenster ZfP-Verfahren zur in-situ Prozessüberwachung in der additiven Fertigung (AM) von Metallen in Hinblick auf die Qualitätssicherung.
Einige der wichtigsten Messgrößen sind hierbei die Temperatur des Schmelzbades und die Abkühlrate, welche starken Einfluss auf das Gefüge und die Eigenspannung haben. Aufgrund der Zugänglichkeit zum Werkstück während des Bauprozesses bieten sich optische Verfahren zu Temperaturbestimmung an. Hierbei stellen jedoch u. a. die hohe Bandbreite der zu messenden Temperaturen, die Bestimmung der Emissivität und ihre Änderung bei Phasenübergängen der verwendeten Legierung große experimentelle Herausforderungen dar. Eine weitere Herausforderung stellt für die IR-Spektroskopie die Absorption durch das Schutzgas und weitere optische Elemente dar. Um diese auch in einem industriellen Umfeld kompensieren zu können, wurde eine Methode entwickelt, die das gemessene Spektrum bei der Verfestigung des Werkstoffes als Referenz nutzt. In diesem Beitrag wird die Anwendung dieser Methode für die IR-Spektrometrie als auch Thermografische Messungen beim Laser-Pulver-Auftragschweißen von 316L gezeigt, wobei beide Methoden weiterhin in Hinblick auf ihre individuellen Vor- und
Nachteile miteinander verglichen werden.
Due to the rapid thermal cycles involved in additive manufacturing of metals, high internal stresses and peculiar microstructures occur, which influence the parts mechanical properties. To systematically examine their formation, in-process measurements of the temperature are needed. Since the part emissivity is strongly inhomogeneous and rapidly changing in the process, the applicability of thermography for the determination of thermodynamic temperatures is limited. Measuring the thermal radiation in different wavelengths simultaneously, temperature and emissivity can be separated. Here, we present results of a preliminary study using multispectral thermography to obtain real temperatures and emissivities in directed energy deposition (DED) processes.
In this study, the influence of the welding speed, the arc power, and the laser focal position on the solidification crack formation for partial penetration laser hybrid–welded thick-walled plates was investigated.
The solidification cracking in the weld root is a result of interaction between metallurgical and geometrical and thermomechanical factors.
Experimentally, a direct correlation between the welding speed and the crack number was observed. That is by reducing the welding velocity, the crack number was decreased. The focal position shows also a significant influence on the crack number. By focusing the laser on the specimen surface, the crack number has been significantly diminished.
The wire feed speed showed a very slight influence on the crack formation. That is due to the large distance between the critical region for cracking and the arc region.
The numerical model shows a high stress concentration in the weld root for both components (vertical and transversal).
Numerically, the reduced welding speed showed a strong impact on stress, as the model demonstrated a lower stress amount by decreasing the welding speed.
The metallurgical factors, such as the assumed accumulation of the low-melting eutectics in the weld root, should be a contribution for solidification cracking, where the tensile stress is acting.
A novel approach for the reconstruction of an equivalent volumetric heat source from a known weld pool shape is proposed. It is based on previously obtained weld pool geometries from a steady-state thermo-fluid dynamics simulation. Hereby, the weld pool dimensions are obtained under consideration of the most crucial physical phenomena, such as phase transformations, thermo-capillary convection, natural convection, and temperature-dependent material properties. The algorithm provides a time and calibration efficient way for the reproduction of the weld pool shape by local Lamé curves. By adjusting their parameters, the identification of the finite elements located within the weld pool is enabled. The heat input due to the equivalent heat source is assured by replacing the detected nodes’ temperature by the melting temperature. The model offers variable parameters making it flexible and adaptable for a wide range of workpiece thicknesses and materials and allows for the investigation of transient thermal effects, e.g., the cooling stage of the workpiece. The calculation times remain acceptably short especially when compared to a fully coupled process simulation. The computational results are in good agreement with performed complete-penetration laser beam welding experiments.
Motivated by the tensile strength loss of 9%Ni steel arc welded joints made using Ni-based austenitic filler metals, the feasibility of maintaining the tensile strength using matching ferritic filler metal has been demonstrated. In comparison with shielded metal arc welded joint made using Ni-based austenitic electrode ENiCrMo-6, higher tensile strength comparable to that of the base metal was obtained using matching ferritic electrode. Besides, sufficient impact toughness energies with much lower mismatch were obtained for weld metal and heat-affected zone.
Welded joint with a lower mechanical mismatching is of considerable importance for achieving acceptable combination of tensile strength and impact toughness.Abetter combination of These mechanical properties is ensured by applying a post weld heat treatment.