The double loop electrochemical potentiodynamic reactivation (EPR) method is a standardised procedure for detecting and quantifying sensitisation on austenitic, ferritic and ferritic-austenitic stainless-steel grades. This sensitisation is caused by microstructural alternations, as the formation of chromium carbides, nitrides or sigma-phases, which generate local chromium depleted zones nearby. The latter strongly influence the corrosion resistance and the electrochemical response of a stainless steel during electrochemical potentiodynamic reactivation, providing important information on the degree of chromium depletion. In case of martensitic stainless steels, which are used for cutlery and surgical instruments, the heat treatment has a strong impact on the microstructure, the material properties and especially on the corrosion resistance. To study this interaction, the EPR method was modified for the application on martensitic stainless steels with about 13 wt.-% chromium. Different H2SO4 concentrations and EPR-parameters were tested and compared on two standard martensitic stainless-steel grades (AISI 420 A / X20Cr13 and AISI 420 C / X46Cr13) to define applicable parameters. Afterwards, these parameters were used to study the effect of austenitisation time and cooling rate on the corrosion resistance of both martensitic stainless steels. The response of both alloys was different due to the different carbon levels, which will be explained by microstructural investigations in detail. All results allow postulating a process window, in which chromium depletion is suppressed and an optimised corrosion resistance is guaranteed. Based on this research, the modified EPR-test is now used to control the heat treatment and its impact on the corrosion resistance of martensitic stainless steels in the cutlery industry. The EPR-test is thus an interesting alternative for manufacturers, processors, users and researchers to the time-consuming exposition test normally used to characterise the corrosion resistance of martensitic stainless steels.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation
(EPR) was used to determine the corrosion resistance and detect chromium depletion in all heattreated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Das Korrosionsverhalten von kohlenstoffhaltigen martensitischen nichtrostenden Stählen variiert in Abhängigkeit der Wärmebehandlung (WB) und der damit eingestellten Mikrostruktur deutlich stärker als bei kohlenstoffarmen ferritischen und austenitischen nichtrostenden Stählen. Bei erhöhtem Kohlenstoffgehalt bestimmt die diffusionsgesteuerte Bildung und Auflösung von Chromkarbiden die Verteilung von Chrom und Kohlenstoff im Gefüge. Bisher lag der Fokus von Forschungsarbeiten zum Einfluss der WB auf dem Anlassen im allgemein bekannten Sensibilisierungsbereich dieser Werkstoffgruppe zwischen 200 °C und 700 °C und der dort auftretenden Chromverarmung. Mit der gezielten WB des X46Cr13 (1.4034) wird gezeigt, dass Temperatur und Dauer beim Austenitisieren sowie die anschließende Abkühlung beim Härten das Korrosionsverhalten schon vor dem Anlassen signifikant beeinflussen. Auf der Basis von thermodynamischen Berechnungen wurden definierte WB ausgewählt, um gezielt unterschiedliche Volumengehalte von Chromkarbiden im Gefüge und somit auch unterschiedliche Chrom bzw. Kohlenstoffgehalte im Mischkristall zu erzeugen. Anschließend wurden die resultierenden Gefügezustände hinsichtlich Chromkarbidanteil und Härte verglichen und das Korrosionsverhalten mit der elektrochemisch potentiodynamischen Reaktivierung (EPR) sowie durch einen Schnelltest mit der KorroPad-Prüfung untersucht. Dabei konnte ein direkter Zusammenhang zwischen WB, Mikrostrukturänderungen und Korrosionsverhalten festgestellt werden. Mit steigender Austenitisierungstemperatur wird der Anteil an Chromkarbiden reduziert und der Kohlenstoff- und Chromgehalt der Matrix erhöht, bis eine vollständige Auflösung der Chromkarbide gegeben und die chemische Nennzusammensetzung der Legierung im Mischkristall erreicht ist. In der direkten Folge wird die Ausbildung der für nichtrostende Stähle charakteristischen Passivschicht erleichtert und das Lochkorrosionsverhalten verbessert. Die Abkühlrate hat neben den Austenitisierungsparametern ebenfalls einen großen Einfluss auf das Korrosionsverhalten. So führt eine langsame Abkühlung an Luft zu einer Chromverarmung im Gefüge, die eine deutlich erhöhte Lochkorrosionsanfälligkeit zur Folge hat. In Abhängigkeit der WB von kohlenstoffhaltigen nichtrostenden Stählen können Mikrostruktur, Härte und Korrosionsbeständigkeit in einem weiten Bereich variieren.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromi-um carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hard-ening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Im Vortrag wird ein innovativer Ansatz zur Herstellung von Referenzmaterialien für systematische Grundlagenuntersuchungen und Methodenentwicklungen vorgestellt. Dieser Ansatz basiert auf der Verwendung eines Lichtbogenschmelzofens (Arc-Melter), der zur Legierungsvariation bei nichtrostenden Stählen verwendet wurde. In Abhängigkeit vom Chromgehalt wurden zunächst Ergebnisse der elektrochemisch potentiodynamischen Reaktivierung (EPR) und der KorroPad-Prüfung vorgestellt, die neue Einblicke zur Nachweisgrenze beider Verfahren liefern. Anschließend wurde der Einfluss vom Schwefelgehalt auf die Lochkorrosionsbeständigkeit dargestellt und dabei gezeigt, dass die in den Normen festgeschriebenen Grenzwerte deutlich zu hoch sind. Darüber hinaus wurden zukünftig geplante Arbeiten vorgestellt, die mit diesem Ansatz möglich sind.
Mit der KorroPad-Prüfung kann die Lochkorrosionsbeständigkeit nichtrostender Stähle auf sehr einfache, schnelle und kostengünstige Weise eingeschätzt werden. Das Kor-roPad ist damit für Hersteller, Verarbeiter und Anwender nichtrostender Stähle eine interessante Alternative zu zeitintensiven Langzeitversuchen und komplexe elektrochemischer Untersuchungsmethoden. Die prinzipiellen Funktionsweise der KorroPad-Prüfung wird im Vortrag beschrieben, um anschließend verschiedene Anwendungen aus Industrie und Forschung vorzustellen. Exemplarisch werden dazu die Bewertung von Schleif- und Passivierungsprozessen, die Qualitätskontrolle der Wärmebehandlung und Oberflächenbearbeitung von Schneidwaren sowie die Optimierung der Schweißnaht-Nachbehandlung vorgestellt. Mit der KorroPad-Prüfung lassen sich aber auch werkstoff- und gefügebedingte Einflüsse auf die Lochkorrosionsbeständigkeit gezielt untersuchen. Dies wird an Beispielen aus aktuellen Forschungsprojekten dargestellt. Die abschließend dargestellte Charakterisierung vom Sensibilisierungsverhalten mit der KorroPad-Prüfung ist verdeutlicht das breite Anwendungsspektrum bei der Charakterisierung von nichtrostenden Stählen.
Der nichtrostende Lean-Duplexstahl 1.4062 (X2CrNiN22-2) verbindet die hohe Festigkeit des Ferrits mit der Duktilität und Zähigkeit des Austenits in einem zweiphasigen Gefüge mit sehr hoher Korrosionsbeständigkeit. Die höchste Korrosionsbeständigkeit wird erreicht, wenn das ferritisch-austenitische Gefüge frei von weiteren Sekundärphasen ist. Dies wird durch ein gezieltes Lösungsglühen bei 1050 °C mit anschließender Abschreckung in Wasser erreicht. Durch thermische Beeinflussung (z.B. beim Schweißen) können Sekundärphasen ausgeschieden und die Korrosionsbeständigkeit des Werkstoffs gesenkt werden. Dies wurde durch eine isotherme Warmauslagerung bei 500 °C bis 900 °C für 0,1 h bis zu 72 h simuliert. Die Veränderung der Korrosionsbeständigkeit wurde mit dem DL-EPR-Verfahren und durch die angepasste KorroPad-Prüfung ermittelt. Die ermittelten Anfälligkeitsbereiche wurden miteinander Verglichen und in zwei Sensibilisierungsschaubildern zusammengefasst.
Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden ermittelt und interpretiert.
Gefüge und Eigenschaften nichtrostender Stählen werden maßgeblich von ihrer chemischen Zusammensetzung und der Wärmebehandlung bestimmt. Eine spezielle Werkstoffgruppe der austenitischen nichtrostenden Stähle enthält ca. 19 Gew.-% Mangan und 0,8 Gew.-% Stickstoff, um das austenitische Gefüge ohne das Legieren mit Nickel sicherzustellen. Die herausragenden mechanischen Eigenschaften dieser Werkstoffe (Rm von 900 2.000 MPa, A5 > 50 %, Av > 350 J) werden nach der Wärmebehandlung (Lösungsglühen und Abschrecken) durch gezielte Kaltverfestigung eingestellt. Das Lösungsglühen beseitigt vorhandene Kaltverfestigung und unerwünschte Ausscheidungsphasen (Cr2N, M23C6 und Sigma-Phase) und bewirkt die homogene Verteilung der Legierungselemente (insbesondere Stickstoff) im Austenit. Dies ist zur Erzielung der Korrosionsbeständigkeit von entscheidender Bedeutung. Im Poster werden systematische Untersuchungen zur Korrosionsbeständigkeit dieser vielversprechenden Werkstoffklasse vorgestellt und die Interaktion zwischen Legierungszusammensetzung, Wärmebehandlung, Gefüge und Korrosionsbeständigkeit dargestellt. Insbesondere der Einfluss von Warmauslagerungsversuchen nach dem Abschrecken wird dabei charakterisiert. Die vom Gefüge bedingten Veränderungen der Korrosionsbeständigkeit werden durch verschiedene Methoden (EPR, KorroPad, Lochkorrosionspotentiale) ermittelt und interpretiert.