Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (443) (entfernen)
Dokumenttyp
- Vortrag (443) (entfernen)
Sprache
- Englisch (287)
- Deutsch (149)
- Mehrsprachig (6)
- Spanisch (1)
Referierte Publikation
- nein (443)
Schlagworte
- Additive Manufacturing (32)
- Korrosion (27)
- Corrosion (21)
- Additive Fertigung (15)
- Additive manufacturing (13)
- MIC (11)
- Microstructure (9)
- Thermografie (9)
- Welding (9)
- Diffraction (8)
Organisationseinheit der BAM
- 9 Komponentensicherheit (105)
- 6 Materialchemie (95)
- 8 Zerstörungsfreie Prüfung (82)
- 7 Bauwerkssicherheit (79)
- 5 Werkstofftechnik (64)
- 7.6 Korrosion und Korrosionsschutz (57)
- 9.3 Schweißtechnische Fertigungsverfahren (52)
- 8.5 Röntgenbildgebung (42)
- 9.4 Integrität von Schweißverbindungen (39)
- 8.0 Abteilungsleitung und andere (31)
Eingeladener Vortrag
- nein (443)
The initial focus of this research was on the development of a general workflow for the documentation and monitoring of historical stained glass windows using structured light scanning.
Therefore windows from different churches, time periods and with different corrosion and damage phenomena were scanned before and after conservation measures.
The weld pool dynamics and shape play a fundamental role in keyhole mode welding. The presented work aims the experimental and numerical investigation of the influence of the weld pool characteristics on the formation of hot cracking. The experimental procedure allows recording the molten pool in the longitudinal section of a butt joint configuration of 15 mm thick structural steel and transparent quartz glass by using a high-speed video camera and two thermal imaging cameras. The observations show that the dimensions of the weld pool vary depending on the depth. The regions close to the surface form a teardrop-shaped weld pool. A bulge-region and its temporal evolution are observed approximately in the middle of the depth of the weld pool, where hot cracking appears. A numerical framework including models for the weld pool dynamics, global temperature field, transient stress state, crystal growth, diffusion and macro-segregation and subroutines for their one-way couplings is developed. The numerically obtained and experimentally observed results are in a good agreement. It is shown that the bulge-region leads to a delay in the solidification behavior, increased temporal tensile stresses and accumulation of impurities in the defect region and hence enhance the probability of hot cracking formation.
A look inside nanoparticles
(2019)
Small-angle scattering is the method of choice when it comes to obtaining information about the interior of nanoparticles. The aim is to make nanotechnology safer. While the use of small-angle neutron scattering (SANS) is limited to a few instruments in the world, small-angle X-ray scattering (SAXS) is widely accessible, with an upward trend. The example of core-shell particles shows how simple their analysis is with data from an Anton Paar laboratory system. Here, SAXS is a central tool for the development of new reference materials based on poly(methyl) acrylate-PVDF core-shell particles. The dimensions of the cores and shells can be precisely determined. A detailed analysis makes it possible to show that the cores contain fluorinated and nonfluorinated polymers, whereas the shell consist only of PVDF. This core-shell particles with a diameter around 40 nm show a significantly higher PVDF beta phase content than the PVDF homopolymer when using an emulsion polymerization technique. This finding is of importance with respect to applications in electroactive devices.
Laser-induced periodic surface structures (LIPSS, ripples) are a universal phenomenon that can be observed on almost any material after the irradiation by linearly polarized laser beams, particularly when using ultrashort laser pulses with durations in the femtosecond to picosecond range.
During the past few years significantly increasing research activities have been reported in the field of LIPSS, since their generation in a single-step process provides a simple way of nanostructuring and surface functionalization towards the control of optical, mechanical, biological, or chemical surface properties. In this contribution the mechanisms of formation and current applications of LIPSS are reviewed, including the colorization of technical surfaces, the control of surface wetting properties, the mimicry of the natural texture of animal integuments, the tailoring of surface colonization by bacterial biofilms, the advancement of medical pacemakers, and the improvement of the tribological performance of nanostructured metal surfaces.
The additional element from the filler wire in the laser beam welding is usually distributed inhomogeneously in the final weld due to the high solidification rate of weld pool. It has been found that the electromagnetic stirring produced by an external oscillating magnetic field can enhance the material mixing in the weld pool to achieve a more uniform element distribution. However, the magnetic field has a highly non-linear and multi-coupled interaction with the weld pool behavior, which makes the quantitative explanation of the physical mechanism difficult. In this study, the effect of electromagnetic stirring on the transport phenomena in the wire feed laser beam welding is investigated by a numerical modelling. A 3D transient multi-physical model considering the magnetohydrodynamics, heat transfer, fluid flow, keyhole dynamics and element transport is developed. The multiple reflections and the Fresnel absorption of the laser on the keyhole wall are calculated using the ray tracing method. The numerical results show that a Lorentz force produced by the oscillating magnetic field and its induced eddy current gives significant influence on the transport phenomena in the molten pool. The forward and downward flow is enhanced by the electromagnetic stirring, which homogenizes the distribution of the additional elements from a nickel-based filler wire in a steel weld pool. The numerical results show a good agreement with the high-speed images of the molten pool, the fusion line from the optical micrograph and the element distribution from the energy dispersive X-ray spectroscopy. This work provides a physical base for the electromagnetic-controlled laser beam welding and some guidance for the selection of electromagnetic parameters.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
To date, there are only very few technologies available for the conversion of low temperature waste heat to electricity. In this talk, we first describe the principle of thermomagnetic generators. Then we focus on the impact of topology of the magnetic circuit within thermomagnetic generators. We demonstrate that the key operational parameters strongly depend on the genus, i.e. the number of holes within the magnetic circuit.
Die Präsentation gibt einen Überblick bezüglich der von der BAM im Rahmen des SimCoLas Verbundprojekts durchgeführten Arbeiten zum Thema "Photonische Prozessketten". Die numerisch abgebildete Prozesskette Tiefziehen/Laserstrahlschweißen wird darsgestellt und diskutiert. Fokus der Diskussion ist die entwickelte Methodik zur konsistenten Abbildung numerischer Prozessketten mit der Applikation Heissrisskritikalität beim Laserstrahlschweißen.
During a European convention of the authorities for market surveillance (AdCO) for explosives the activities of the notified bodies are presented, putting a focus on matters concerning market surveillance.
The presentation outlined in detail, which verifications are possible
with explosives, while practical tests involving initiation of
explosives are excluded. Elements of labeling and the conclusions in
view of quality control were explained, and typical failures by
manufacturers to comply were orally described.
Powder bed -based technologies are amongst the most successful Additive Manufacturing (AM) techniques. "Selective laser sintering/melting" (SLS/SLM) and "binder jetting 3D printing" (3DP) especially are leading AM technologies for metals and polymers, thanks to their high productivity and scalability. In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method which enables the use of SLS/SLM and 3DP technologies for advanced ceramic materials. LSD consists in the layer-by-layer deposition of a ceramic slurry by means of a doctor blade. Each layer is deposited and dried to achieve a highly packed powder layer, which can be used for SLM or for 3DP. This technique offers high flexibility in the ceramic feedstock used, especially concerning material and particle size, and is capable of producing parts with physical and mechanical properties comparable to traditionally shaped parts. In this presentation, the LSD technique will be introduced and several examples of application to porcelain, SiC and alumina products will be reported.
The layerwise slurry deposition (LSD) has been established in the recent years as a method for the deposition of ceramic powder layers. The LSD consists in the layer-by-layer deposition of a ceramic slurry by means of a doctor blade; each layer is sequentially deposited and dried to achieve a highly packed powder layer.
The combination of binder jetting and LSD was introduced as a novel technology named LSD-print. The LSD-print takes advantage of the speed of binder jetting to print large areas, parallel to the flexibility of the LSD, which allows the deposition of highly packed powder layers with a variety of ceramic materials.
The working principle and history of the LSD technology will be shortly discussed. A theoretical background will be also discussed, highlighting advantages and drawbacks of the LSD compared to the deposition of a dry powder.
The last part of the talk will be dedicated to highlight recent results on the LSD-print of SiSiC of geometrically complex components, in collaboration between BAM and HC Starck Ceramics GmbH. Density, microstructure and mechanical properties of LSD-printed and isostatic pressed samples will be discussed and compared.
During their lifetime, polymer components subjected to mechanical loads and environmental influences show a loss of their mechanical properties required for their specific applications. In this respect, the craze-crack damage mechanism slow crack growth (SCG) is relevant for PE-HD components used in high-performance applications such as pipes and containers for the storage and transport of dangerous goods. SCG is considered to be the major failure mechanism in polyolefins and it typically occurs suddenly and unexpectedly. Due to the fields of application, SCG is a safety relevant issue. To test for the resistance of PE-HD pipe and container materials against SCG, the full-notch creep test (FNCT) is widely applied in Europe. In this study, SCG phenomena in PE-HD are investigated in detail based on an improved FNCT, especially including the consideration of the influence of environmental liquids effecting the damage mechanism. Using an enhanced fracture surface and a crack propagation analysis with imaging techniques such as light microscopy (LM), laser scanning microscopy (LSM), X-ray computed tomography (CT-scan) and scanning electron microscopy (SEM), detailed data concerning SCG are obtained.
The combined application of FNCT and such imaging techniques is explicitly advantageous and recommended to gain important information on damage occurring to PE-HD induced by mechanical stress and the influence of environmental liquids, which is essential within the Fourth Industry Revolution.
Powder bed -based technologies are amongst the most successful Additive Manufacturing (AM) techniques. "Selective laser sintering/melting" (SLS/SLM) and "binder jetting 3D printing" (3DP) especially are leading AM technologies for metals and polymers, thanks to their high productivity and scalability.
However, the flowability of the powder used in these processes is essential to achieve defect-free and densely packed powder layers. For standard powder bed AM technologies, this limits the use of many raw materials which are too fine or too cohesive.
This presentation will discuss the possibilities to either optimize the powder raw material to adapt it to the specific AM process, or to develop novel AM technologies which are able to process powders in a wider range of conditions.
In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method which enables the use of very fine ceramic particles.
Powder bed -based technologies are amongst the most successful Additive Manufacturing (AM) techniques. "Selective laser sintering/melting" (SLS/SLM) and "binder jetting 3D printing" (3DP) especially are leading AM technologies for metals and polymers, thanks to their high productivity and scalability.
However, the flowability of the powder used in these processes is essential to achieve defect-free and densely packed powder layers. For standard powder bed AM technologies, this limits the use of many raw materials which are too fine or too cohesive.
This presentation will discuss the possibilities to either optimize the powder raw material to adapt it to the specific AM process, or to develop novel AM technologies which are able to process powders in a wider range of conditions.
In this context, the "layerwise slurry deposition" (LSD) has been developed as a layer deposition method which enables the use of very fine ceramic particles. Another technology, the Gas Flow Assisted Powder Deposition, can increase the stability of the powder bed and the packing density, even in extreme conditions such as in absence of gravitational forces.
The rational synthesis and use of nanomaterials require the characterization of many different properties, ranging from particle size and size distribution over surface chemistry to more applicationrelevant features like optical, electrochemical, and magnetic properties. In the following, several methods for the characterization of functional groups on nanomaterials, like polymer and silica nanoparticles, semiconductor quantum dots, and lanthanide-based upconversion nanocrystals are presented. Additionally, procedures for the measurement of the key spectroscopic performance parameters of nanomaterials with linear and nonlinear photoluminescence, such as the photoluminescence quantum yield, are presented for the UV/vis/NIR/SWIR.
An overview of the BAM funed Focus Area Materials Project "AGIL" will be presented. AGIL focussed on the stdiy of the ageing characteristics of additively manufactured austenitic stainless steel with a "powder to mechanical failure" Approach. Recent Highlights are presented and a perspective for future studies.
At BAM, which is a federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes assessment of elastomeric seals applied in the casks. One of the aims is to identify a suitable method for estimating the service lifetime of the seals with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) for up to five years. In order to assess sealability, O-rings were aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings were aged as well. In order to understand the underlying ageing mechanisms in each material, material properties such as hardness, density and tensile properties were examined. Additionally, compression set (CS), which represents the recovery behaviour of a seal after release from compression, is measured. For obtaining results closely related to practical conditions, O-rings with a full-scale cord diameter of 10 mm were aged. However, this set-up can lead to heterogeneous ageing caused by diffusion-limited oxidation (DLO) effects especially for HNBR, resulting in distorted bulk properties such as compression set. However, if DLO-affected data is excluded, extrapolations of CS data are possible using time-temperature shifts.
For selecting an appropriate end-of-lifetime criterion, leakage rate measurements were performed, since leakage rate is the only characteristic directly correlated to the performance of the sealing system. A significant increase in leakage rate was considered as the end of the lifetime. However, the O-rings remained leak tight under static conditions even though material properties had already degraded strongly. For this reason, a modified, more demanding leakage test involving a fast small decompression of the seal was developed that allowed determining a more conservative end-of-lifetime criterion with a safety margin for EPDM seals. FKM, which is a very heat and oxidation resistant material, exhibited only little degradation, even though it had the smallest activation energy.
AKR an Betonfahrbahndecken - ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion(AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt.
Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCI-Zugabe die Löslichkeit von SiÖ2 zunimmt und die von AI2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löse versuche veranschaulichen, dass die nach der Alkali-Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügbaren Gesteinskörnungen.
Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliempfindlich eingestuften Gesteinskörnungen erlaubt.
Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Aufträge der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorgestellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmittel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydrophobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundären Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.