Niobium carbide is a ceramic material which can be used with excellent results to replace tungsten carbide with cobalt binder. Furthermore, it might be manufactured by classic ceramic technologies and even colloidal processing. To achieve high toughness and strength, it is necessary to have a perfect mix of hard phase and binder, which is mainly achieved by ball milling. Mechanical and physical properties as well as results on different tribological and application-oriented machining tests are presented. The results have been compared with results obtained with NbC grades with Co and Fe3Al binders as well as with pure binderless hot-pressed NbC and SPS sintered Nb2O5.
In the present work it was shown that the addition of VC or a combination of VC + Ti(C0.7N0.3) was efficient in reducing the NbC grain growth during liquid phase sintering, when compared to NbC-Ni equivalents. A finest NbC grain size of 1.48 µm was obtained in the NbC-15 Ti(C0.7N0.3)-10 Ni-7.5 VC cermet, exhibiting a hardness of 1486 +/- 7 kg/mm2 and a fracture toughness of 8.7 +/- 0.1 MPa m 1/2.