Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
Sprache
- Englisch (24)
Referierte Publikation
- ja (24) (entfernen)
Schlagworte
- Steel (24) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (6)
- 5.1 Mikrostruktur Design und Degradation (6)
- 9 Komponentensicherheit (6)
- 6 Materialchemie (5)
- 9.0 Abteilungsleitung und andere (4)
- 6.1 Oberflächen- und Dünnschichtanalyse (2)
- 7 Bauwerkssicherheit (2)
- 7.6 Korrosion und Korrosionsschutz (2)
- 9.4 Integrität von Schweißverbindungen (2)
- 5.0 Abteilungsleitung und andere (1)
Paper des Monats
- ja (1)
Industries transporting CO2 gas-saturated fluids have infrastructures made of carbon steel. This is a good material with great mechanical properties but prone to corrosion and potential failure. Corrosion in sweet environments involves the formation of FeCO3 as a corrosion film, which is recognized to play a protective role under certain conditions. This work on the dissolution of corrosion films in sweet environments, under acidic and undersaturated conditions, demonstrates that the effects on the integrity of steel are far more significant than the damage observed on the surface of the corrosion film. Our results prove that dissolution of FeCO3 involved the presence of an amorphous phase, the intermediate formation of FeCl2 or FeCl+, and the presence of a phase with short distance atom–atom correlations. The amorphous phase was identified as a mixture of retained γ-Fe and Fe3C. Partially broken α-Fe and Fe3C structures were identified to prove the damage on the material, confirming the interface zone without evident damage on the corrosion film. Dissolution affected both the α-Fe and FeCO3, with the lattice [102̅] from the FeCO3 crystalline structure being the fastest to dissolve. The damage of steel at the molecular scale was evident at the macroscale with pit depths of up to 250 μm. The impact on the integrity of steel can be, therefore, more drastic than frequently reported in industrial operations of CO2 transport industries that use cleaning procedures (e.g., acid treatment, pigging) as part of their operational activities.
To visualize the varying tetragonal distortions in high carbon martensitic steels by EBSD, two different approaches have been applied on backscattered Kikuchi diffraction (BKD) patterns. A band-edge refinement technique called Refined Accuracy (RA) (Oxford Instruments) is compared with a technique called Pattern Matching (PM), which optimizes the fit to a simulated BKD signal. RA distinguishes between hypothetical phases of different fixed 𝑐∕𝑎, while PM determines a best fitting continuous 𝑐∕𝑎 by projective transformation of a master pattern. Both techniques require stored BKD patterns.
The sensitivity of the 𝑐∕𝑎-determination was tested by investigating the microstructure of a ferritic steel with an expected 𝑐∕𝑎 = 1. The influence of the Kikuchi pattern noise on 𝑐∕𝑎 was compared for a single or 40 averaged frames per measuring point, and turned out to be not significant. The application of RA and PM on the martensitic microstructure delivered qualitatively similar maps of 𝑐∕𝑎. The comparison of RA and PM shows that RA is suitably fast and precise during mapping the martensite 𝑐∕𝑎 ratio in analyses of high carbon martensite, especially for fast initial surveys. As RA leads quantitatively to higher noise in 𝑐∕𝑎, the PM analysis can be used for higher precision results.
This paper is focused on the approximation of absorbed Charpy impact energy-temperature curves (KV-T) and the management of sub-size test piece results in Charpy pendulum impact tests. Both subjects are frequently underestimated but may have a strong impact on the assessment of product quality and structural integrity. The status of related test standards, product standards, structural integrity assessment procedures and corresponding research is reviewed.
It is concluded that the state of regulation is partly insufficient and wrong. There is a wide gap between the state of knowledge in the field of materials testing and the requirements of product standards and structural integrity assessment procedures. The present paper aims at boosting and supporting the necessary discussion among the parties involved to raise the level of technical safety. Correspondingly, a large experimental database was created by Charpy impact testing of popular modern structural Steels with nominal yield strength from 235 MPa to 960 MPa. KV-T data were generated using test pieces with thicknesses between 2.5 mm and 10 mm. Different strategies for KV-T curve fitting, definition of transition temperatures, as well as upper and lower shelf energy levels were followed, and different scaling procedures were applied to the sub-size test piece results. The results show that proportional scaling of sub-size to full-size test piece results in terms of KV should be disallowed because it is a wrong approach.
Regulations still incorporating such procedures should be revised as soon as possible. Existing nonproportional scaling and conversion procedures were applied. The results obtained illustrate that neither an overall nor consistent conservatism nor an adequate conservatism level can be achieved. In summary, the standardizing bodies should enforce the discussion to revise relevant test standards considering more precise specifications on Charpy data fitting. Furthermore, proposals are made for an improved management of sub-size test piece results.
As onshore installation capacity is limited, the increase in the number of offshore wind turbines (OWT) is a major goal. In that connection, the OWTs continuously increase in size and weight and demand adequate foundations concepts like monopiles or tripods. These components are typically manufactured from welded mild steel plates with thickness up to 200 mm. The predominant welding technique is submerged arc welding (SAW). In accordance with the standards, the occurrence of hydrogen-assisted cracking is anticipated by either a minimum waiting time (MWT, before non-destructive testing of the welded joint is allowed) at ambient or a hydrogen removal heat treatment (HRHT) at elevated temperatures. The effectiveness of both can be estimated by calculation of the diffusion time, i.e., diffusion coefficients. In this study, these coefficients are obtained for the first time for a thick-walled S420G2+M offshore steel grade and its multi-layer SAW joint. The electrochemical permeation technique at ambient temperature is used for the determination of diffusion coefficients for both the base material and the weld metal. The coefficients are within a range of 1025 to 1024 mm2/s (whereas the weld metal had the lowest) and are used for an analytical and numerical calculation of the hydrogen diffusion and the related MWT. The results showed that long MWT can occur, which would be necessary to significantly decrease the hydrogen concentration. Weld metal diffusion coefficients at elevated temperatures were calculated from hydrogen desorption experiments by carrier gas hot extraction. They are within a range of 1023 mm2/s and used for the characterization of a HRHT dwell-time. The analytical calculation shows the same tendency of long necessary times also at elevated temperatures. That means the necessary time is strongly influenced by the considered plate thickness and the estimation of any MWT/HRHT via diffusion coefficients should be critically discussed.
Metals that are exposed to high pressure hydrogen gas may undergo detrimental failure by embrittlement. Understanding the mechanisms and driving forces of hydrogen absorption on the surface of metals is crucial for avoiding hydrogen embrittlement. In this study, the effect of stress-enhanced gaseous hydrogen uptake in bulk metals is investigated in detail. For that purpose, a generalized form of Sievert's law is derived from thermodynamic potentials considering the effect of microstructural trapping sites and multiaxial stresses. This new equation is parametrized and verified using experimental data for carbon steels, which were charged under gaseous hydrogen atmosphere at pressures up to 1000 bar. The role of microstructural trapping sites on the parameter identification is critically discussed.
Interpreting high-temperature corrosion induced by mixed-gas atmospheres is challenging due to the different contributions of oxidizing gases. Here, a comprehensive study on the combined oxidation/sulfidation using label molecules is presented. Fe-Cr model alloys with 2 wt% and 9 wt% Cr were isothermally exposed using a volumetric mixture of 0.5%S16O2/27%H218O and 0.5%S16O2/7%H218O at 650 ◦C for 5 h and then characterized by secondary ion mass spectroscopy (SIMS). Additionally, the reactions were followed in-situ utilizing energy dispersive X-ray diffraction. The study showed that both S16O2 and H218O contribute to the oxidation of the alloys but to different extents depending on the Cr-content.
Determination of fatigue crack propagation thresholds for steel in presence of environmental effects
(2021)
The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed.
Geothermal brines often contain high amounts of lead and copper ions that can precipitate as native Cu and Pb as consequence of galvanic corrosion when brines react with carbon steel materials. This contribution evaluates which materials could overcome the problem of galvanic corrosion at geothermal environment.
The behavior of these materials in water containing high chloride concentration (> 100 g/L NaCl) as well as various amounts of dissolved bCl2 and/or CuCl2 was characterized by electrochemical and exposure measurements.
Both methods reveal carbon steel suffers corrosion susceptibility, accompanied by Cu◦ and/or Pb◦ precipitation on the surface. Electrochemical measurements on stainless steels result in significant difference in corrosion and repassivation potentials (Ecorr = -189 mV, Erep = 70 mV), indicating a good corrosion resistance.
Offshore wind turbines (OWT) are a major goal of the energy strategy of Germany encompassing the increase of the installed wind power. OWT components are manufactured from welded steel plates with thicknesses up to 200 mm. The underlying standards and technical recommendations for construction of OWTs encompass specifications of so-called minimum waiting time (MWT) before non-destructive testing of the weld joints is allowed. Reason is the increased risk of time-delayed hydrogen assisted cold cracking as hydrogen diffusion is very slow due to the very thick plates. The strict consideration of those long MWT up to 48 h during the construction of OWTs leads to significant financial burden (like disproportionately high costs for installer ships as well as storage problems (onshore)). In this study, weld joints made of S355 ML were examined in comparison with the offshore steel grade S460 G2+M. The aim was to optimize, i.e., reduce, the MWT before NDT considering varied heat input, hydrogen concentration and using self-restraint weld tests. This would significantly reduce the manufacturing time and costs of OWT construction. To quantify the necessary delay time until hydrogen-assisted cold cracks appear, acoustic emission analysis was applied directly after welding for at least 48 h.
The impact of the microstructure of Fe-16Cr-0.2C on high-temperature oxidation – sulphidation in SO2
(2021)
This study elucidates the impact of the microstructure of Fe-16Cr-0.2C on oxide layer formation at 650 ◦C in Ar-0.5 % SO2. A cold-rolled and two heat-treated states of the alloy were exposed for up to 1000 h. The samples were characterised in detail from microstructural and chemical perspectives using scanning electron microscopy (SEM), X-ray diffraction (XRD) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). The microstructural modification of the alloy by heat-treatment was advantageous. It was found that Cr-carbides support chromia formation and reduce sulphidation when their area fraction is low and diameter is small.