Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Posterpräsentation (7)
- Vortrag (4)
- Forschungsdatensatz (1)
Sprache
- Englisch (12)
Referierte Publikation
- nein (12)
Schlagworte
- PE-HD (12) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (4)
- 5.3 Polymere Verbundwerkstoffe (4)
- 7 Bauwerkssicherheit (4)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (4)
- 4 Material und Umwelt (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 5.5 Materialmodellierung (1)
Eingeladener Vortrag
- nein (4)
The dataset provided in this repository comprises data obtained from a series of full-notch creep tests (FNCT) performed on selected high-density polyethylene (PE-HD) materials (for further details, see section 1 Materials in this document) in accordance with the corresponding standard ISO 16770.
The FNCT is one of the mechanical testing procedures used to characterize polymer materials with respect to their environmental stress cracking (ESC) behavior. It is widely applied for PE-HD materials, that are predominantly used for pipe and container applications. It is based on the determination of the time to failure for a test specimen under constant mechanical load in a well-defined and temperature controlled liquid environment. The test device used here also allows for continuous monitoring of applied force, specimen elongation and temperature.
As the well-known damage mechanisms slow crack growth (SCG) and environmental stress cracking (ESC) are the major causes for possible failure of polyolefin-based materials, especially for PE-HD, they are highly relevant and need to be considered thoroughly. Furthermore, due to slight but perceptible differences in damaging effect, a differentiation between SCG and ESC is expedient. SCG appears in “inert” or “neutral” media without a decisive influence of the surrounding medium whereas ESC occurs in “active” media, which influence the failure behavior and time to failure crucially.
To characterize the inherent resistance of the material against those damage mechanisms, the well-established Full-Notch Creep Test (FNCT) is used. In this study, the FNCT – usually applied according to ISO 16770 [3] using a few universal model liquid media and mainly for pipe materials – is extended by investigations with appropriate parameters of selected relevant PE-HD container materials also in real media, such as the topical fuels diesel and biodiesel. The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Especially, mechanical stress and temperature were varied systematically during FNCT and time to failure values, time-dependent elongation data as well as detailed fracture surface analysis by laser scanning microscopy (LSM) were combined for the first time (Fig. 1). Particularly, the fracture surface analysis provides a sound basis to characterize failure behavior, mainly regarding the balance between brittle crack propagation and ductile deformation. Therefore, fracture surface analysis is an essential tool for a decent assessment of SCG and ESC by FNCT measurements.
The first documentation of fuel biodeterioration dates back to the late 19th century. However, extensive studies concerning the microbial fuel contamination started in 1980’s. Polymeric fuel storage tanks containing diesel and biodiesel provide environmental conditions for microbial growth. Several studies demonstrated that bacteria, which were found in contaminated fuel systems, can use fuels as macronutrient; but such bacteria can also cause microbiologically influenced corrosion and fouling.
The aim of this study is to investigate the initial attachment behavior of bacteria, isolated from a diesel contamination, on neat and photooxidized high-density polyethylene (PE-HD). Two common PE-HD’s, less- and biodiesel-stabilized, were radiated to UV light representing a tank exposed to sunlight. The effect of photooxidiation on PE-HD’s surface were characterized chemically by Fourier-transform infrared spectroscopy (FTIR). The attached bacteria Pseudomonas aeruginosa and Bacillus subtilis on the polymer surface were evaluated by fluorescence microscopy and colony-forming unit tests (CFU).
PE-HD as a polymeric fuel storage tank material: Photooxidation, fuel sorption and long-term storage
(2018)
High-density polyethylene (PE-HD) is a commodity thermoplastic polymer which is typically used for packing of dangerous goods. Its good resistance against photooxidation, fuels, chemicals and other environmental factors in addition to low production costs makes PE-HD attractive for fuel storage applications. Typical engine fuels stored in polymer tanks are petrol, diesel and biodiesel that receives increasing attention as proper alternative to fossil fuels. One of the major problems with biodiesel is its susceptibility to oxidize due to its chemical composition of unsaturated fatty acids which also can cause polymer degradation.
The aim of this study is to investigate the influence of different environmental factors, UV radiation and commonly stored fuels, on the mechanical, physical and chemical properties of two types of PE-HD polymers (stabilized and non-stabilized). The influence on the mechanical properties was tested by Charpy and tensile tests, chemical and physical properties were evaluated by Fourier-transform infrared spectroscopy (FTIR) and by dynamical mechanical analysis (DMA) tests. Samples were characterized after varying exposure time of UV radiation and after fully and partially immersion in biodiesel. In addition, similar experiments were conducted using diesel for comparison.
Damage of PE-HD induced by liquid media - Full Notch Creep Testing (FNCT) and Imaging analysis
(2017)
Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications.
Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant damage mechanisms. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure.
To characterize the inherent resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used. Therefore, the FNCT is of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD – especially for automotive but also for most other high-performance applications.
In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigations of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed.
The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Additional to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Correlations of elongation behavior and data derived from imaging analysis such as fracture plane roughness were obtained.
High-density polyethylene (PE-HD) is a widely applied plastic for fuel storage tank applications. But such tanks, filled with diesel or biodiesel, provide excellent environmental conditions for growth of a broad spectrum of fungi and various bacteria1. This can result in fuel contamination, engine plugging or possible (bio-) degradation2. Our research focusses on the initial attachment phase of Bacillus sp. and Pseudomonas aeruginosa isolated from a „dieselpest“2 on two distinctly PE-HD materials, typical for fuel storage tank applications, pre-damaged thermally and by UV-irradiation.
Sustainable energy and clean engine fuels receive more and more attention. Petrodiesel could be substituted by biofuels such as biodiesel produced from renewable resources. Biodiesel is derived by transesterification of oils with alcohols for example vegetable oils, animal fats or food waste. Its chemical composition of unsaturated fatty methyl acids causes biodiesels susceptibility to oxidation. Especially, the polymer-biodiesel performance under long-term conditions has been considered only in few researches.
Our study addresses a long-term storage scenario of a polymeric fuel tank containing biodiesel or diesel.
Renewable resources become more and more relevant to maintain energy demands for an increasing global population. Biosynthetic fuels like biodiesel might replace conventional petrochemical fuels. In this study the influence of microbial growth on biodiesel and diesel on the storage tank systems were investigated. Polymeric fuel storage tanks for diesel and biodiesel provide suitable environmental conditions for a broad spectrum of fungi and various bacteria, including cyanobacteria and aerobic heterotrophic, and even anaerobic, fermentative Bacteria. However, the questions whether and how ageing of the materials is affected by biofouling processes have not been answered so far. Therefore, a model system for biofilm formation was established to study the initial attachment phase of bacteria in dependency of ageing, quality and surface modification of thermoplastic polymers used for storage tank systems. The microbial survey is closely connected with a detailed characterization of the material’s properties and its ageing processes.
A widely applied plastic used for fuel storage tanks is high-density polyethylene (PE-HD), which is available with various additives to increase UV-light stability and even for the storage of biodiesel. These materials were aged under UV-light and temperature using a defined climate chamber set-up. Further, the repeated filling of fuels was mimicked for such storage tanks, as this has an important impact on the life-cycle length for the storage Container. The aged polymers showed a significant change in the material’s characteristics, including surface characteristics (e.g. hydrophobicity) and carbonyl groups. The effect of the changed material properties on the biofilm formation are studied using bacterial isolates, previously obtained from a “dieselpest”, and as a model-reference E. coli. The unaged polymers showed already some significant differences for the initial attachment of E. coli K12. Polyethylene with additives was colonized faster than the reference material (without additives) although the final biofilm coverage was not impaired. Likewise, the settlement of a kerosene-isolated Bacillus species on the unaged materials independently of additives was only minor interfered.
In future, our results should give stakeholders in industry and public authorities a better estimation of the life-cycle security for fuel storage tank systems and on the fuel quality. Further, our results could help to test and develop new materials or additives to prevent biofouling processes.
The FNCT is widely used to characterize the slow crack growth (SCG) behavior of polyolefinic materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure. The test is of greatest importance for pipe and blow molding types of PE-HD - especially for transport and packaging of dangerous goods but also for most other high-performance applications.
Usually the FNCT is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100.
In our study, selected relevant PE-HD materials are investigated also in real media – practical formulations as well as representative pure chemicals – and influences of temperature and geometry of specimen and notch are explicitly addressed. Furthermore, the investigations comprise also the ESC behavior of PE-HD in media that are sorbed to a significant extent – one example are fuels, such as diesel and biodiesel – based on comparison with samples previously saturated with those media. Thus, also the underlying diffusion controlled sorption process has to be assessed before.
The investigations were performed using a FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
The Full-Notch Creep Test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure tf*. Usually the FNCT is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100 (detergent).
Selected relevant PE-HD materials are investigated also in real media and influences of temperature and geometry of specimen and notch are explicitly addressed. The investigations comprise also the ESC behavior of PE-HD in media that are sorbed to a significant extent – such as Diesel and Biodiesel – based on comparison with samples previously saturated with those media.