Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (2) (entfernen)
Sprache
- Englisch (2)
Schlagworte
- Crack initiation (2) (entfernen)
Organisationseinheit der BAM
Irradiation assisted stress corrosion cracking (IASCC) is known to be a combination of applied stress, and a corrosive environment in irradiated materials, but an appropriate understanding of how each of these components affects cracking is not yet clear. In this work, we isolate the role of grain boundary (GB) oxidation in IASCC. For this purpose, solution-annealed 304L stainless steel irradiated in reactor to 5.4 or 69 dpa was studied using a miniaturized four-point bend technique. Two modes of bend tests were conducted; straining in simulated pressurized water reactor primary water (PW) at 320 ◦C in an incremental manner, and pre-oxidation in PW at 320 ◦C without application of stress followed by dynamic straining in purified Ar at the same temperature until crack initiation. Exposure of the 5.4 dpa sample for 210 h in high temperature water initiated cracks in Ar at 60% of the yield stress (0.6YS), whereas the companion sample of the same dose exposed for 1010 h cracked in Ar at 0.5YS. The long-term exposure in water led to GB oxidation that ultimately lowered the crack initiation stress. Dynamic straining in water resulted in larger crack lengths and greater crack depths indicating stress accelerated oxidation and cracking. Dislocation pile-ups at dislocation channel-grain boundary sites provide an amplification of the applied stress to a level consistent with the fracture stress of the grain boundary oxide, providing an explanation for IASCC that occurs at applied stresses well below the irradiated yield stress of the alloy. There was no evidence of cracking upon straining of an unoxidized 69 dpa sample in Ar to well above yield, confirming that the irradiated state is not inherently susceptible to intergranular (IG) cracking and that oxidized GBs are responsible for initiation of IG cracking.
Environmentally-assisted material degradation involves mass transport and mechanical processes interacting in the material. A well-known example is hydrogen-induced stress-corrosion cracking. One major challenge within this scope is the quantification of the coupling mechanisms in question. The computational modeling of environmentally-assisted cracks is the key objective of this investigation and realised within the theory of gradient-extended dissipative continua with lengthscales. The modeling of sharp crack discontinuities is replaced by a diffusive crack model based on the introduction of a crack phase-field to maintain the evolution of complex crack topologies. Within a thermodynamical framework allowing for mechanical and mass transport processes the crack phasefield is capable to model crack initiation and propagation by the finite element method. As complex crack situations such as crack initiation, curvilinear crack patterns and crack branching are usually hard to realise with sharp crack models, they can be assessed without the requirement of a predefined crack path within this method. The numerical modeling of a showcase demonstrates a crack initiation as well as a crack propagation situation with respect to the determination of stress-intensity factors; a crack deviation situation with a curvilinear crack path is modeled by the introduction of a geometrical perturbation and a locally enhanced species concentration.