Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2018 (7) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (4)
- Vortrag (2)
- Zeitschriftenartikel (1)
Sprache
- Deutsch (7) (entfernen)
Schlagworte
- Automated manufacturing (1)
- Automatisierte Fertigung (1)
- Digitalisierung (1)
- Digitization (1)
- Electromagnetic support (1)
- Elektromagnetische Schmelzbadunterstützung (1)
- Equivalent stress concentration factors (1)
- Ferromagnetischer Stahl (1)
- Hohlprofilknoten (1)
- Hybrid laser arc welding (1)
- Kerbspannungskonzept (1)
- Laser- und Lichtbogenenergie (1)
- Laserimplantation (1)
- Laserstrahlschweißen (1)
- Lichtbogensensorik (1)
- Life Cycle Assessment (LCA) Fusion welding (1)
- Life Cycle Assessment (LCA) Impact categories (1)
- Life Cycle Assessment (LCA) Schweißprozesse (1)
- Life Cycle Assessment (LCA) Umweltwirkungen (1)
- MAG Prozesssteuerung (1)
- MSG-Engspaltschweißen (1)
- Notch stress approach (1)
- Profilvermessung (1)
- Schweißnahtgeometrie (1)
- Sensorik (1)
- Tubular joints (1)
- Weld seam geometry (1)
- Äquivalente Spannungskonzentrationsfaktoren (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
Automatisierungs- und Regelkonzepte für das MSG-Engspaltschweißen - Pendel- und Füllgradregelung
(2018)
Das MSG-Engspaltschweißen eignet sich auf Grund der I-Nahtvorbereitung besonders für das wirtschaftliche Fügen bei hohen Blechdicken über 100 mm und bietet darüber hinaus zusätzliche technologische Vorteile. Für die automatisierte Anwendung des Verfahrens unter Produktionsbedingungen muss dabei die Prozesssicherheit auch für mitunter große Variationen der Spaltbreite entlang der Schweißnaht gesichert bleiben. In erster Linie betrifft dies bei mechanischer Auslenkung der Drahtelektrode die Adaption der Pendelbewegung auf die jeweilige Spaltbreite um eine ausreichende Flankenanbindung zu garantieren. Für die Online-Regelung der Pendelbewegung mittels Lichtbogensensorik wurde eine Methode implementiert die die notwendigen Pendelwinkel an jeder Nahtflanke unabhängig ermittelt und darüber hinaus Fehlstellungen des Brenners sowie Veränderungen des Kontaktrohrabstandes und der Prozessparameter eigenständig kompensiert. Eine Füllgradregelung auf Grundlage optischer Erfassung und Auswertung der Schweißnahtgeometrie wurde zusätzlich eingesetzt um bei veränderlichen Nahtquerschnittsflächen einen vorgegebenen, gleichbleibenden Lagenaufbau zu erzielen.
Das bislang zur Vermeidung unzulässiger Wurzelüberhöhungen beim Laserstrahlschweißen von Aluminiumlegierungen bzw. austenitischem Stahl eingesetzte Verfahren der elektromagnetischen Schmelzbadstütze konnte innerhalb der vorliegenden Untersuchung erfolgreich zur Kompensation des hydrostatischen Druckes von ferromagnetischen Stählen übertragen werden. Es wurden dabei Laserstrahlschweißversuche in PA-Position an bis zu 20 mm dickem Duplexstahl 1.4462 sowie Baustahl S235JR durchgeführt. Unter konstanten Schweißparametern wurden Durchschweißungen generiert. Dem hydrostatischen Druck wurde unter Verwendung der Technologie zur elektromagnetischen Schmelzbadunterstützung durch Variation der Oszillationsfrequenz und der AC-Leistung des Magnetsystems entgegengewirkt.
Zunächst konzentrierten sich die Versuche auf den Duplexstahl 1.4462, welcher jeweils aus 50 % Ferrit und Austenit besteht. Hierbei konnte festgestellt werden, dass zur idealen Kompensation von 15 mm bei einer Frequenz von 1,7 kHz eine AC-Leistung von 1,6 kW erforderlich ist, die Schweißnähte aber bereits bei einer AC-Leistung von ca. 0,8 kW in die Bewertungsgruppe B der DIN EN ISO 13919-1:1996-09 eingeordent werden können. Zur idealen Kompensation des hydrostatischen Druckes bei 20 mm dickem Duplexstahl war eine um 20 % höhere AC-Leistung notwendig. Im Anschluss an die Versuche mit dem Duplexstahl wurden die Untersuchungen auf bis zu 20 mm dicke Proben aus Baustahl S235JR erweitert. Für 15 mm konnten die Schweißnähte bei einer Frequenz von 1,7 kHz ab einer AC-Leistung von 1,3 kW in die Bewertungsgruppe B eingeordnet werden. Zur idealen Kompensation von 20 mm dickem Baustahl war eine AC-Leistung von 1,6 kW bei einer Frequenz von 636 Hz nötig. Mit steigender AC-Leistung konnte in allen Versuchsreihen eine sukzessive Verringerung
der Wurzelüberhöhung demonstriert werden.
Hybrides Auftragschweißen: Potentiale des laserunterstützten Plasma-Pulver-Auftragschweißens (PTA)
(2018)
In diesem Beitrag wurden Untersuchungen zu einem neuartigen hybriden Laser-Plasma-Beschichtungsverfahren vorgestellt. Mit dem Ziel, die Produktivität und Wirtschaftlichkeit von Korrosions- und Verschleißschutzschichten zu steigern, wurde das kostengünstige PTA-Verfahren durch einen Laser als zweite Energiequelle ergänzt. Die vorlaufende Laserstrahlung stabilisiert den Plasmalichtbogen und ermöglicht erst eine Auftragsschweißung bei hohen Geschwindigkeiten. Die hohen Auftragraten von 4,2-5,7 kg/h bei gleichzeitig Streckenenergien von 630-720 J/cm zeigen das mögliche Potential des vorgestellten hybriden Ansatzes. In weiteren Untersuchungen muss der Prozess z.B. in Bezug auf die Oberflächenwelligkeit der Beschichtungen über eine Parameteroptimierung weiter verbessert werden. Nach den bisherigen gesammelten Erfahrungen mit dem Hybridprozess ist davon auszugehen, dass durch eine Anpassung der Energiedichteverteilung das Lasers, die Prozessgeschwindigkeiten noch einmal gesteigert werden können.
The development within the offshore wind energy sector towards more powerful turbines combined with increasing water depth for new wind parks is challenging both, the designer as well as the manufacturer of support structures. Besides XL-monopiles the jacket support structure is a reasonable alternative due to the high rigidity combined with low material consumption. However, the effort for manufacturing of the hollow section joints reduces the economic potential of jacket structures significantly. Therefore, a changeover from an individual towards a serial production based on automated manufactured tubular joints combined with standardized pipes must be achieved. Hence, this paper addresses the welding process chain of automated manufactured tubular joints including digitization of the relevant manufacturing parameters such as laser scanning of the weld seam geometry. Additionally, a methodology for the computation of the notch radius as well as the weld seam angle is presented based on the scanned profiles of three analysis points of an automated manufactured tubular X-joint. Subsequently, these parameters are considered within the notch stress approach based fatigue design and their impact is quantified by a comparison with the structural stress approach using equivalent stress concentration factors.
In diesem Vortrag werden die aktuellen Forschungsergebnisse im Bereich der ökologischen Bilanzierung von Schweißprozessen dargestellt. Der Fokus liegt hierbei in der Ermittlung relevanter Wirkkategorien zur Charakterisierung der Umweltwirkungen von Schweißprozessen. Exemplarisch für verschiedene Verfahrenskombinationen werden die ökologischen Umweltwirkungen auf Basis eines Life Cycle Assessments ermittelt und verfahrensspezifische Einflussgrößen analysiert.
In einer Vielzahl technischer Anwendungen spielt die Aufrechterhaltung eines definierten Reibungs- und Verschleißverhaltens zwischen bewegten Oberflächen für die Sicherheit und Funktionalität eine entscheidende Rolle. Die Oberflächentechnik versucht durch geeignete Verfahren die Randschichten zu ertüchtigen, um Reibung und Verschleiß zu kontrollieren. Eine Verbesserung der Materialeigenschaften kann durch flächige Beschichtungen erreicht werden. Zusätzlich ermöglichen Oberflächenstrukturierungen breite Möglichkeiten zur Beeinflussung des Schmierungszustandes bzw. der Kontaktbedingungen. Neben Negativstrukturen bieten ebenfalls erhabene Mikrostrukturen großes Potenzial zur Beeinflussung des tribologischen Verhaltens. Ihr Einsatz ist aber aufgrund der besonderen Verschleißproblematik erhabener Strukturen momentan limitiert, so dass in der Regel zusätzliche verschleißreduzierende Beschichtungen notwendig werden.
In diesem Beitrag wurde das Verfahren der Laserimplantation angewandt, mit dem erhabene und separierte Oberflächenstrukturen hoher Verschleißfestigkeit in einem Fertigungsschritt erzeugbar sind. Das Verfahren basiert auf einem lokalisierten Dispergieren von Hartstoffpartikeln. Hierfür wurde erstmalig ein gepulster Faserlaser mit hoher Strahlqualität zur Erzeugung punkt- und linienförmiger Mikrostrukturen angewandt. Versuche wurden auf dem Kaltarbeitsstahl X153CrMoV12 unter Anwendung von Titandiborid als Hartstoff durchgeführt. Anhand von Härtemessungen konnte gezeigt werden, dass sowohl punkt- als auch linienförmige Strukturen mit Härten über 1000 HV1 und einer feinkörnigen Mikrostruktur mit feinverteilten Hartstoffpartikeln herstellbar sind. Des Weiteren war es möglich, die Implantgeometrien, welche an Querschliffen und durch Weißlichtinterferometeraufnahmen erfasst wurden, durch die Pulsleistung und Pulsdauer zu steuern.
The laser hybrid welding process offers many advantages regarding deep penetration, increased welding velocity and with the help of the supplied filler wire an improved bridgeability to gap and misalignment tolerances. High power laser systems with a power of approx. 30 kW are already available on the market. Nevertheless, multi-layer technology with an arc process is still used for welding of plates from a thickness from 20 mm. A potential cause is the process instability with increasing laser power. It is inevitable that gravity drop-out due to the high hydrostatic pressure at increasing wall thickness especially at welding in flat position and with a low welding speed. The surface tension decreases with increasing root width resulting from low welding velocities. To prevent such inadmissible defects of the seam a use of weld pool support is required. Usual weld pool support systems such as ceramic or powder supports require a mechanical detachment which is time-consuming. The electromagnetic weld pool support system described in this work shows an alternative weld pool support which works contactless. It is based on generating Lorentz forces in the weld pool due to oscillating magnetic field and induced eddy currents. This innovative technology offers single pass welds up to 28 mm in flat position and reduced welding velocity with a laser power of just 19 kW. It also leads to improved mechanical-technological properties of the seams because of the slow cooling rate. With usage of an electromagnetic weld pool support the limitation of the hybrid laser arc welding process in the thick sheet metal will be extend.