Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (30)
- Posterpräsentation (15)
- Beitrag zu einem Tagungsband (13)
- Zeitschriftenartikel (9)
- Dissertation (1)
- Forschungsbericht (1)
Schlagworte
- KorroPad (34)
- Korrosion (31)
- Nichtrostender Stahl (30)
- EPR (21)
- Corrosion resistance (20)
- Heat treatment (19)
- Wärmebehandlung (19)
- Korrosionsbeständigkeit (16)
- Lochkorrosion (16)
- Stainless steel (14)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (30)
The corrosion resistance of martensitic stainless steels (MSS) depends strongly on the chemical composition and the applied heat treatment. Both determine the distribution of the alloying elements in the microstructure and the resulting material properties. The addition of nitrogen is known to be beneficial for the pitting corrosion resistance of stainless steels. In case of MSS this effect is not only connected to nitro-gen itself because nitrogen can be used to substitute carbon which also influences the result of the heat treatment process. This paper shows the effect of nitrogen on the corrosion resistance in relation to the hardening process of MSS. Therefore the effects of austenitization temperature and cooling rate on microstructure, hardness and corrosion resistance were studied on the MSS X30CrMoN15 1 and X50CrMoV15. The effect of different cooling rates was studied using the jominy end quench test. The changes in corrosion resistance were detected with electrochemical potentiodynamic reactivation (EPR) and by the determination of critical pitting potentials. Besides this experimental approach thermodynamic calculations with the software thermocalc will be presented and used for the interpretation of the effect of nitrogen on the corrosion resistance of MSS.
Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt.
Härte, Schneidleistung und Korrosionsbeständigkeit sind die wichtigsten Qualitätsmerkmale von Schneidwaren, die nur durch eine optimal durchgeführte Wärmebehandlung des martensitischen nichtrostenden Stahls 1.4116 (X50CrMoV15) erreicht werden können. In der industriellen Fertigung wird die Korrosionsbeständigkeit von Schneidwaren durch Wechseltauchversuche überprüft, die herstellerübergreifend eine große Schwankung der Korrosionsbeständigkeit zeigen. In den letzten Jahren wurden neue elektrochemische Untersuchungsmethoden für die Werkstoffgruppe der martensitischen nichtrostenden Stähle entwickelt, welche die geringe Lochkorrosionsbeständigkeit von Schneidwaren auf das Phänomen der Chromverarmung zurückführen. Derzeit wird in der wissenschaftlichen und in der industriellen Gemeinschaft der Schritt des Anlassens als Ursache der Chromverarmung angesehen. Bei Schneidwaren sind die Anlasstemperaturen allerdings zu gering, um die auftretende Chromverarmung zu erklären. Aus diesem Grund wurde eine systematische Untersuchung der wichtigsten Wärmebehandlungsparameter: Härtetemperatur, Haltedauer, Abkühlrate und Anlasstemperatur durchgeführt, um den Einfluss aller Wärmebehandlungsparameter auf das Auftreten von Chromverarmung aufzuklären. Durch die elektrochemisch potentiodynamische Reaktivierung (EPR) erfolgte der Nachweis von Chromverarmung. Außerdem wurde die Lochkorrosionsanfälligkeit durch die anwendernahe KorroPad-Prüfung und die Bestimmung kritischen Lochkorrosionspotentiale ermittelt. Beides zeigt den Einfluss der durch die Wärmebehandlung erzeugten Chromverarmung auf die Lochkorrosionsbeständigkeit, die beim Einsatz und bei der Reinigung von Schneidwaren notwendig sind.
Die Korrosionsbeständigkeit geschweißter Konstruktionen aus nichtrostenden Duplexstählen wird von den Schweißparametern und der Nachbehandlung der Oberflächen bestimmt. Eine etablierte Methode der Schweißnahtnachbehandlung ist das Strahlen der Oberfläche mit Glasperlen. Diese Methode soll aus wirtschaftlichen Gründen durch das Strahlen mit Korund ersetzt werden, welches deutliche Zeit- und Kostenvorteile bietet. Besonders bei der Lochkorrosionsbeständigkeit hat sich das Schleifen mit Korund bereits als nachteilig erwiesen, weshalb diese Umstellung auch beim Stahlen kritisch hinterfragt wird. Daher wurden Probeschweißungen bei der Firma Modersohn hergestellt und mit verschiedenen Oberflächenbearbeitungsmethoden (Glasperlenstrahlen, Korundstrahlen, Beizen, Elektropolieren, Schleifen) nachbehandelt. Diese verschiedenen Oberflächenzustände wurden analytisch (REM, Rauheit) charakterisiert und hinsichtlich ihrer Lochkorrosionsbeständigkeit vergleichend untersucht werden, um die Eignung des Strahlens mit Korund zu beurteilen.
Einfluss des Schwefelgehalts auf die Korrosionsbeständigkeit des nichtrostenden Stahls 1.4404
(2016)
Die Korrosionsbeständigkeit nichtrostender Stähle wird maßgeblich von ihrer chemischen Zusammensetzung bestimmt. Der tendenzielle Einfluss ist für die Hauptlegierungselemente in der wissenschaftlichen Fachliteratur beschrieben. Bei Begleitelement Schwefel gibt es dagegen keine konkreten Untersuchungen die belegen, ab welchem Gehalt mit einer Verringerung der Korrosionsbeständigkeit zu rechnen ist. Im Lichtbogenschmelzofen wurden verschiedene Legierungen mit abgestuftem Schwefelgehalten hergestellt, um den Einfluss dieses Begleitelementes auf die Korrosionsbeständigkeit systematisch zu untersuchen. Die KorroPad-Prüfung und die Bestimmung kritischer Lochkorrosionspotentiale wurden zur Charakterisierung der Legierungen genutzt. Beide Methoden belegen eine zunehmende Verringerung der Lochkorrosionsbeständigkeit mit dem Schwefelgehalt.
The corrosion resistance of martensitic stainless steels (MSS) depends strongly on the chemical composition and the applied heat treatment. Both determines the distribution of the alloying elements in the microstructure and the resulting material properties. The addition of nitrogen is known to be beneficial for the pitting corrosion resistance of stainless steels. In case of MSS this effect is not only connected to nitrogen itself because nitrogen can be used to substitute carbon which also influences the result of the heat treatment process. This paper shows the effect of nitrogen on the corrosion resistance in relation to the hardening process of MSS. Therefore the effects of austenitization duration, austenitization temperature and cooling rate on microstructure, hardness and corrosion resistance were studied on the MSS X30CrMoN15 1 and X50CrMoV15. The effect of different cooling rates was studied in the range of > 100 K/s down to 1 K/s using the jominy end quench test. The changes in corrosion resistance were detected with electrochemical potentiodynamic reactivation (EPR) and by the determination of critical pitting potentials. Besides this experimental approach thermodynamic calculations with the software thermocalc will be presented and used for the interpretation of the effect of nitrogen on the corrosion resistance of MSS.
Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt.
Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt.
Die Korrosionsbeständigkeit martensitischer nichtrostender Stähle (MNS) wird wesentlich von der chemischen Zusammensetzung und dem Wärmebehandlungszustand beeinflusst. Beides bestimmt die Verteilung der Legierungselemente im Gefüge und die daraus resultierenden Werkstoffeigenschaften. Das Legieren mit Stickstoff bewirkt im Allgemeinen eine Verbesserung der Lochkorrosionsbeständigkeit von nichtrostenden Stählen. Bei martensitischen nichtrostenden Stählen ist dieser Effekt nicht nur auf den Stickstoffgehalt selbst zurückzuführen, sondern auch auf den gleichzeitig verringerten Kohlenstoffgehalt, der ebenfalls das Ergebnis der Wärmebehandlung beeinflusst. In dieser Arbeit wird der Einfluss von Stickstoff auf die Korrosionsbeständigkeit in Bezug zum Härtungsprozess von MNS dargestellt. Dazu wird vergleichend der Effekt von Austenitisierungsdauer, -temperatur und Abkühlgeschwindigkeit auf Gefüge, Härte und Korrosionsbeständigkeit der MNS X50CrMoV15 und X30CrMoN15 1 untersucht. Die Abkühlgeschwindigkeit wurde mit dem Stirnabschreckversuch gezielt variiert, um den Einfluss von Abkühlgeschwindigkeiten von > 100 K/s bis 1 K/s zu charakterisieren. Die Veränderungen der Korrosionsbeständigkeit werden durch die elektrochemisch potentiodynamische Reaktivierung (EPR) und durch die Bestimmung kritischer Lochkorrosionspotentiale dokumentiert. Neben diesem experimentellen Ansatz werden auch die Ergebnisse von thermodynamischen Berechnungen mit der Software Thermocalc vorgestellt und abschließend auch zur Interpretation des Einflusses von Stickstoff auf die Korrosionsbeständigkeit martensitischer nichtrostender Stähle genutzt.
The novel heat treatment concept of “Quenching and Partitioning” (Q&P) enables producing low alloyed martensitic steels with high strength and formability. Therefore austenite, retaining from a quenching temperature between Mf and Ms, is stabilised by carbon diffusion. This stabilised austenite transforms in martensite (TRIP effect) under mechanical loading. Current investigations on the Q&P heat treatment of martensitic stainless steels reveal a further enhancement of mechanical properties due to higher amounts of austenite. Thus a tensile strength of 1.800 MPa and a maximum elongation of 20 % are possible, while mechanical properties under compression are much higher due to a distinct SD effect.
The presentation aims to gain a further understanding of the Q&P heat treatment and the resulting mechanical properties for the steel X46Cr13, especially the mechanical behaviour under dynamic mechanical loading condition. Results of drop work and Split Hopkinson Pressure Bar test confirms the findings of quasi static compression test. Furthermore, Charpy impact tests show higher impact toughness compared to the common heat treatment of quenching and tempering (Q&T). Complementary investigations indicate a higher corrosion resistance of Q&P compared to Q&T.