The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.
The damage process of short glass fibre (30% weight) reinforced polyamide caused by mechanical loading was investigated from the beginning on micro cracking level to the incipient crack of mm-dimension. Based on high resolution computer tomography and the X-ray-refraction technique the inner surface due to micro-cracking at the short fibre ends and the fibre matrix debonding of the skin surface of the filament was determined quantitatively. With the knowledge of the fatigue crack propagation rate and fracture toughness of the material from former research projects, it was derived that the total inner surface due to micro cracks measured by X-ray refraction is much higher than the specimen could have withstand the load, supposed the surface is in a localized crack. Hence, the damage process could be described from micro to macro level. Accompanying fractographic investigations endorse the modelling based on the NDT-techniques.
Concrete of today has only little in common with the traditional concrete used a few decades ago. It has become a high performance material, which can be adjusted for high performance applications and according to ultimate user specifications. The reason for the rapid evolvement was the increasing awareness about how the rheology of concrete can be improved without negatively affecting the mechanical properties of concrete by chemical admixtures.
The stress vs. strain curve of materials is affected the rate of imposed straining. Among the methods for dynamic testing the technique known as 'split Hopkinson pressure bar' (SHPB) has evolved into the most widely used one to exert high-speed straining. The theory behind it comprises simple equations to compute stress and strain. The reliability of the strain analysis can be assessed by digital image correlation (DIC). The present results indicate that the visually observed strain is smaller than predicted by theory.
Build-up strategies for generating components of cylindrical shape with laser metal deposition
(2015)
Laser Metal Deposition LMD) as additive manufacturing process offers the potential to produce near net shape components. This reduces the amount of material and post-processing. The components are composed of individual layers. Already mall irregularities within a layer can add up over multiple layers and lead to error propagation. This paper deals with the issue of build-up strategies to minimize irregularities and prevent error propagation. Different travel paths and the influence of a changing starting point regarding to error propagation are discussed. Different deposition rates between core and peripheral area are detected and successfully compensated by adjusting the build-up sequence. Stainless steel and titanium alloy Ti-6Al-4V are used in the experiments. The results are intended to illustrate the potential of an adjusted build-up strategy and provide basic information on the way to an automated deposition process. This paper is of interest for engineers in industry or science using LMD as additive manufacturing process.
In the past few years, the share of earthen building materials used in constructions in Central Europe has increased. That is due to growing acknowledgement of its qualities regarding balancing of humidity, absorption of odours and acoustical insulation.
To regulate these (mostly indoor) uses, the German Institute for Standardization (DIN) has published norms for adobe, earth mortar for masonry and earth plaster. In addition to these traditional building materials, earthen panels have been developed. As an ecological alternative to gypsum plaster boards, they combine climatic advantages of traditional materials with economic advantages of industrial processing, i.e. prefabrication and drywall techniques. Earthen panels are a composite layered material, comparable to Textile Reinforced Concrete (TRC). Most products contain an inner layer of reed tubes which improve the tensile strength and reduce the weight. Often, one or both surfaces are reinforced with a fibrous net to prevent cracks in the plastering that is usually applied on top. Additives range from straw to expanded clay. Special panels contain waxes that improve their heat storage capacity or water pipes to allow the usage as flat heating and cooling systems.
The numerical simulations of high power laser keyhole welding at different welding positions are performed by using Volume-Of-Fluid (VOF) method. The main material is SS400. The multi-physics phenomenon is considered using several models, such as the heat flux of Gaussian heat source, the recoil pressure with Clausisus-Clapeyron equation, the Marangoni flow considering temperature gradient, the buoyancy force with Boussinesq approximation, the additional shear stress and heat source due to metallic vapor ejected through keyhole entrance, the bubble formation assumed as adiabatic bubble, and the multiple-reflection by solving proper discriminant, are used. To analyze the fluid flow pattern, the concept of streamline formed by reconstructing the value of the velocity vector is applied.
Partial and full penetration cases at different welding positions are considered. The welding position seems to have only a minor influence on bead formation characteristics in both cases. This is probably due to the fact that the recoil pressure has a major influence when compared to other driving forces. The flow characteristics and fluid velocity in weld pool are analyzed to compare the gravity direction effect at different welding positions. It is observed that the clockwise flow pattern is mainly formed by the recoil pressure on the keyhole surface in the case of partial penetration. The laser energy can't maintain the whole weld pool when the weld pool size becomes too large. And then the solidification starts from the middle part of weld pool and a necked weld pool shape is formed. In the full penetration welding, the weld pool flow patterns are affected by the leakage of laser power through the full penetration keyhole and also by surface tension. Furthermore, the numerical simulation of full penetration welding with AISI316L is also performed to analyze the effect of material properties. The weld bead shapes obtained by simulations were compared with the corresponding experimental results to confirm the validity of the process models adopted and the CFD simulation tool.
Structuring of LTCC substrates by a combination of pressure-assisted sintering and hot-embossing
(2015)
A novel technology for the structuring of LTCC surfaces is introduced. The material is shaped in a zero-shrinkage process by embossing a glassy carbon mold into the softened LTCC directly after termination of the shrinkage. Three commercially available LTCC compositions (Ceramtape GC, Heratape CT707, and DP951) were tested. Diverse raised and lowered structures including rings, grids, and characters were fabricated. Different material behavior was observed for the tested compositions. Promising results were achieved with Ceramtape GC. Embossing of precise, 40 µm deep circular cavities and 50 µm high raised characters is demonstrated. Processing of 100 × 100 mm² substrates is possible. DP951 showed very good moldability, but also unwanted material displacement due to evaporating lead. A high displacement capacity but uneven heights of embossed structures were observed on CT707 samples. SEM investigations proved the precise transfer of surface contours from the mold to the LTCC. Thereby, the high potential of the hot-embossing process for micro-patterning of LTCC is illustrated.
From the last decades the earth construction has a growing interest due to the high sustainability (low C02 emissions), thermal and acoustic performance, fire resistance and cost of the raw material (soil). In fact, earth construction can constitute a feasible solution for a more sustainable construction industry in developed countries. Nowadays the research areas on earthen construction focus from one side on the improvement of the materials for new buildings, on the other side on the Conservation of existing architectural heritage.
Historical earthen buildings are often damaged by static or dynamic loads in form of extensive cracking. All too often these cracks are insufficiently or inappropriately repaired, if at all, because of lack of knowledge and/or technology. In particular, the behaviour of crack repair by grouting poses a challenge in earthen materials and demands specific requirements for the grouting mortar, such as low water content, good water retention, low shrinkage, etc. Cracks in earthen construction can be repaired by grouting to re-establish structural continuity, and can also be used to consolidate voids and gaps, or as a complement to other strengthening techniques such as the introduction of tie-rods.
In the framework of earthen materials for new constructions, the major drawback is that traditional earthen materials are typically considered as non-standard. The great variability and heterogeneity of the properties of the available soils, the lack of quality control in the manufacturing of the earthen materials and in the construction process can be pointed out as the main reasons behind this Situation. Furthermore, only few countries issued Standards and recommendations supporting earth construction, discouraging the design of earth construction by the technical community in countries where these documents are absent.
For the design of laminates the knowledge of the failure behaviour of plies under multiaxial stresses is a necessary precondition. The strength of plies under multiaxial stresses commonly is determined by standard off-axis tests using fixed clamps. By varying the off axis angle the ratio of shear to normal stresses can be prescribed. However, by preventing the rotation a complex stress field develops which strongly varies with the off axis angle as well. While these effects are not crucial when determining the elastic material parameters since the stress state in the center of the specimen is not far from the ideal uniaxial stress state they have a great influence on the failure behaviour.