Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (44) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (44)
Sprache
- Englisch (44)
Referierte Publikation
- ja (44) (entfernen)
Schlagworte
- Corrosion (3)
- Crystallization (3)
- Bioactive glass (2)
- Carbon steel (2)
- Condensate (2)
- Degradation (2)
- Fatigue (2)
- Impurities (2)
- NMR spectroscopy (2)
- Oxidation (2)
Organisationseinheit der BAM
- 5 Werkstofftechnik (44) (entfernen)
Carbidic Austempered Ductile Iron (CADI) microstructures containing eutectic carbides can be produced by the addition of carbide stabilizing elements, such as chromium. Carbides formed from the addition of Cr are eutectic of M3C type. The presence of such hard phases can enhance the abrasion wear resistance of ductile iron. A new CADI can be produced by the addition of Nb. Niobium carbide particles are formed in the beginning of solidification and remain stable once they are insoluble in solid iron matrix. The dry sand abrasive wear resistance of ductile irons alloyed with 1.0, 1.8, and 2.4 wt% Nb were tested in both “as-cast” and “heat treated” conditions using standard ASTM G65. Results were compared to abrasive wear data obtained on ductile iron alloyed with 1 wt% Cr, CADI (1 wt% Cr), and the basic composition of iron without carbide stabilizing elements. In the “ascast” condition, the addition of Nb did not lead to a reduction in wear, while CADI with Nb is a promising substitute for CADI with Cr addition, because both materials showed very similar values of abrasion resistance.
Micro-ploughing and micro-cutting mechanisms were observed on the worn surfaces of ductile irons. Abrasive wear resistance of these alloys was correlated with the volume fraction of carbides.
Due to the stochastic nature of crack nucleation by Vickers indentation, a statistical analysis of propagation rates of 185 radial cracks was performed. Crack growth was observed directly using a video camera with high Image acquisition rate. It is found that propagation rates are controlled by the environmental reactions at the crack-tip shortly after their initiation (< 1 s). Calibration of the stress intensity KI showed that the residual stress factor χ and the exponent n of the equation KI==χPc−n (with P==load and c==crack length) are broadly distributed among the 185 analyzed cracks, ranging from 10−16 to 104 and from 0.1 to 5, respectively. For the most frequent crack, the equation KI==0.052Pc−1.47 holds. The results show that correlations of indentation-induced crack length to stress intensity necessitate the use of statistical significant data that are calibrated by the environmental reactions at the crack-tip.
Hydrogen gas diffusivity of fourteen glasses of the Na2O-Al2O3-SiO2 system are studied along the joins quartzalbite-jadeite-nepheline (Qz-Ab-Jd-Np, fully polymerized) and albite-sodium disilicate (Ab-Ds, depolymerized).
Density measurements show that ionic porosity decreases from 54.4% (Qz) to 51.5% (Np) and from 52.4% (Ab) to 50.2% (Ds). Hydrogen diffusivity D follows similar trends but at another scale. D at 523 K decreases from 4×10−12 to 3×10−14m2 s−1 (Qz-Np) and from 4×10−13 to 3×10−15m2 s−1 (Ab-Ds). Charge compensating Na+ acting as a filling agent in fully polymerized network structures leads to up to one order of Magnitude higher diffusivities as depolymerized glass structures of the same SiO2 content where Na+ takes the role of a
modifier ion. Temperature dependence of the diffusivity indicates that both the activation energy involved with the moving H2 molecule as well as the accessible volume in the structure contribute to this compositional trend.
Roaldite – Fe4N – has been identified in the São Julião de Moreira iron meteorite using electron backscatter diffraction (EBSD) and simultaneously acquired energy-dispersive x-ray spectroscopy (EDS). Mean-periodic-number images derived from raw EBSD patterns confirm this phase by an even higher spatial resolution compared to EDS.
Roaldite appears in the form of systematically and repetitively aligned plates. Despite the locally heavy plastic deformation, it is shown that the origin of the oriented precipitation of roaldite is linked to the orientation of the kamacite matrix. Roaldite can be considered to be precipitated from kamacite using an inverse Kurdjumov-Sachs (K-S) or Nishiyama-Wassermann (N-W) orientation relationship. A more accurate discrimination is impossible due to the accumulated shock deformation, which blurs the local reference orientation of kamacite. The habit plane of roaldite is found to be {112}R, which is most likely parallel to {120}K of kamacite. Some of the roaldite plates contain two orientation variants which repeatedly alternate. Their misorientation angle is about 12°.
An effective method for evaluating the fatigue strength of thick unidirectional composite laminates of wing spar caps has been presented here. A typical width-tapered bending specimen has been developed for a four-point loading set up. Static and fatigue loading was performed at a load ratio R = -1. The complex stress state has been investigated numerically by finite element analysis. Finally, the concept is proven experimentally on specimens made of pultruded fibre rods.
The fatigue behavior of the continuously tapered width by water Jet cutting has been compared to discrete tapering via rod-drop. The new method enables a screening of material fatigue behavior caused by normal and shear loading.
Friction stir welding (FSW) of high-melting temperature alloys, such as steel and Inconel, requires tooling that can survive under the applied loads at the elevated temperatures. Tungsten-Rhenium (W-Re) alloys are a suitable candidate for this application; however, the costs typically associated with achieving the required densities and grain structure for the tooling are high due to the lengthy traditional processing required. Further costs are incurred in machining the starting bar stock to the final FSW tooling configuration. An alternate processing method is used in this study to shorten the fabrication time using direct current sintering which rapidly consolidates the starting powders at lower temperatures than used in traditional powder metallurgy. Although this process enables retention of the fine grain size, the sintering time is too short to form the desired single, solid phase. Therefore, the specimens were subjected to a post-consolidation heat treatment to fully solutionize the W matrix. Once the desired density and solid solution phase was verified in coupons, the final processing parameters were used to consolidate a net shape tool for FSW.
Chemically modified bioactive glasses based on ICIE16 were prepared with the melt-quenching method using water as a quenching medium. The sinterability of these bioactive glasses was investigated and is discussed in this article. The sintering experiments were conducted with different sintering temperatures, sintering times and heating rates. Those parameters are crucial for dense glass with an amorphous structure. The particle size (d50) of the starting glass powder was determined at 88 μm and kept constant. The pre-pressed glass pellets were cold-isostatically pressed at 300 MPa to a green density of around 63 %. Density development, phase identification, shrinkage behavior and the microstructure were investigated to determine the sinterability of the developed glasses. The glass powders were sintered at different temperatures inside the processing window while crystallization was monitored. The results have shown that the sinterability of the developed glasses strongly dependsonthe proposed chemical additions. The highest density reached was 96 %, which belongs to BP1 glass with sintering conditions of 20 K/min heating rate for 60 min at 750 °C.
An investigation of the two-component phase diagram of the CaNaPO4- CaKPO4system performed using various analysis techniques is reported. The continuous solid solution series of α-CaMPO4 existing above 700 °C undergoes eutectoid decomposition during cooling to β-CaMPO4-based solid solutions enriched with Na and K, and to an intermediate nonstoichiometric compound with an ideal composition of CaK0.6Na0.4PO4. All three compounds exhibit significant volumetric effects associated with first-order phase transitions, with positive volume changes under cooling for the intermediate compound. Increased K content in ceramics based on CaKyNa1-yPO4 compositions enhances the strength properties of those ceramics, including their fracture toughness, which is associated with increased density. Increased K content also has a smaller effect of inducing phase transformations accompanied by strong volume changes.
The crystallization behavior of sodium ion conductive Na2MnP2O7 glass was examined to clarify the crystallization mechanism. The formation of thermodynamically metastable phase, layered Na2MnP2O7, at the surface of the glass occurred. Heat treatment at 430 °C for 3 h lead to surface crystals of Na2MnP2O7 oriented with the (101) direction perpendicular to the sample surface. As the heat treatment temperature increased, the glass-ceramic samples deformed, and the presence numerous micro bubbles due to dissolved water was detected.