A composite material is a combination of two or more materials with very different mechanical, thermal and electrical properties. The various forms of composite materials, due to their high material properties, are widely used as structural materials in the aviation, space, marine, automobile, and sports industries. However, some defects like voids, delamination, or inhomogeneous fiber distribution that form during the fabricating processes of composites can seriously affect the mechanical properties of the composite material. In this study, several imaging NDE techniques such as: thermography, high frequency eddy current, ultrasonic, x-ray radiography, x-ray laminography, and high resolution x-ray CT were conducted to characterize the microstructure of carbon fiber composites. Then, a 3D analysis was implemented by the destructive technique of serial sectioning for the same sample tested by the NDE methods. To better analyze the results of this work and extract a clear volume image for all features and defects contained in the composite material, an intensive comparison was conducted among hundreds of 3D-NDE and multi serial sections’ scan images showing the microstructure variation.
Fast digital radiography was used to observe the crack development during single pass bead-on-plate gas tungsten arc welding with a minifocus X-ray source and a digital detector array with 75-micrometer pixel size. The sample material were 5 mm thick AlMgSi plates. An acquisition rate of 12 frames per second and an exposure time of 40 ms per frame were used for real-time observation of the hot crack propagation during welding. The basic spatial resolution of the images is about 80 µm. A 3D laminographic reconstruction of the acquired 2D radiographic images gives access to the volumetric extent of the cracks in the welded sample. The parallel use of a high-speed camera during welding allows the real-time inspection of surface cracks. The development of surface cracks was compared with the crack’s distribution in the sample volume and these results were correlated to the used welding parameters.