During Rutherford cable production the wires are plastically deformed and their initially round shape is distorted. Using X-ray absorption tomography we have determined the 3D shape of an unreacted Nb3Sn 11 T dipole Rutherford cable, and of a reacted and impregnated Nb3Sn cable double stack. State-of-theart image processing was applied to correct for tomographic artefacts caused by the large cable aspect ratio, for the segmentation of the individual wires and subelement bundles inside the wires, and for the calculation of the wire cross sectional area and shape variations. The 11 T dipole cable cross section oscillates by 2% with a frequency of 1.24 mm (1/80 of the transposition pitch length of the 40 wire cable). A comparatively stronger cross sectional area variation is observed in the individual wires at the thin edge of the keystoned cable where the wire aspect ratio is largest.
In the framework of the development of high field magnets made of Nb3Sn superconductor for projects like HL-LHC and FCC studies, it is needed to refine the understanding of the coil winding process and its impact on the overall mechanical behavior of the conductor. For this purpose, a new cable winding setup has been developed in order to compare the windability of different Nb3Sn Rutherford cables. In addition, various geometrical cable inspection methods were tested and compared. First experimental results obtained with the new set-up for winding tests are summarized.