Geosynthetic materials are applied in measures for coastal protection. Weathering or any damage of constructions, as shown by a field study in Kaliningrad Oblast (Russia), could lead to the littering of the beach or the sea (marine littering) and the discharge of possibly harmful additives into the marine environment. The ageing behavior of a widely used geotextile made of polypropylene was studied by artificial accelerated ageing in water-filled autoclaves at temperatures of 30 to 80° C
and pressures of 10 to 50 bar. Tensile strength tests were used to evaluate the progress of ageing, concluding that temperature rather than pressure was the main factor influencing the ageing of geotextiles. Using a modified Arrhenius equation, it was possible to calculate the half-life for the loss of 50% of the strain, which corresponds to approximately 330 years.
2021 marks the 10th anniversary of the first ERA.Net RUS joint call for European-Russian STI cooperation projects. Pooling the resources of more than 20 European and Russian funding agencies, more than 150 projects were funded with an estimated budget of about € 60 million.
Being even larger than many thematic ERA.NETs, the ERA.Net RUS Plus has been the biggest and most successful regional ERA.NET so far. Indicating a strong demand for scientific cooperation, the smaller-scale projects funded within the ERA.Net RUS (Plus) calls perfectly complement Russian participation in the EU Framework Programmes.
Not least of all, the ERA-Net RUS calls are examples of successful collaboration at a time when cooperation in other fields is complicated by the politically challenging situation. These calls contributed to keeping the communication channels open.
Against this background a dedicated event in late 2021 highlighted what has been achieved within the first decade of the initiative. The project EI-GEO coordinated by BAM was selected as best practice project. The presentation displays the main results of the project and discusses the key success factors.
Geosynthetics are widely used in hydraulic engineering and within coastal protection constructions at the Baltic Sea shore, such as walls, promenades, and gabions walls. Storms influence leads to deformation of some of the protection structures and cause the release of geotextiles onto the beach. Fragments of geotextile migrate along the shore, experiencing additional degradation and destruction down to macro-, meso-, and micro-particles. During October 2017 - March 2018, the Baltic Sea shore along the Sambia Peninsula (Kaliningrad Oblast of the Russian Federation) was monitored to establish the contamination of sandy beaches by geotextiles that had degraded. Several local sources of pollution of beaches by geosynthetic materials were established.
Testing of the oxidative resistance of polyolefin based geosynthetics in
autoclaves at high oxygen pressure has been suggested as an alternative method to
conventional forced-air oven aging. The intention is to shorten considerably the testing
time and to ensure that aging is performed under the condition of rate-controlled
and not diffusion-limited oxidation. We compare data from high pressure autoclave
tests (HPAT) with data from oven aging and water immersion tests at 80 °C. For this,
the stabilization of the samples has to be taken into account. Polyolefin based geosynthetics
are usually stabilized by two types of “packages” of antioxidants (AO), designated
here as P1 and P2. P1 consists of phenols and phosphites, P2 of hindered amine
stabilizers (HAS) in addition to a marginal stabilization P1 of the resin for the manufacturing
process. Phenolic and phosphite AO are quickly consumed in the HPAT.
Failure time is tremendously reduced compared to forced-air oven aging or water
immersion. The results are discussed within the framework of a basic autoxidation
scheme (Wise et al., 1997). The reduction is much greater than expected from theoretical
considerations. Therefore, a direct and degrading reaction of oxygen with the AO
has to be assumed. In case of HAS, the time dependence of the degradation of tensile
properties in the HPAT is significantly different from the dependence observed in
conventional forced-air oven aging and their effectiveness is likewise strongly reduced.
A conclusive interpretation of HPAT results needs a better understanding of
what happens to the AO at high oxygen pressure.
Plastic products used in geotechnical engineering, so-called geosynthetics, are often made of polyolefins (polyethylene or polypropylene) and stabilized against oxidative degradation by antioxidants (AO). Three types of AO “packages” are used: (P1) phenols and phosphites/sulfides, (P2) hindered amines (HAS) with a marginal stabilization P1 of the basic resin, (P3) a combination of packages P1 and P2 with comparable amounts of phenol and HAS. We report about long-lasting oven aging and water immersion tests at 80 °C of 29 different polyolefin based products (geomembranes, geonets and geotextiles). Pronounced differences in the degradation behavior were found depending solely on the type of AO package. In case of P1, the oxidative degradation is prevented by the AO. Autocatalytic oxidation only begins after depletion of AO and may lead to catastrophic failure depending on the environmental conditions. In case of P2, degradation starts right from the beginning. However, it is decelerated and proceeds gradually. In case of P3, the degradation behavior seems to be a superposition of the characteristics obtained for P1 and P2. Plotting the fractional loss of the AO in P1 and P2 as function of the square root of aging time, we identified two regimes of AO depletion. We suggest to attribute this observation to the different mechanisms of AO depletion.