Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
Sprache
- Englisch (5)
Referierte Publikation
- nein (5)
Schlagworte
- Acoustic emission (5) (entfernen)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (4)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (4)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 5 Werkstofftechnik (1)
- 5.0 Abteilungsleitung und andere (1)
- 7 Bauwerkssicherheit (1)
- 7.1 Baustoffe (1)
- 7.4 Baustofftechnologie (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
Typically, the near-eutectic Al-Si alloys consist of highly interconnected three-dimensional network of the eutectic Silicon (Si) and intermetallics embedded into Aluminium (Al) matrix. For further improvement of the mechanical properties of such alloys, often, one single ceramic reinforcement phase, e.g. silicon carbide (SiC) or aluminium oxide (Al2O3) in the form of fibres or particles is added. However, hybrid reinforcements (fibres and particles) can further improve wear resistance and fracture toughness, and additionally, reduce anisotropy of the material. The engineering of metal matrix composites (MMC) for specific application requirements benefits from a comprehensive knowledge of the failure behaviour. Therefore, damage evolution under compression was investigated on:
- pure near-eutectic AlSi12CuMgNi matrix alloy
- type I: matrix reinforced with random-planar oriented Al2O3 short fibres (15 vol.%)
- type II: matrix reinforced with random-planar oriented Al2O3 short fibres (7 vol.%) and additional SiC particles (15 vol.%)
The analysis of damage mechanism was carried out in two rather independent but complementary studies. First, selected sister samples of every material were exposed to quasi-static compression (traverse control). The compression tests were interrupted at different strain levels. Miniature cylinders with a diameter of 1mm were extracted from the pre-strained samples and investigated by synchrotron computed tomography (SX-µCT) with a spatial resolution of about 0.7 µm. For the pure matrix alloy, microcracks are confined to the intermetallic particles and to the eutectic Si, hence no damage was observed in the Aluminium. The composite type II revealed a more effective strain accumulation (less damage) than type I at low plastic strain (up to 5 %), but a more catastrophic damage development due to cracking of the SiC clusters at higher strain levels.
The second approach to study the damage initiation and accumulation in the materials subjected to compressive load was Acoustic Emission (AE) analysis. In this case the in-situ monitoring of the acoustic emission signal was performed during compression tests on specimens with dimension of several mm. For all three material types, AE activity set at 2% strain. Differences in AE behaviour of the three materials was proven based on AE hitrate, signal peak amplitudes as well as weighted peak frequencies (WPF). Future work focuses on combination of AE and SX-µCT aiming for more detailed knowledge on damage mechanism of metal matrix composites.
To better understanding the failure of adhesive joints tensile tests were carried out on miniature test specimens from Norway spruce in the synchrotron. Urea-formaldehyde resin was used as adhesive. e. For comparison purposes, tensile tests were carried out on solid wood and on bonded miniature tensile shear samples with acoustic emission. The acoustic emission signals of all the experiments occurred with classified pattern recognition. This resulted in two classes of signals for each two frequency peaks. One class consisted of the low-frequency and the other of the higher-frequency peak of higher intensity, but this was essentially independent from the structure (solid wood or plywood) and size scale of the test specimens. The influence of the adhesive layers was determined on wood test specimens on laboratory scale and on miniature test specimens with an adhesive layer and selected fiber orientations. This gave evidence that the sound emission signals from the failure of the adhesive layer presumably of the class with low frequency signals peak in the range of services can be assigned.
For a better understanding of the damage of glued wood tensile tests on miniature specimens made of glued spruce wood with acoustic emission and in-situ synchrotron-based X-ray computer microtomography has been monitored. As adhesive, urea-formaldehyde resin was used. For comparison purposes, tensile tests were carried out on solid wood and bonded miniature tensile shear samples with acoustic emission. The acoustic emission signals of all experiments were with classified pattern recognition. This resulted in two classes of signals for each two frequency peaks. In one class was the low-frequency, in the other the higher frequency peak of higher intensity, but this essentially independent from the structure (solid wood or plywood) and the size scale of the test specimens. The influence of the adhesive layers was determined on plywood test specimens in laboratory scale and on miniature test specimens with an adhesive layer and selected fiber orientations examined. This gave evidence that the sound emission signals from the failure of the adhesive layer presumably of the class with low frequency signals peak in the range of services can be assigned.
Acoustic emission testing
(2018)