The failure of composites is initiated by imperfections on microscale. The interface between fiber and matrix is a key parameter concerning failure initiation. In order to get an improved understanding of local failure processes a fracture mechanical analysis of interfacial failure in a composite ply under transverse stresses is performed. The mixed mode energy release rate is calculated. In addition the failure of interfaces under cyclic loading is studied on a single fiber model. The quasistatic debonding process is compared with the interfacial failure under fatigue loading. It is shown that the tan delta can be used as an indicator for the damage propagation.
The premise for the development of improved failure criteria for fiber reinforced composites is the understanding of the failure processes on microscale. On microscale the local behaviour of the matrix polymer is crucial. It significantly differs from that found in macroscopic measurements. The present study is focused on the plastic material behaviour of a standard epoxy resin. Local plastic strains are measured in tensile test by using digital image correlation. A multilinear plastic law is implemented by the experimental data. The stress field arising in an idealised representative volume element of a unidirectional ply is analysed by finite element calculations. The change of the stress and strain field due to plastic deformation according to the multilinear plastic law is shown. The change leads to a shift of the critical locations where failure is likely to initiate. In addition, the failure type changes from stress based to strain based failure. The dominant role of the shear strains is shown.