Test procedure to characterize the cracking susceptibility of RSW-steels has been developed
During externally loaded test procedure all investigated steels (HDT780CD+Z100, HDT780C+ZE75/75, HX340LAD+Z100, HCT690TD+Z100) showed a cracking behavior
With increased specimen load, the crack length grows for the micro-alloyed-steel and TRIP-steel
Complex phase steels behavior during test procedure:
Crack length growth with increasing force could not be determined
The cracking susceptibility of electro-galvanized steels is less than hot-dip galvanized steels (in this case)
30