Here, we show that calcium sulfate dihydrate (gypsum) can be directly, rapidly and reversibly converted to calcium sulfate hemihydrate (bassanite) in high salinity solutions (brines). The optimum conditions for the efficient production of bassanite in a short time (<5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the better-known behaviour of the bassanite phase in low-salt environments. In low-salinity aqueous solutions, bassanite is considered to be metastable with respect to gypsum and anhydrite, and therefore gypsum-to-bassanite conversion does not occur in pure water. Interestingly, the high-salinity transformation of gypsum-to-bassanite has been reported by many authors and used in practice for several decades, although its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures was inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline phase for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios.
In this article, a partial selection of experiments on enhancing the impact resistance of structural components with non-metallic, textile-reinforced concrete is discussed. The focus is on the experimental investigations in which the impact resistance of thin, textile-reinforced concrete plates is characterized. The article discusses the materials, fabrics and test setup used. For the experimental work, a drop tower from the Otto Mohr Laboratory, which belongs to the Technische Universtät Dresden, was used. Furthermore, the experimental results are presented and evaluated using different methods. Based on the collected data, a suitable approach to determining the perforation velocity of an impactor through the investigated thin, textile-reinforced concrete plates is shown.
The crystallization of calcium hydroxide (Ca(OH)2, CH, portlandite) is a key process during the early stages of cement hydration. In the present work, we have revisited the formation of this mineral through nucleation and growth from supersaturated aqueous solutions, in the light of the currently emerging picture of multistage “non-classical” crystallization. To that end, we developed a titration-based assay, in which stock solutions of both relevant ions are added simultaneously into a reservoir, where supersaturation increases slowly at constant stoichiometry until nucleation occurs. This procedure allows both pre- and early post-nucleation phenomena to be analyzed quantitatively. Complementarily, the early stages of portlandite mineralization were probed by various advanced characterization techniques, including cryo-transmission electron microscopy (cryo-TEM), in-situ small-angle X-ray scattering (SAXS), pair distribution function (PDF) analysis of high-energy X-ray scattering (HEXS) data, and analytical ultracentrifugation (AUC). The experimental data show that the formation of calcium hydroxide starts with the association of ions into complexes and clusters, which subsequently coalesce to form amorphous nanoparticles – much like what has been observed in the case of calcium carbonate and other prominent minerals. Subsequently, these particles aggregate and build networks, which eventually transform into hexagonal Ca(OH)2 crystals. The presence of a soluble polycarboxylate – as a known inhibitor of portlandite crystallization – does not change the main characteristics of this multistep nucleation pathway, but it proved capable of significantly extending the lifetime of the amorphous intermediate phase and thus delaying the transition to the final crystalline phase. Our observations confirm the notion that “non-classical” crystallization is a much more common phenomenon than initially believed – and that, for minerals forming in aqueous environments, it may actually be the rule rather than the exception.