Welding processes of duplex stainless steels cause an unbalanced austenite (γ)/ferrite (δ) ratio due to high cooling rates and changes in chemical composition. That causes a degradation of mechanical properties and corrosion resistance. In situ monitoring of the weld pool is to be realized with the help of laser-induced breakdown spectroscopy (LIBS). A major advantage of this technique is the highly accurate time and spatially resolved measurement of the chemical composition during welding. Previous research has established that the LIBS method is suitable to detect chemical elements during welding and to show a distribution of selected elements. Chemical composition in the WM and HAZ can now be quantified using calibration curves generated by certified reference materials (CRM). Furthermore, a cooling rate can be plotted against the measured electron temperature.
Hydrogen assisted stress corrosion and cold cracking represent still a major topic regarding the safety of welded steel components against failure in many industrial branches. Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or at cathodic protection. Additionally, understanding and avoidance of hydrogen entry into weld microstructures from gaseous pressurized environments becomes increasingly important for renewable energy components. There are two types of metallurgical mechanisms associated with hydrogen assisted cracking, i.e. the cracking as well as hydrogen transport and trapping mechanisms. For numerical modelling, it has to be considered that both types are not independent of each other, that the mechanisms are not yet completely clarified and that validation of such models strongly depends on implementation of the correct hydrogen related materials properties. However, quite significant achievements have been made in modelling of hydrogen assisted cracking by indirect coupling of thermal, stress-strain as well as hydrogen uptake and diffusion analyses. After a brief introduction into the subject and by revisiting various proposed cracking mechanisms, the present contribution focuses on recent developments of a numerical model based on a comparison of actual hydrogen concentrations and mechanical loads with respective hydrogen dependent material properties as crack initiation and propagation criteria. The basic procedure for numerical simulation of crack initiation and propagation is outlined and it is shown how such numerical simulations can be validated experimentally. Furthermore, it is highlighted how such a procedure has been extended to a comprehensive model for life time prediction of welded steel pipeline components and experimentally verified. Finally, it is outlined how the model can be extended to simulate cracking in heterogeneous steel microstructures on the different scales.