Three binary fcc-structured alloys (fcc–Ir0.50Pt0.50, fcc Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50) were 14 prepared from [Ir(NH3)5Cl][PtCl6], [Ir(NH3)5Cl][PtBr6], [Rh(NH3)5Cl]2[PtCl6]Cl2 and 15 [Rh(NH3)5Cl][PdCl4]·H2O, respectively, as single-source precursors. All alloys were prepared by 16 thermal decomposition in gaseous hydrogen flow below 800 °C. Fcc–Ir0.50Pt0.50 and fcc–Rh0.50Pd0.50 17 correspond to miscibility gaps on binary metallic phase diagrams and can be considered as 18 metastable alloys. Detailed comparison of [Ir(NH3)5Cl][PtCl6] and [Ir(NH3)5Cl][PtBr6] crystal 19 structures suggests that two isoformular salts are not isostructural. In [Ir(NH3)5Cl][PtBr6], specific 20 Br…Br interactions are responsible for crystal structure arrangement. Room temperature 21 compressibility of fcc–Ir0.50Pt0.50, fcc–Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50 has been investigated up to 50 GPa 22 in diamond anvil cells. All investigated fcc-structured binary alloys are stable under compression. 23 Atomic volumes and bulk moduli show good agreement with ideal solutions model. For fcc–24 Ir0.50Pt0.50, V0/Z = 14.597(6) Å3·atom-1, B0 = 321(6) GPa, B0' = 6(1); for fcc–Rh0.66Pt0.33, V0/Z = 14.211(3) 25 Å3·atom-1, B0 =259(1) GPa, B0' = 6.66(9); for fcc–Rh0.50Pd0.50, V0/Z = 14.18(2) Å3·atom-1, B0 =223(4) GPa, 26 B0' = 5.0(3).
A hydrothermal synthesis of ZrW2-xMoxO8 (0 ≤ x ≤ 2) from the corresponding precursors is reported in this paper. High-temperature and high-pressure data are presented for the sample with x = 1.6. An increase in temperature initiates the phase transition from tetragonal precursor to orthorhombic-ZrW2-xMoxO8 (x = 1.6) with the subsequent formation of cubic and trigonal phases. The thermolysis parameter of the disordered cubic ZrW2-xMoxO8 (x = 1.6) phase is 803 K, and the coefficient of thermal expansion is α = -4.6∙10–6 K−1. Data on ZrW2-xMoxO8 (x = 1.6) structure as a function of pressure are obtained for the first time. Pressureinduced changes from cubic to orthorhombic ZrW2-xMoxO8 (x = 1.6) phase at 1.38 GPa are observed. The sample amorphization is irreversible during decompression.
In this paper we report high-pressure synchrotron x-ray powder diffraction data for the cubic ZrWMoO8. For the first time, extensive structural study of ZrWMoO8 solid solution as a function of pressure was performed. This study shows that disordered cubic-ZrWMoO8 (space group Pa) transforms to ordered cubic-ZrWMoO8 (space group P) at low pressure. A further high-pressure influence leads followed by amorphization of the sample at 2.2 GPa. All transformations are irreversible. Our work will have high impact in the design of new composite materials with well-defined thermal expansion, especially for applications under extreme conditions and high mechanic stress.