As subcritical crack growth (SCCG) can reduce tensile strength of glasses by many orders of magnitude, the potential for improvement of fatigue behaviour is most intriguing in developing ultra-strong glasses. An essential bottleneck is the basic understanding of the numerous interplaying pressure-, temperature- and water-affected relaxation phenomena at the crack tip and related toughening strategies. Therefore, the present project aims to advance the basic understanding of structural relaxation effects and local properties caused by increased water concentration and tensile stresses at the crack tip as they are a key for structural toughening designs to develop SCCG-free glasses and glass surfaces.
Our first studies give clear evidence that glass structure and dynamics is strongly modified upon hydration of glasses. These changes are highly related to the nature of network formers but are affected as well by the counter ions (network modifier). Results of the 1st project part suggest that structural relaxation below glass transition temperature, i.e. overlapping of short-range (beta) and long-range (alpha) interactions can contribute to SCCG in water-free environments and that structurally dissolved water in the glasses can have decisive impact on this effect.
In the 2nd project stage specific glasses compositions will be investigated to gain an improved understanding on the relation of sub-Tg relaxation and inert SCCG as well as to shed light to the related effects of dissolved water and its speciation. These glasses cover a broader range of different glass topologies and binding partners, whereby the coupling of alpha and beta relaxations is varied systematically by alkali-, alkaline earth ions and water species concentrations. Preparation of hydrous glasses (up to 8 wt% water) will be performed by high pressure syntheses. Structure will be resolved by NMR, Raman and IR spectroscopy while structural relaxation is accessed in the temperature and frequency domain using dynamic mechanical spectroscopy and ultrasonic damping. We will focus on measurements of inert SCCG (region III) conducting experiments in vacuum and dry gas atmospheres using indentation techniques and stressing of glass specimens in DCB geometry.
Experimental data on SCCG will be provided to SPP groups, which deals with fatigue in metallic glasses and vice versa we will test theoretical predictions of ab-initio simulations of partner within SPP 1594 in order to quantify the effect of water on the crack tip. In summa topological factors controlling the subcritical crack growth with respect to water will be identified from which structural toughening designs for highly fatigue resistant-glasses can be derived.
Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during the sintering, which results in poor mechanical properties and reduced bioactivity. Recently, new bioactive glasses with improved crystallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. The aim of this study was to investigate the sintering and crystallization behavior of these new bioactive glasses.
Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases are detected. The thermal properties of all glasses were studied by DTA measurements, and the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles progressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization of beta-HAp.
Nowadays, the use of bioactive glasses is established for bone regeneration; however glasses are used mostly as powders, granules or in a paste. Sintered scaffolds are not used clinically, because of the in inherent problem of crystallization during the sintering process, resulting in poor mechanical properties and reduced bioactivity. The aim of this study was therefore to design new bioactive glasses, which combine improved processing and sintering with bioactivity.
Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkalioxide ratio was increased, sodiumoxide was partially replaced by potassiumoxide and up to 8 mol% calciumflorid were added, in order to stabilize the glass against crystallization.
The sintering behavior of the new glasses was characterized by heating microscopy and compared to Bioglass® 45S5. The results showed that the new glasses achieved a sintered density of 88-99 % in contrast to only 57-67% for Bioglass® 45S5. In addition FTIR and XRD analyses showed that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases were detected. The thermal properties of all glasses were studied by DTA and DSC measures, and the influence of grain size and heating rate were characterized. These studies showed a shift of start and end temperature of sintering process as well as the final density. The structure of sintered specimens during and after sintering was examined using light and electron microscopy (REM).
Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during sintering. Recently, new bioactive glasses with improved crys-tallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. Whereas Bioglass® 45S5 powder compacts crystallize during sintering, for the new glasses no crystalline phases were detected. Additionally the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles pro-gressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization.
Bioglass® 45S5 is mainly used clinically as powders, granules or pastes instead of sintered compacts. This is due to the inherent problem of crystallization during the sintering, which results in poor mechanical properties and reduced bioactivity. Recently, new bioactive glasses with improved crystallization stability have been developed as promising candidates for manufacturing of sintered powder compacts for bone regeneration, which combine improved sintering behavior with bioactivity. Compared with the well-known Bioglass® 45S5 (SiO2-P2O5-CaO-Na2O) the calcium/alkali oxide ratio was increased, sodium oxide was partially replaced by potassium oxide and up to 3 mol% calcium fluoride were added, in order to stabilize the glass against crystallization. The aim of this study was to investigate the sintering and crystallization behavior of these new bioactive glasses.
Sintering and crystallization were characterized by heating microscopy, XRD, FTIR, SEM, and DTA. The results show that a sintered density of 88-99 % is achieved in contrast to only 57-67% for Bioglass® 45S5. In addition, FTIR and XRD analyses show that Bioglass® 45S5 crystallized during sintering while for the new glasses no crystalline phases are detected. The thermal properties of all glasses were studied by DTA measurements, and the influence of grain size was characterized. These studies showed that full densification can be attained for particle size < 32 µm, whereas coarser particles progressively increase residual porosity. Observed foaming phenomena, are strongly retarded by crystallization of beta-HAp.
An understanding on crystallization behavior and kinetics in glasses is one of the important topics in the glass science and technology. Tsukada et al.1) found an extremely unique and curious phenomenon in the crystallization of multiferroic (ferroelectric and ferroelastic properties) ’-Gd2(MoO4)3 crystals in Gd2O3-MoO3-B2O3 glasses. That is, crystals formed in the crystallization break into small pieces with a triangle prism or pyramidal shape having a length of 50-150 um spontaneously during the crystallization in the inside of an electric furnace, not during the cooling in air after the crystallization. They proposed to call this phenomenon “self-powdering phenomenon”. To the best of our knowledge, such a self-powdering phenomenon has not been observed in the crystallization of any other glasses. To investigate this phenomenon is very important for the glass science and for the preparation of bulk crystallized glasses with ferroelastic crystals. In this work, the preparation of crystallized glasses keeping the original shape is challenged, and the mechanism of self-powdering phenomenon is proposed. Glasses with the compositions of 21Gd2O3-63MoO3-(16-x)B2O3-xTeO2 (mol%) (x=0, 2, 4, 8) such as 21Gd2O3-63MoO3-16B2O3 (GM16B) and 21Gd2O3-63MoO3-8B2O3-8TeO2 (GM8T8B) were prepared using a conventional melt quenching technique. The quenched glasses were heat-treated at some temperatures, and the crystalline phase present in the crystallized samples was identified by X-ray diffraction (XRD) analyses, and the morphology and birefringence of crystals formed were observed using a polarized optical microscope (POM). The densities of GM16B and GM8T8B glasses are 4.76 g/cm3 and 4.91 g/cam3, respectively, and these values are higher than the density of ’-Gd2(MoO4)3 crystal, 4.555 g/cm3. These differences in the density might induce the large stresses in the inside of crystals during the crystal growth. The crystallized glasses of GM16B with ’-Gd2(MoO4)3 crystals do not keep the original glass shape, showing self-powdering phenomenon (breaking into small pieces). However, the crystallized glasses of GM8T8B keep the original glass shape without indicating any self-powdering. It is proposed that the stress at the interface between the glassy phase and ’-Gd2(MoO4)3 crystalline phase might be reduced in GM8T8B glasses containing TeO2 with weak Te-O bonds.
The development of glassy hydrogen barriers requires the determination of low H2 permeabilities. Previous studies and numerical simulations have shown that the VHE powder method (vacuum hot extraction with mass spectrometric gas detection) is suitable for this purpose. The measured isothermal gas emission is fitted to a classical diffusion model for spherical particles from which the diffusion coefficient of the glass is calculated. The H2 permeability is determined by means of the solubility determined from the same measurement data. This presentation is referring to the optimization of the method regarding sample preparation and measurement data evaluation using suitable experimentally determined particle size distributions is reported. For quartz glass, it is shown that the accuracy of classical measuring methods is achieved with the VHE powder method. Furthermore, other examples of substantially gas-tighter glasses are given.
Compared to its intrinsic strength, the practical strength of glasses is substantially
lowered by microscopic flaws. Their sub critical growth from the surface is strongly
affected by ambient humidity.
A new device was designed to enable the observation of sub critical crack growth
(SCCG) in vacuum and controlled atmosphere. It allows measurements in transparent and
semi-transparent materials in double cantilever beam (DCB) geometry. The aim of the
present work is to study the effect of crystals on crack growth.
Solar glass in arid and semi-arid regions is exposed to sand storms which can affect the durability of PV modules. Related erosion processes have been extensively studied but the results given are difficult to compare due to being obtained by different variables like particle speed and sand mass. This study correlates the damage of solar panels to the cumulative impact energy as a global parameter.
Crack healing in glasses
(2017)
Fundamental understanding of crack healing in glassy crystalline materials is very important for many applications, especially for solid oxide fuel cells (SOFC) sealants since cracks caused by mechanical stress or thermal cycling still remain a substantial bottleneck in developing durable SOFC. Previous studies on soda lime silicate glass published by Singh showed that crack healing is driven by viscous flow. There he postulated that the healing progress is proportional to time, t, and the inverse viscosity. This finding would allow to present for a given glass data of crack healing measured at different temperatures in a master curve, if the healing progress is plotted versus t/η. Such master curves would be a helpful tool in understanding crack healing kinetics. To verify the applicability of such master curves, crack healing in non-crystallizing soda-lime-silicate (NCS) and sodium-borosilicate glasses (NBS) was studied. Cracks were generated by Vickers indention and healed isothermally at different temperatures. Crack healing progress was monitored by optical and electron microscopy. The results show that the above mentioned proportionalities applies to the two glasses. In both cases the afore developed master curve could be obtained.