Die im MVT-Test standardmäßig erfasste Gesamtrisslänge erlaubt keine direkten Rückschlüsse auf die Heißrissanfälligkeit des untersuchten Werkstoffs. Der vorliegende Beitrag erläutert, inwiefern aus der Morphologie von Oberflächenrissen an MVT-Proben dennoch auf das Werkstoffverhalten geschlossen werden kann.
The subject of this study is how, and to what extent, Varestraint/Transvarestraint test results are influenced by both testing parameters and characteristics of evaluation methods. Several different high-alloyed martensitic LTT (low Transformation temperature) filler materials, CrNi and CrMn type, were selected for examination due to their rather distinctive solidification cracking behaviour, which aroused interest after previous studies. First, the effects of different process parameter sets on the solidification cracking response were measured using standard approaches. Subsequently, microfocus X-ray computer tomography (μCT) scans were performed on the specimens. The results consistently show sub-surface cracking to significant yet varying extents. Different primary solidification types were found using wavelength dispersive X-ray (WDX) analysis conducted on filler metals with varying Cr/Ni equivalent ratios. This aspect is regarded as the main difference between the CrNiand CrMn-type materials in matters of cracking characteristics. Results show that when it comes to testing of modern highperformance alloys, one set of standard Varestraint testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Für moderne Hochleistungswerkstoffe scheinen Standardparameter der Erstarrungsrissprüfung mittels MVT-Test in vielen Fällen ungeeignet. Dieser Vortrag erläutert die charakteristischen Besonderheiten der betrachteten Werkstoffe, und zeigt überdies alternative Analysemethoden auf, mit denen fehlerhafte Einschätzungen von Erstarrungsrissanfälligkeiten vermieden werden können.
Solidification cracking of metals is a well-researched topic in the field of welding science. A material’s susceptibility to solidification cracking can be tested using numerous different specialized test procedures, one of which is the Modified Varestraint-/Transvarestraint test (MVT). It was developed at BAM in 1982 and is internationally standardised. Over the decades, this test has been extensively used to characterise the solidification cracking resistance of many different materials.
The present study was conducted to further investigate the influences of the standardised MVT testing parameters, as well as the characteristics of evaluation methods on the results. Several different high alloyed martensitic LTT (low transformation temperature) filler materials, CrNi and CrMn type, were used. In previous pilot studies, these alloys have shown a rather distinctive solidification cracking behaviour.
First, the effects of different process parameter sets on the solidification cracking response were measured using the standard approach. Subsequently, μCT scans were performed on the specimens. The results consistently show sub surface cracking, to significant, yet varying extents. Different Primary solidification types were found using WDX-analysis, an aspect that is regarded to be the main difference between the CrNi- and CrMn-type materials and their cracking characteristics.
Results show that when it comes to testing of modern high-performance alloys, one set of standard MVT testing parameters might not be equally suitable for all materials. Also, to properly accommodate different solidification types, sub-surface cracking has to be taken into account.
Ermittlung eines allgemeingültigen Erstarrungsrisskennwerts durch Abstraktion gängiger Heißrisstests
(2017)
Ergebnisse von Untersuchungen zur Heißrissanfälligkeit metallischer Werkstoffe, die aus gängigen Heißrisstests gewonnen wurden, sind i.A. schlecht mit Ergebnissen aus anderen Testverfahren vergleichbar. Darüber hinaus ist die Fehlererkennungsgenauigkeit der etablierten Testverfahren mitunter dürftig. Auch die Übertragbarkeit der rein Werkstoff-orientieren Testergebnisse auf reale Bauteile gestaltet sich schwierig. Insgesamt ist das Phänomen der Heißrissbildung nicht ausreichend erforscht und verstanden, als dass es in Konstruktion und/oder Bauteilfertigung vorhergesagt werden könnte.
Die vorliegende Arbeit befasst sich mit der Abstraktion gängiger Testverfahren, um verfahrensspezifische Einflüsse möglichst zu eliminieren, sodass eine universellere Beurteilung von Werkstoffen vorgenommen werden kann. Die gewonnenen Ergebnisse können so besser für Simulationen bzw. Vorhersagen der Heißrissanfälligkeit realer Bauteile herangezogen werden.