X-ray refraction is analogous to visible light deflection by matter; it occurs at boundaries between different media. The main difference between visible light and X-rays is that in the latter case deflection angles are very small, from a few seconds to a few minutes of arc (i.e., the refraction index n is near to 1). Importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks and quantify their densities in bulk (not too heavy) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, they can detect objects with size above a few wavelengths of the radiation.
Such techniques, especially at the Synchrotron BESSY II, Berlin, Germany, can be used in-situ, i.e. when the specimen is subjected to temperatures or external loads.
The use of X-ray refraction analysis yields quantitative information, which can be directly input in kinetics, mechanical and damage models.
We hereby show the application of non-destructive X-ray refraction radiography (SXRR, 2D mapping also called topography) to problems in additive manufacturing:
1) Porosity analysis in PBF-LM-Ti64. Through the use of SXRR, we could not only map the (very sparse) porosity distribution between the layers and quantify it, but also classify, and thereby separate, the filled porosity (unmolten powder) from the keyhole and gas pores (Figure 1).
2) In-situ heat treatment of laser powder bed fusion PBF-LM-AlSi10Mg to monitor microstructure and porosity evolution as a function of temperature (Figure 2). By means of SXRR we indirectly observed the initial eutectic Si network break down into larger particles as a function of increasing temperature. We also could detect the thermally induced porosity (TIP). Such changes in the Si-phase morphology upon heating is currently only possible using scanning electron microscopy, but with a much smaller field-of-view. SXRR also allows observing the growth of some individual pores, usually studied via X-ray computed tomography, but again on much smaller fields-of-view.
Our results show the great potential of in-situ SXRR as a tool to gain in-depth knowledge of the defect distribution and the susceptibility of any material to thermally induced damage and/or microstructure evolution over statistically relevant volumes.
To see and not to see - Möglichkeiten und Grenzen der Schadensanalyse mit CT an Kompositmaterialien
(2020)
Anhand von drei Beispielen (Datenfusion an CFK; Machine Learning an Metall-Matrix-Kompositen sowie Refraktion an CFK) wird gezeigt, wie die BAM mit neuen Analysemethoden mehr Informationen aus CT-Datensätzen extrahieren kann, sowie mit der Refraktion eine Analysemethode besitzt, die in Fällen eingesetzt werden kann, bei denen klassische Durchstrahlungsmethoden kein Ergebnis liefern.
An unusual microstructure, inherent residual stresses and void formation are the three key aspects to control when assessing metallic parts made by LPBF. This talk explains an experiment to unravel the interlinked influence of the two mechanisms for the formation of residual stresses in LPBF: the temperature gradient mechanism and constricted solidification shrinkage. The impact of each mechanism on the shape and magnitudes of the residual stress distribution is described. Combined results from neutron diffraction, X-ray diffraction, computed tomography and in-situ thermography are presented.
Also, influence of scan strategies as well as surface roughness of subjacent layers on void formation is shown. Results from computed tomography and in-situ thermography of a specimen dedicated to study the interaction of the melt pool with layers of powder underneath the currently illuminated surface are presented.
Synchrotron X-ray diffraction is a powerful non-destructive technique for the analysis of the material stress-state. High cooling rates and heterogeneous temperature distributions during additive manufacturing lead to high residual stresses. These high residual stresses play a crucial role in the ability to achieve complex geometries with accuracy since they can promote distortion of parts during manufacturing. Furthermore, residual stresses are critical for the mechanical performance of parts in terms of durability and safety.
In the present study, Ti-6Al-4V bridge-like specimens were manufactured additively by selective laser melting (SLM) under different laser scanning speed conditions in order to compare the effect of process energy density on the residual stress state. Subsurface residual stress analysis was conducted by means of synchrotron X-ray diffraction in energy dispersive mode for three conditions: as-built on base plate, released from base plate, and after heat treatment on the base plate. The quantitative residual stress characterization shows a correlation with the qualitative bridge curvature method. Computed tomography (CT) was carried out to ensure that no stress relief took place owing to the presence of porosity. CT allows obtaining spatial and size pores distribution which helps in optimization of the SLM process.
High tensile residual stresses were found at the lateral surface for samples in the as-built conditions. We observed that higher laser energy density during fabrication leads to lower residual stresses. Samples in released condition showed redistribution of the stresses due to distortion.
Near eutectic cast Al–Si alloys are the basis of all Al-alloys used for pistons due to their high fluidity and relatively high strength-to-weight ratio. Their microstructure is characterized by the presence of eutectic-Si embedded in an age hardenable -Al matrix. During solution heat treatment, the eutectic Si network undergoes a process of gradual disintegration, reducing the load bearing capability and the strength of the alloy. The improvement of the high temperature strength is achieved by addition of transition elements such as Cu, Mg or Ni through the formation of stiff intermetallic (IM) phases.
In present study a near-eutectic AlSi12CuMgNi alloy produced by squeeze casting was investigated in as-cast condition. The in-situ neutron diffraction compression tests revealed the stress partitioning mechanism between phases of the alloy. Large stresses were found in IMs, showing their significant role as a reinforcement elements. After the failure of IM and Si phases the load is transferred back to the Al matrix, inducing further plastic deformation in it, yet without creating microcracking. The neutron diffraction experiments were coupled with assessment of internal damage after ex-situ compression tests by synchrotron radiation computed tomography. The quantitative analysis of CT data revealed that local tensile stresses in IM and Si phases induce microcracks with preferential orientation, parallel to the axis of applied load.
Altogether, present experimental data was used as an input for the developed micromechanical model based on Maxwell homogenization scheme. In contrast to the neutron diffraction experiment, which can only determine stress differences between the axial and radial sample directions, the model allows predicting the principal stresses in each phase of the alloy.
Additively manufactured (AM) triply periodic metallic minimum surface structures (TPMSS, from the English Triply Periodic Minimum Surface Structures) fulfill several requirements in both biomedical and engineering fields: tunable mechanical properties, low sensitivity to manufacturing defects, mechanical stability, and high energy absorption. However, they also present some quality control challenges that may prevent their successful application. In fact, optimization of the AM process is impossible without considering structural features such as manufacturing accuracy, internal defects, and surface topography and roughness. In this study, quantitative nondestructive analysis of Ti-6Al-4V alloy TPMSS was performed using X-ray computed tomography (XCT). Several new image analysis workflows are presented to evaluate the effects of buildup direction on wall thickness distribution, wall degradation, and surface roughness reduction due to chemical etching of TPMSS. It is shown that the fabrication accuracy is different for the structural elements printed parallel and orthogonal to the fabricated layers. Different strategies for chemical etching showed different powder removal capabilities and thus a gradient in wall thickness. This affected the mechanical performance under compression by reducing the yield stress. A positive effect of chemical etching is the reduction of surface roughness, which can potentially improve the fatigue properties of the components. Finally, XCT was used to correlate the amount of powder retained with the pore size of the TPMSS, which can further improve the manufacturing process.
Nominal-actual comparisons are routinely performed to compare a manufactured specimen to a reference specimen. X-ray Computed Tomography (CT) has brought a profound change in the way that tolerance verifications are performed in industry, by allowing the inner and outer geometries of an object to be measured, without the need for external access or destructive testing. As a results, CT is increasingly used in additive manufacturing applications, where a nominal-actual comparison performed between the digital model (CAD file), used as an input for the 3D printer, and the CT volume from the printed part, can provide invaluable information as to the accuracy of the printing process. However, the nominal-actual comparison process is somewhat different when applied to additively manufactured specimens by comparison to conventionally manufactured specimens.
The overview of the activity of group 8.5 Micro-NDT (BAM, Belin, Germany) in the field of additively manufacturing material characterization will be presented. The challenges in the residual stress analysis of AM components are discussed on the basis on the show studies performed in BAM. Also, the synchrotron X-ray refraction technique, available in BAM, is presented, showing example of in-situ heating test of Al10SiMg AM material.
The material and damage behaviour of additively manufactured polyamide 12 (PA12) under dynamic loading was characterized by cyclic tests and microstructure analysis. The results were used to develop a numerical material and damage model. In a recent study, it was shown that the material and damage behaviour of 3D printed PA12 under quasistatic loading is simulated in a realistic way by coupling the
material model by Chaboche and the damage model by Gurson-Tvergaard-Needleman (GTN).
Using microscopy, X-ray refraction, and computed tomography, a porosity of about 5% was evaluated. These results served as a starting point for the present work. For the dynamic load, both the previously used Chaboche model and the GTN model were extended. Furthermore, the temperature was measured during the experiment and the self-heating effect was observed. Therefore, a temperaturedependent material parameters for the simulation were introduced. Considering the results of mechanical experiments, microstructural investigations, and self-heating effects, a good agreement between Experiment and numerical simulation could be achieved.