Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (13)
- Zeitschriftenartikel (9)
- Beitrag zu einem Tagungsband (1)
- Posterpräsentation (1)
- Forschungsdatensatz (1)
Schlagworte
- 3D printing (25) (entfernen)
Organisationseinheit der BAM
- 5 Werkstofftechnik (9)
- 5.4 Multimateriale Fertigungsprozesse (9)
- 8 Zerstörungsfreie Prüfung (8)
- 8.0 Abteilungsleitung und andere (6)
- 9 Komponentensicherheit (5)
- 9.3 Schweißtechnische Fertigungsverfahren (5)
- 4 Material und Umwelt (3)
- 6 Materialchemie (3)
- 8.5 Röntgenbildgebung (3)
- 6.5 Synthese und Streuverfahren nanostrukturierter Materialien (2)
Eingeladener Vortrag
- nein (13)
Several Additive Manufacturing (AM) processes are based on the deposition of a powder to form a powder-bed layer-by-layer which typically has a low packing density (35-50%) and consequently hinders the ability of sintering ceramic parts to full density. The layerwise slurry deposition (LSD) is an innovative process for the deposition of layers in AM. In the LSD, a slurry with no or small organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). When coupled with a printing head or with a laser, the LSD enables novel AM technologies inspired to the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder-bed. This approach has been successfully applied to silicate ceramics, but implementing technical ceramic slurries is more challenging, because the water is drained too quickly from the suspension into the pores of the previous porous layer. In this presentation, the variables involved in the LSD will be analyzed and the latest improvements in the deposition setup will be described. The application of the LSD to technical ceramics has the potential of generating additive manufacturing parts which in the green state are comparable to those produced by slip casting.
Several Additive Manufacturing (AM) processes are based on the deposition of a powder to form a powder-bed layer-by-layer which typically has a low packing density (35-50%) and consequently hinders the ability of sintering ceramic parts to full density.
The layerwise slurry deposition (LSD) is an innovative process for the deposition of layers in AM. In the LSD, a slurry with no or small organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). When coupled with a printing head or with a laser, the LSD enables novel AM technologies inspired to the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder-bed. This approach has been successfully applied to silicate ceramics, but implementing technical ceramic slurries is more challenging, because the water is drained too quickly from the suspension into the pores of the previous porous layer forming a cast.
In this presentation, the variables involved in the LSD will be analyzed and the latest improvements in the deposition setup will be described. The application of the LSD to technical ceramics has the potential of generating additive manufacturing parts which in the green state are comparable to those produced by slip casting.
The layerwise slurry deposition (LSD) is an innovative process for the deposition of layers in AM. In the LSD, a slurry with no or low organic content is repetitively spread as thin layers on each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). The LSD therefore shares aspects both of tape casting and slip casting. The LSD differentiates from the classical powder-based AM layer deposition, which typically are able to achieve only a low packing density (35-50%), consequently hindering the ability of sintering ceramic parts to full density. The LSD is coupled with the principles of selective laser sintering (SLS) or binder printing, to generate novel processes which take advantage of the possibility of achieving a highly dense powder-bed.
This presentation will describe the most recent developments in the application of the LSD to technical ceramics, in particular Al2O3 and SiC, discussing potential and issues connected to the layer deposition and the selective laser sintering of such layers.
Hydroxyapatite (HA) is a bioceramic material with excellent biological properties. However, these properties are strongly dependent of ist crystallinity degree, with high values of crystallinity associated to poor resorption rates and bioactivity. This work evaluates the properties of HA samples produced by two different free-forming conformation methods, CNC machining and 3D printing. In both cases, porous gypsum samples were produced and subsequently converted into HA in a reaction with di-ammonium hydrogen phosphate at 100°C and pH 8. A total conversion of the samples was achieved after 36 h independently of the conformation method used. The microstructure, however, before and after the conversion is showed to be dependent on the method used. After conversion the machined samples achieved a Maximum compressive strength of 3.5 MPaforporosities of circa 80%, while 3D printed samples achieved a tensile strength of 2.0 MPa by porosities of 61%.
Additive manufacturing (3D printing) of ceramics and other materials offers significant advantages compared to conventional production processes for several applications. While ceramics have been extensively investigated in this regard, additive manufacturing of geopolymers have received much less attention to date. In the present contribution we study a ‘standard’ metakaolin-based geopolymer, a fly ash-based geopolymer and a silica-based one-part geopolymer regarding their suitability for additive manufacturing via selective laser curing. Model geometries such as bars and cuboids could be produced by this route. After selective laser curing the specimens were additionally cured at 80 °C for 24 h. The specimens were studied by means of scanning electron microscopy (SEM) and powder X-ray diffraction (XRD). SEM showed that the precursors in all geopolymers had reacted partially and geopolymeric gel had formed. XRD confirmed these results and additionally revealed that the crystalline byproducts (zeolites) in the one-part geopolymer differed from the byproducts observed in conventionally produced samples. This indicates that also the geopolymerization reactions differ between the two synthesis routes. The mechanical strength after selective laser curing and 80 °C-curing appeared to be highest for the metakaolin-based geopolymer. However, SEM also showed that a significant volume of macropores remained in most regions of all specimens, while some regions in the metakaolin-based geopolymer appeared to be significantly denser. These preliminary results demonstrate that selective laser curing offers potential for the production of geopolymers, but more research has to be undertaken to optimize the process.
An improved method of powder 3D printing leading to dense ceramic parts is presented. The application of powder-based binder jetting 3D printing technologies to technical ceramics is generally limited by the low packing density of the powder and by the need to use a flowable powder. With layer-wise slurry deposition, it is, however, possible to deposit powder beds with high particle packing and furthermore using submicron powders. This method was combined with the binder jetting technology to develop a novel process, named LSD-print. By means of LSD-print, a submicron Al2O3 powder could be processed to produce samples with a density comparable with that of standard pressed samples, both in the green state and after sintering.
Powder based Additive Manufacturing (AM) processes are widely used for metallic and polymeric materials, but rarely commercially used for ceramic materials, especially for technical ceramics. This seemingly contradicting observation is explained by the fact that in powder based AM, a dry flowable powder needs to be used. Technical ceramics powders are in fact typically very fine and poorly flowable, which makes them not suitable for AM. The layerwise slurry deposition (LSD) is an innovative process for the deposition of powder layers with a high packing density for powder based AM. In the LSD process, a ceramic slurry is deposited to form thin powder layers, rather than using a dry powder This allows the use of fine powders and achieves high packing density (55-60%) in the layers after drying. When coupled with a printing head or with a laser source, the LSD enables novel AM technologies which are similar to *Denotes Presenter 42nd International Conference & Exposition on Advanced Ceramics & Composites 127 Abstracts the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder bed. The LSD -3D printing, in particular, offers the potential of producing large (> 100 mm) and high quality ceramic parts, with microstructure and properties similar to traditional processing. This presentation will give an overview of the milestones in the development of this technology, with focus on the latest results applied both to silicate and to technical ceramics.
The Layerwise Slurry Deposition is a technology for the deposition of highly packed powder layers. A powder bed is achieved by depositing and drying layers of a ceramic suspension by means of a doctor blade. This deposition technique was combined with the binder jetting technology to develop a novel Additive Manufacturing technology, named LSD-print. The LSD-print was applied to a porcelain ceramic. It is shown that it was possible to produce parts with high definition, good surface finish and at the same time having physical and mechanical properties close to those of traditionally processed porcelain, e.g. by slip casting.
This technology shows high future potential for being integrated alongside traditional production of porce-lain, as it is easily scalable to large areas while maintaining a good definition. Both the Layerwise Slurry Deposition method and the binder jetting technologies are readily scalable to areas as large as > 1 m2.
Summary: A screening test for potential emissions of volatile organic compounds (VOC) was run on different thermoplastic filaments used for 3D printing. The method of direct thermal desorption was used to simulate the high temperatures during the 3D printing process and to identify the main compounds emitted from the filaments. A large number of unexpected compounds were detected that might affect the user’s health and have an impact on indoor air chemistry.
Introduction: The use of desktop 3D printers is increasing. Compared to other devices with known emissions, e.g. laser printers, there is still a lack of information on possible emissions of VOC and ultrafine particles during operation and the effect on indoor air quality. Most of the commercially available desktop 3D printers operate with a molten polymer deposition. For this process a solid thermoplastic filament is heated in an extrusion nozzle. Most filaments for desktop 3D printers use either acrylonitrile butadiene styrene (ABS) or polylactic acid (PLA) as filament. Alternatives are polyvinyl alcohol (PVA) or polycarbonate (PC).
Method: Eight different thermoplastic filaments for 3D printers were analysed by direct thermal desorption followed by GC-MS identification of the emitted substances. Direct thermal desorption was done by desorbing 5 mg of the feedstock for 1 minute at a temperature of 210°C. This is an average temperature for 3D printing with thermoplastic filaments.
Results and conclusions: The comparison of the 4 different filament groups showed the highest overall emissions from ABS, followed by PLA, PC and PVA. Filament ABS 2 emitted mainly SVOCs and triphenyl phosphate, the latter has the highest emission for a single compound from all evaluated filaments.
Thermoplastic filaments are a new source of VOC emissions due to the high temperatures associated with 3D printing, which can reach up to 270°C. Some of the detected compounds like lactic acid, lactide and bisphenol A have never been described before in the indoor environment. Additionally some of the main substances could not be identified and some others might have the potential to affect the indoor air chemistry.
The appearance of some newly detected compounds raises concerns about potential health effects for the users of 3D printers at home.
Im Rahmen des Themenfeld Projektes „Process Monitoring of AM“ (ProMoAM) evaluiert die BAM gegenwärtig die Anwendbarkeit verschiedenster ZfP-Verfahren, darunter die Thermografie, zur Prozessüberwachung in der additiven Fertigung von Metallen in Hinblick auf die Qualitätssicherung.
In diesem Beitrag werden SWIR-Thermografiemessungen während des Bauprozesses mittels Laser Pulver Auftragsschweißen (LPA) vorgestellt. Eine Herausforderung im Rahmen dieser Messungen liegt in der Positionierung der Kamera, welche entweder fixiert am Schweißarm, also mitbewegt, oder fixiert in der Baukammer, also stationär, erfolgen kann, wobei beide Varianten mit individuellen Vor- und Nachteilen verbunden sind. Eine stationäre Befestigung der Kamera ermöglicht zwar eine einfachere Zuordnung der Messdaten zu der jeweiligen Position im Bauteil, führt jedoch bei komplexeren Geometrien zwangsläufig zu Problemen durch Abschattungen und zu defokussierten Bereichen. Zur Auswertung von Thermogrammen, welche durch eine mit dem Schweißarm mitbewegte Kamera aufgenommen wurden, sind hingegen für jedes Bild akkurate Positionsdaten der Kamera nötig um die Messdaten einer Position im Bauteil zuzuordnen. Da die Positionsdaten des Schweißarmes im allgemeinen Fall durch die Anlagensoftware nicht zur Verfügung gestellt werden, muss diese Information durch zusätzliche Messungen aufgezeichnet werden. Hierzu verwenden wir einen an der Kamera befestigten Beschleunigungssensor. Dieser ermöglicht einen zeitlichen Abgleich mit dem vorprogrammierten Verfahrweg des Schweißarmes, welcher im Allgemeinen noch Unsicherheiten bezüglich genauer Geschwindigkeiten und Beschleunigungen offenlässt. Weiterhin untersuchen wir den Einfluss des empfindlichen Spektralbereiches der IR-Kamera durch den Vergleich von Messungen mit verschiedenen schmalbandigen Bandpassfiltern (25 nm FWHM) in einem Bereich von 1150 nm bis 1550 nm.