ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
The concrete prism test at 60°C facilitates accelerated testing of alkali-silica reactivity of aggregates within five months. Manual measurement is usually conducted to determine expansion of test specimen every 28 days. This conventional procedure gives only limited insight to expansion behaviour of ASR-affected prisms. Due to the large time intervals, expansion exceeding the critical value of 0.3 mm/m is likely to be noticed late. Continuous recording applied in this work resolves this problem and delivers beneficial information on the shape of the expansion curve.
Different types of aggregate have been tested applying continuous and manual measurement to the concrete specimens.
Models of ASR-induced expansion, available in the open literature, so far are validated with discontinuous data hardly tracing the modelled curve. Continuous measurement improves validation and further model development.