Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
A new method for sampling wear particles directly from the lubricant reservoir has been developed and applied successfully for analyzing wear particles by high-resolution scanning electron microscopy in transmission mode having coupled energy-dispersive X-ray spectroscopy. The lubricated tribological testing was carried out with fully formulated as well as with non-formulated synthetic base oil. It was possible to analyze individual particles with dimensions as small as about 5–30 nm which are likely the 'primary' wear particles. A majority of the particles, however, are agglomerated and, thus, lead to the formation of larger agglomerates of up to a few micrometers. Chemical analysis led to the conclusion that most of the observed particles generated in formulated oil, especially the larger ones, are composed of the additives of the lubricant oil. In non-formulated base oil, the primary particles are of similar dimensions but contain only iron, chromium and oxygen, but most likely stem from the mating materials. This finding points to the fact that the main wear mechanism under lubricated conditions with fully formulated oil is more like a continuous shearing process rather than a catastrophic failure with the generation of larger primary particles. When the oil is non-formulated, however, several wear mechanisms act simultaneously and the wear rate is increased significantly. Generated larger primary particles are milled down to the nanoscale. When the oil is fully formulated, wear mainly takes places at the additive layer or tribofilm; thus, the steel surface is protected.
Pristine, reduced, and alkylated graphene oxides are applied as lubricating additives in paraffin grease. It has revealed that their crystalline structure governs the tribological properties of grease for steel tribo-pair. The microstructural analyses of grease samples showed that a loose fiber network of soap in the presence of graphene-based additive allows their facile release for efficient lubrication. The surface analyses based on the microscopic and elemental mapping show the development of a graphene-derived protective film on the worn scars, which protected the tribo-surfaces and subsided the wear. The reduced graphene oxide (rGO) with the interlamellar distance of 0.35 nm in the (002) plane provided minimum resistance to shear and exhibited maximum reduction in coefficient of friction (COF) for the paraffin grease. The presence of oxygen functionalities in the basal of pristine and alkylated graphene oxide (GO) compromised the interlamellar shearing under tribo-stress; consequently, higher COF than that of rGO.
Tribological properties of ultrahigh-molecular weight polyethylene (UHMWPE) and cross-linked polyethylene (XLPE) were studied in two different wear modes. Firstly, reciprocating sliding wear studies under non-conformal contact investigated the effects of counterface surface roughness (polished, lapped and ground) of Ti6Al4V on the friction and wear of the polyethylenes. Secondly, two-body abrasive wear studies in conformal contact against different abrasive grit size papers were also carried out to ascertain the wear sensitivity of the polyethylenes under these adverse conditions. Wear mechanisms were studied using optical and scanning electron micrographs. The results of the reciprocating sliding wear studies showed that surface roughness of the counterface influenced friction and wear characteristics although no correlation was found between the coefficient of friction and specific wear rate. XLPE demonstrated wear sensitivity, particularly under severe abrasive wear condition. The results indicated that the performance of the polyethylenes greatly depends upon the tribological system under which it is operating.