It has been shown that selected types of substituents are able to vary the oxidative behavior of multi-walled carbon nanotubes. Such substituents investigated were sterically hindered secondary amino groups bonded in grafted piperidine units and covalently bonded bromine groups. Their interference and activity was preliminary determined in the model cumene and then in oil diesel fraction and low density polyethylene oxidation reactions. Results obtained indicate that chemical linking of amine moieties containing –NH groups directly to the carbon nanotubes core significantly increases their intrinsic anti-oxidative capacity while the grafting of Br-groups provokes the opposite functioning of the pristine samples. This inference was proved by thermogravimetric and differential thermal analysis of the polyethylene composites and experiments on profound aerobic oxidation of petroleum naphthenic fraction derived from the commercial Baku oils blend diesel cut.
Waste disposal of carbon nanotube (CNT) containing products is expected to be the most important pathway for release of CNTs into the environment. In the present work, the use of radiolabelled CNTs (14C-CNT) for polycarbonate polymer nanocomposites with 1 wt% 14C-CNT content allowed for the first time to quantify and differentiate the CNT release according to the type of impact along the materials' ageing history. After an initial exposure of the nanocomposite by solar-like irradiation, further environmental impacts were applied to composite material. They aimed at mimicking disposal site conditions that may induce further ageing effects and CNT release. This study included shaking in water, rapid temperature changes, soaking in humic acid solution as well as waste water effluent, and, finally, gentle mechanical abrasion. All ageing impacts were applied sequentially, both on pristine (control) and on solar-irradiated nanocomposites. All experiments were accompanied by absolute quantification of radioactive release as well as chemical and morphological analyses of the nanocomposite surfaces using infra-red (IR) spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The morphological analysis showed that spectral irradiation can uncover CNT networks on the outer nanocomposite surface layers by polymer degradation. After having subjected the solar-irradiated nanocomposite to all studied disposal site effect, the total radioactive release was quantified to amount to 64 mg CNT/m2, whereas only 0.8 mg CNT/m2 were found for the un-irradiated control sample. Solar degradation of polymers was thus found to significantly increase the propensity of the studied polymer nanocomposites to release CNTs during ageing effects at the product's end-of-life typical for disposal sites.