The largest percentage of component life under fatigue loading conditions is spent in the short crack regime and in the initial phase of long cracks. The use of Fracture Mechanics in the characterization of fatigue crack growth rate curves has proven to be a useful and adequate tool in the prediction of fatigue lifetimes as long as certain conditions are satisfied. All the above implies the need for a methodical and accurate procedure of assessment of the material response in order to achieve a reliable prediction of lifetime in components under safe conditions, based on the damage tolerance approach. It also highlights the need to analyse the response of increasingly reduced thicknesses, which, as time goes by, show greater differences with respect to those commonly studied and defined in standards and design guidelines, as well as to the experimental studies that can be found in the literature at present. Some examples of thin-walled components are turbine blades or certain additively manufactured parts where, additionally, variations in material properties can occur locally and should also be examined.
The present study deals with the experimental characterization of short crack propagation in SLM (selective-laser-melting) manufactured stainless steel. More specifically, the determination of cyclic R-curves is discussed. This describes the dependency of the crack propagation threshold on crack growth during the short crack propagation stage. For metals, the threshold, starting at a material-intrinsic value, increases until it reaches a value independent of the crack length due to crack closure phenomena which build up at that stage. The cyclic R-curve, when used in the frame of a cyclic R curve analysis, characterizes the resistance of a material to fatigue crack growth and the ability to arrest a physically short crack. Thus, it is the link between classical fatigue and fracture mechanics. In the high-cycle-fatigue range, the short crack propagation stage dominates the overall lifetime, i.e., the number of cycles until failure. Below the fatigue limit crack arrest of hitherto propagable micro-cracks will occur. The effort for the experimental characterization of the short fatigue crack propagation behavior and the cyclic R-curve is very high compared to experiments on long crack propagation. A very exact measurement of crack extension is required, since small increments need to be depicted. Pre-cracking must leave a closure free initial crack, since closure must be build up only by the cyclic R-curve. The closure-free status is achieved by compression pre-cracking. The aim of the present study is an insight into the influence of an AM process on the short crack propagation threshold. Cyclic R-curves are experimentally determined at different load-ratios for 316L austenitic steel specimens produced by SLM and conventional manufacturing. Residual stresses are measured in the crack plane and their influence on the cyclic R-curve is discussed.