The wear rates of self-mated alumina couples show that friction as well as wear is largely determined by the above-mentioned hydro-thermal conditions. The presence of water and its amount available in the surrounding system either in liquid or in gaseous form plays a key role for friction and wear behavior and can be beneficial for the tribological profile of steam degradation resistant materials. Hot steam enhances the tribo-chemical formations of oxides and hydroxides on MgO-ZrO2 alumina and antimony impregnated carbon.
The friction and wear properties of polyetherimide composites under dry oscillating sliding condition at room temperature (RT) as well as at elevated temperature (120 °C) was investigated. The polymer specimens were made to oscillate against steel cylinder as a counterpart. The friction and wear properties of PEI and composites were strongly influenced by the temperature. In case of carbon fiber composite abrasive action of carbon fibers has severely damaged the counterpart and resulted in accelerated wear of the composite at RT. Solid lubricants filled (PTFE, MoS2, graphite) along with glass fiber is beneficial in improving the friction and wear performance of the PEI composite at RT, whereas at elevated temperature wear performance was deteriorated.
The influence of temperature and counterbody material on the tribological properties of a-C:H
coatings deposited on Cronidur 30 steel has been investigated in a lubricated ball on disk
contact situation with alpha-alumina and silicon nitride as counterbodies. The results show, that the wear volumes of the systems increase exponentially with increasing temperature, for alpha-alumina more than for silicon nitride. Two different wear mechanisms seem to have a
major influence: First, the abrasive action due to materials hardness and second, the tribo-oxidation when silicon nitride is counter material.